CROSS-LINKING OF EPOXY-OLIGOESTERIC MIXTURES IN THE PRESENCE OF CARBOXY-CONTAINING DERIVATIVE OF ED-24 EPOXY RESIN

Abstract. Cross-linking of epoxy-oligomeric mixtures has been studied at room temperature and at heating to 383, 403 and 423 K for 15, 30, 45, 60 and 75 min in the presence of polyethylenepolyamine. The mixtures consist of industrial ED-20 epoxy resin, oligoesteracrylate TGM-3 and carboxy-containing derivative of ED-24 epoxy resin. The effect of mixture composition, temperature and process time on the gel-fraction content and hardness of polymeric films has been examined. Using IR-spectroscopy the chemism of network formation has been determined

Usieciowane mieszaniny epoksydowo-izocyjanianowe zawierające żywicę Epidian-6 modyfikowaną glikolami

Polymeric films of cross-linked structure may be formed using epoxy-isocyanate blends composed of Epidian-5 epoxy resin, 4,4'-diphenylmethanediisocyanate (MDI), Z-1 polyamine hardener and Epidian-6 epoxy resin modified by glycols. The effect of the component natures and ratio, process temperature and time on the gel-fraction content, as well as film hardness, was examined. The chemistry of the film forming process was determined using infrared-spectroscopy (IR).Z mieszaniny epoksydowo-izocyjanianowej, otrzymanej z żywicy epoksydowej Epidian-5, utwardzacza Z-1 i diizocyjanianu 4,4'-metylenodifenylu (MDI), oraz żywicy epoksydowej Epidian-6 zmodyfikowanej glikolami wytwarzano folie polimerowe o usieciowanej strukturze chemicznej. Oceniano wpływ składu jakościowego i ilościowego mieszaniny, temperatury oraz czasu reakcji na zawartość frakcji żelowej gotowych folii polimerowych i ich twardość. Przebieg procesu formowania folii badano metodą spektroskopii w podczerwieni (IR)

Synteza i właściwości karboksylowej pochodnej monometakrylanu Epidianu 6

We present the synthesis of an oligomer with carboxy and methacrylic groups based on Epidian 6. The effect of the catalyst nature and amount, solvent nature and process temperature on the rate of the reaction between Epidian 6 monomethacrylate and adipic acid was examined at 313, 323 and 333 K in the presence of 4-dimethylaminopyridine, 1,4-diazobicyclo[2.2.2]octane, and benzyltriammonium chloride. The synthesized oligomer was characterized using chemical and IR-spectroscopic analyses. We suggest the use of the synthesized product as an active additive to epoxy-oligoesteric blends based on Epidian 5. The chemistry of the film forming process has been determined using IR-spectroscopy.Na bazie żywicy epoksydowej Epidian 6 w temp. 313, 323 oraz 333 K w obecności 4-dimetyloaminopirydyny, 1,4-diazobicyklo[2.2.2]oktanu oraz chlorku benzylotriamoniowego otrzymywano oligomery zawierające grupy karboksylowe i metakrylowe. Zbadano wpływ ilości i rodzaju użytego katalizatora, rozpuszczalnika oraz temperatury procesu na szybkość reakcji monometakrylanu Epidianu6 z kwasem adypinowym. Zsyntetyzowany oligomer charakteryzowano metodami chemicznymi i na podstawie analizy FT-IR. Przebieg procesu formowania cienkich warstw (błon) badano za pomocą spektroskopii w podczerwieni. Uzyskany produkt może być wykorzystany jako aktywny dodatek do mieszanin epoksydowo-oligoestrowych wytwarzanych z żywicy Epidian 5