Proton conductivity of multifunctional metal phosphonate frameworks

Metal phosphonates exhibit attractive characteristics for proton conductivity, such as tunable functionality, chemical and thermal stability and the existence of H-bond networks with acidic protons within their structure.1 In the present work, we examine the relationship between crystal structure and proton conductivity for several metal (mono-, di- and tri-valent) phosphonates containing rigid: (5-(dihydroxyphosphoryl)isophthalic acid, PiPhtA and 2-hydroxyphosphonoacetic acid, HPAA) or flexible: (hexa- or octamethylenediamine-N,N,N′,N′-tetrakis(methylenephosphonic acid, H8HDTMP or H8ODTMP) multifunctional ligands. The crystalline hybrid derivatives prepared show a great structural diversity, from 1D to 3D open-frameworks possessing hydrogen-bonded water molecules and phosphonic and carboxylic acid groups. The rigid 3D framework of Ca-PiPhtA, that exhibits a proton conductivity of 5.7•10-4 S/cm as synthesized, transforms into a layered compound upon exposure to ammonia vapors2 with increased proton conductivity (6.6•10-3 S/cm). The flexible frameworks of magnesium or lanthanide phosphonates, with 1D channels, present conductivities higher than 10-3 S/cm. Their activation energies fall in the range corresponding to a Grotthuss mechanism.3,4 For M(I)-HPAA solids conductivities up to 5.6•10-3 S/cm were measured. References 1. P. Ramaswamy, N.E. Wong, G.K.H. Shimizu, Chem. Soc. Rev. 43 (2014) 5913. 2. M. Bazaga-García, R.M.P. Colodrero, M. Papadaki, P. Garczarek, J. Zoń, P. Olivera-Pastor, E.R. Losilla, L. León-Reina, M.A.G. Aranda, D. Choquesillo-Lazarte, K.D. Demadis, A. Cabeza, J. Amer. Chem. Soc. 136 (2014) 5731. 3. R.M.P. Colodrero, P. Olivera-Pastor, E.R. Losilla, D. Hernández-Alonso, M.A.G. Aranda, L. Leon-Reina, J. Rius, K.D. Demadis, B. Moreau, D. Villemin, M. Palomino, F. Rey, A. Cabeza, Inorg. Chem. 51 (2012) 7689. 4. R.M.P. Colodrero, P. Olivera-Pastor, E.R. Losilla, M.A.G. Aranda, L. Leon-Reina, M. Papadaki, A.C. McKinlay, R.E. Morris, K.D. Demadis, A. Cabeza, Dalton Trans. 41 (2012) 4045.Universidad de Málaga. Campus de Excelencia Internacional Andalucía Tech. Junta de Andalucía, Proyecto Excelencia FQM-1656. Ministerio de Economía y Competitividad, MAT2013-41836-

Multifunctional lanthanum tetraphosphonates: Flexible, ultramicroporous and proton-conducting hybrid frameworks

A new flexible ultramicroporous solid, La(H5DTMP)·7H2O (1), has been crystallized at room temperature using the tetraphosphonic acid H8DTMP, hexamethylenediamine-N,N,N′,N′-tetrakis(methylenephosphonic acid). Its crystal structure, solved by synchrotron powder X-ray diffraction, is characterised by a 3D pillared open-framework containing 1D channels filled with water. Upon dehydration, a new related crystalline phase, La(H5DTMP) (2) is formed. Partial rehydration of 2 led to La(H5DTMP)·2H2O (3). These new phases contain highly corrugated layers showing different degrees of conformational flexibility of the long organic chain. The combination of the structural study and the gas adsorption characterization (N2 and CO2) suggests an ultramicroporous flexible framework. NO isotherms are indicative of a strong irreversible adsorption of NO within the pores. Impedance data indicates that 1 is a proton-conductor with a conductivity of 8 × 10−3 S cm−1 at 297 K and 98% of relative humidity, and an activation energy of 0.25 eV.Proyecto nacional MAT2010-15175 (MICINN, España

Active study: undetected prevalence and clinical inertia in the treatment of breakthrough cancer pain (BTcP)

Aims To prove if there is clinical inertia in the identification and treatment of episodes of breakthrough cancer pain (BTcP), comparing actual results from clinical practice with clinical oncologists’ prior perception. Design Observational and descriptive study, using information collected by practising medical oncologists, at three moments: (a) questionnaire regarding their professional judgement of the handling of patients with BTcP in their practice, (b) cross-sectional clinical screening, to detect possible existing cases of BTcP in a representative sample of their patients, (c) retrospective self-audit of clinical case histories of patients diagnosed with BTcP to find out about how it has been handled. Participants and study period A random sample on a state level of 108 specialists in medical oncology. 540 patients who suffer some type of cancer pain on the designated study date for each specialist (July–December 2016). Results The global prevalence of BTcP in the study sample covered 91.3% of the patients who were suffering some type of cancer pain. Barely 2% of the doctors surveyed suspected figures around this mark. 40.9% of the cases had not been previously detected as BTcP by their doctors. Although 90% of the patients who had previously been diagnosed with BTcP received a specific analgesic treatment for the symptoms, 42% of those patients with known BTcP were not able to control their episodes of pain. Conclusions Clinical inertia is a serious problem in the handling of BTcP in medical oncology services, where it is the subject of a significantly low level of detection and treatment, despite the contrasting perception of specialists.pre-print339 K

Combined Raman spectroscopic and Rietveld analyses as a useful and nondestructive approach to studying flint raw materials at prehistoric archaeological sites

Artículo sobre análisis de espectroscopía

Tuning Proton Conductivity in A Multifunctional Calcium Phosphonate Hybrid Framework

Multi-chelating phosphonate ligands are organic linkers alternative to polycarboxylates and other ligands providing synthetic access to a number of thermally- and chemically-stable MOFs [1]. Metal phosphonates are amenable for accessing suitable and highly conducting materials both by tuning structural features and post-synthesis treatment [2,3]. For instance, proton conductivity values in the order of 10−2 S cm–1 have been reported for several phosphonate-based compounds [4]. We report hereby the synthesis, structural characterization and proton conductivity of an open framework hybrid, Ca2[(HO3PC6H3COOH)2]2[(HO3PC6H3(COO)2H).(H2O)2].5H2O, that combines Ca2+ ions and the rigid polyfunctional ligand 5-(dihydroxyphosphoryl)isophthalic acid. This compound was obtained by slow crystallization at ambient conditions at pH 3. Its complex pillared layered structure, solved by single crystal X-ray analysis, contains hydrophilic 1D channels filled with both water and acidic phosphonate and carboxylate groups creating a hydrogen-bonded network. Partial removal of the lattice water at 75 °C causes a monoclinic structural distortion but still retaining the initial conductivity properties (5.7x10-4 Sxcm-1). Exposure of the sample to ammonia vapor from a concentrated aqueous solution led to major structural changes resulting in a new layered material containing seven NH3 and sixteen H2O molecules per formula. This solid exhibits enhanced conductivity, reaching 6.6x10-3 S.cm-1, as measured at 98 % RH and T = 24 °C. Activation energies were between 0.23 and 0.40 eV, typical of a Grothuss mechanism of proton conduction.Universidad de Málaga. Campus de Excelencia Internacional Andalucía Tech. Proyecto Excelencia Junta de Andalucía, FQM-1656. MAT2010-15175

Aluminum-rich belite sulfoaluminate cements: clinkering and early age hydration

Belite sulfoaluminate (BSA) cements have been proposed as environmentally friendly building materials, as their production may release up to 35% less CO2 into the atmosphere when compared to ordinary Portland cements. Here, we discuss the laboratory production of three aluminum-rich BSA clinkers with nominal mineralogical compositions in the range C2S (50-60%), C4A3$(20- 30$, i.e. a value as close as possible to the nominal composition. Under these experimental conditions, three different BSA clinkers, nominally with 20, 30 and 30 wt% of C4A3$, had 19.6, 27.1 and 27.7 wt$ respectively, as determined by Rietveld analysis. We also studied the complex hydration process of BSA cements prepared by mixing BSA clinkers and gypsum. We present a methodology to establish the phase assemblage evolution of BSA cement pastes with time, including amorphous phases and free water. The methodology is based on Rietveld quantitative phase analysis of synchrotron and laboratory X-ray powder diffraction data coupled with chemical constraints. A parallel calorimetric study is also reported. It is shown that the b-C2S phase is more reactive in aluminum-rich BSA cements than in standard belite cements. On the other hand, C4A3$ reacts faster than the belite phases. The gypsum ratio in the cement is also shown to be an important factor in the phase evolution

Influence of fly ash blending on hydration and physical behavior of Belite-Alite-Ye'elimite cements

A cement powder, composed of belite, alite and ye’elimite, was blended with 0, 15 and 30 wt% of fly ash and the resulting lended cements were further characterized. During hydration, the presence of fly ash caused the partial inhibition of both AFt degradation and belite reactivity, even after 180 days. The compressive strength of the corresponding mortars increased by increasing the fly ash content (68, 73 and 82 MPa for mortars with 0, 15 and 30 wt% of fly ash, respectively, at 180 curing days), mainly due to the diminishing porosity and pore size values. Although pozzolanic reaction has not been directly proved there are indirect evidences.This work is part of the Ph.D. of D. Londono-Zuluaga funded by Beca Colciencias 646—Doctorado en el exterior and Enlaza Mundos 2013 program grant. Cement and Building materials group (CEMATCO) from National University of Colombia is acknowledged for providing the calorimetric measurements. Funding from Spanish MINECO BIA2017-82391-R and I3 (IEDI-2016-0079) grants, co-funded by FEDER, are acknowledged

Guest Molecule-Responsive Functional Calcium Phosphonate Frameworks for Tuned Proton Conductivity

We report the synthesis, structural characterization, and functionality of an open-framework hybrid that combines Ca2+ ions and the rigid polyfunctional ligand 5-(dihydroxyphosphoryl) isophthalic acid (PiPhtA). Ca-PiPhtA-I is obtained by slow crystallization at ambient conditions from acidic (pH≈3) aqueous solutions. It possesses a high water content (both Ca coordinated and in the lattice), and importantly, it exhibits water-filled 1D channels. At 75 °C, Ca-PiPhtA-I is partially dehydrated and exhibits a crystalline diffraction pattern that can be indexed in a monoclinic cell with parameters close to the pristine phase. Rietveld refinement was carried out for the sample heated at 75 °C, Ca-PiPhtA-II, using synchrotron powder X-ray diffraction data.All connectivity modes of the “parent” Ca-PiPhtA-I framework are retained in Ca-PiPhtA-II. Upon Ca-PiPhtA-I exposure to ammonia vapors (28% aqueous NH3) a new derivative is obtained (Ca-PiPhtA-NH3) containing 7 NH3 and 16 H2O molecules according to elemental and thermal analyses. Ca-PiPhtA-NH3 exhibits a complex X-ray diffraction pattern with peaks at 15.3 and 13.0 Å that suggest partial breaking and transformation of the parent pillared structure. Although detailed structural identification of Ca-PiPhtA-NH3 was not possible, due in part to nonequilibrium adsorption conditions and the lack of crystallinity, FT-IR spectra and DTA-TG analysis indicate profound structural changes compared to the pristine Ca-PiPhtA-I. At 98% RH and T = 24 °C, proton conductivity, σ, for Ca PiPhtA-I is 5.7 ×10−4 S·cm−1. It increases to 1.3 × 10−3 S·cm−1 upon activation by preheating the sample at 40 °C for 2 h followed by water equilibration at room temperature under controlled conditions. Ca-PiPhtA-NH3 exhibits the highest proton conductivity, 6.6 × 10−3 S·cm−1, measured at 98% RH and T = 24 °C. Ea for proton transfer in the above-mentioned frameworks range between 0.23 and 0.4 eV, typical of a Grothuss mechanism of proton conduction.Proyecto nacional MAT2010-1517

The Large Observatory for x-ray timing

The Large Observatory For x-ray Timing (LOFT) was studied within ESA M3 Cosmic Vision framework and participated in the final down-selection for a launch slot in 2022-2024. Thanks to the unprecedented combination of effective area and spectral resolution of its main instrument, LOFT will study the behaviour of matter under extreme conditions, such as the strong gravitational field in the innermost regions of accretion flows close to black holes and neutron stars, and the supra-nuclear densities in the interior of neutron stars. The science payload is based on a Large Area Detector (LAD, 10 m2 effective area, 2-30 keV, 240 eV spectral resolution, 1° collimated field of view) and a WideField Monitor (WFM, 2-50 keV, 4 steradian field of view, 1 arcmin source location accuracy, 300 eV spectral resolution). The WFM is equipped with an on-board system for bright events (e.g. GRB) localization. The trigger time and position of these events are broadcast to the ground within 30 s from discovery. In this paper we present the status of the mission at the end of its Phase A study

The LOFT mission concept: a status update

The Large Observatory For x-ray Timing (LOFT) is a mission concept which was proposed to ESA as M3 and M4 candidate in the framework of the Cosmic Vision 2015-2025 program. Thanks to the unprecedented combination of effective area and spectral resolution of its main instrument and the uniquely large field of view of its wide field monitor, LOFT will be able to study the behaviour of matter in extreme conditions such as the strong gravitational field in the innermost regions close to black holes and neutron stars and the supra-nuclear densities in the interiors of neutron stars. The science payload is based on a Large Area Detector (LAD, >8m2 effective area, 2-30 keV, 240 eV spectral resolution, 1 degree collimated field of view) and a Wide Field Monitor (WFM, 2-50 keV, 4 steradian field of view, 1 arcmin source location accuracy, 300 eV spectral resolution). The WFM is equipped with an on-board system for bright events (e.g., GRB) localization. The trigger time and position of these events are broadcast to the ground within 30 s from discovery. In this paper we present the current technical and programmatic status of the mission