Embrittlement of MISSE 5 Polymers After 13 Months of Space Exposure
Understanding space environment induced degradation of spacecraft materials is essential when designing durable and stable spacecraft components. As a result of space radiation, debris impacts, atomic oxygen interaction, and thermal cycling, the outer surfaces of space materials degrade when exposed to low Earth orbit (LEO). The objective of this study was to measure the embrittlement of 37 thin film polymers after LEO space exposure. The polymers were flown aboard the International Space Station and exposed to the LEO space environment as part of the Materials International Space Station Experiment 5 (MISSE 5). The samples were flown in a nadir-facing position for 13 months and were exposed to thermal cycling along with low doses of atomic oxygen, direct solar radiation and omnidirectional charged particle radiation. The samples were analyzed for space-induced embrittlement using a bend-test procedure in which the strain necessary to induce surface cracking was determined. Bend-testing was conducted using successively smaller mandrels to apply a surface strain to samples placed on a semi-suspended pliable platform. A pristine sample was also tested for each flight sample. Eighteen of the 37 flight samples experienced some degree of surface cracking during bend-testing, while none of the pristine samples experienced any degree of cracking. The results indicate that 49 percent of the MISSE 5 thin film polymers became embrittled in the space environment even though they were exposed to low doses (approx.2.75 krad (Si) dose through 127 mm Kapton) of ionizing radiation
Overview of the MISSE 7 Polymers and Zenith Polymers Experiments After 1.5 Years of Space Exposure
As part of the Materials International Space Station Experiment 7 (MISSE 7), two experiments called the Polymers Experiment and the Zenith Polymers Experiment were flown on the exterior of the International Space Station (ISS) and exposed to the low Earth orbit (LEO) space environment for 1.5 years. The Polymers Experiment contained 47 samples, which were flown in a ram or wake flight orientation. The objectives of the Polymers Experiment were to determine the LEO atomic oxygen erosion yield (Ey, volume loss per incident oxygen atoms, given in cu cm/atom) of the polymers, and to determine if atomic oxygen erosion of high and low ash containing polymers is dependent on fluence. The Zenith Polymers Experiment was flown in a zenith flight orientation. The primary objective of the Zenith Polymers Experiment was to determine the effect of solar exposure on the erosion of fluoropolymers. Kapton H (DuPont, Wilmington, DE) was flown in each experiment for atomic oxygen fluence determination. This paper provides an introduction to both the MISSE 7 Polymers Experiment and the MISSE 7 Zenith Polymers Experiment, and provides initial erosion yield results
Erosion Results of the MISSE 8 Polymers Experiment After 2 Years of Space Exposure on the International Space Station
Polymers and other oxidizable materials on the exterior of spacecraft in the low Earth orbit (LEO) space environment can be eroded due to reaction with atomic oxygen (AO). Therefore, in order to design durable spacecraft, it is important to know the LEO AO erosion yield (E(sub y), volume loss per incident oxygen atom) of materials susceptible to AO reaction. A spaceflight experiment, called the Polymers Experiment, which contained 42 samples, was developed to determine the effect of solar exposure on the AO E(sub y) of fluoropolymers flown in ram, wake, or zenith orientations. The Polymers Experiment was exposed to the LEO space environment on the exterior of the International Space Station (ISS) as part of the Materials International Space Station Experiment 8 (MISSE 8) mission. The MISSE 8 mission included samples flown in a zenith/nadir orientation for 2.14 years in the MISSE 8 Passive Experiment Container (PEC), and samples flown in a ram/wake orientation for 2.0 years in the Optical Reflector Materials Experiment-III (ORMatEIII) tray. The experiment included Kapton H (Registered Trademark) witness samples for AO fluence determination in each orientation. This paper provides an overview of the MISSE 8 mission, a description of the flight experiment with details on the polymers flown, the characterization techniques used, the AO fluence for each exposure orientation, and the LEO E(sub y) results. The E(sub y) of Teflon fluorinated ethylene propylene (FEP) samples flown in ram, wake, and zenith orientations have been compared, and the E(sub y) was found to be highly dependent on orientation and therefore environmental exposure. The FEP E(sub y) was found to directly correlate with the solar exposure/AO fluence ratio showing the effect of solar radiation and/or heating due to solar exposure on FEP erosion. In addition, back-surface carbon painted FEP (C-FEP) flown in the zenith orientation had a significantly higher E(sub y) than clear FEP or Al-FEP further indicating that heating has a significant impact on the erosion of FEP. This experiment provides valuable LEO flight data on the erosion of Teflon FEP, a commonly used spacecraft thermal insulation
MISSE 6 Stressed Polymers Experiment Atomic Oxygen Erosion Data
Polymers and other oxidizable materials used on the exterior of spacecraft in the low Earth orbit (LEO) space environment can be eroded away by reaction with atomic oxygen (AO). For spacecraft design, it is important to know the LEO AO erosion yield, Ey (volume loss per incident oxygen atom), of materials susceptible to AO erosion. The Stressed Polymers Experiment was developed and flown as part of the Materials International Space Station Experiment 6 (MISSE 6) to compare the AO erosion yields of stressed and non-stressed polymers to determine if erosion is dependent upon stress while in LEO. The experiment contained 36 thin film polymer samples that were exposed to ram AO for 1.45 years. This paper provides an overview of the Stressed Polymers Experiment with details on the polymers flown, the characterization techniques used, the AO fluence, and the erosion yield results. The MISSE 6 data are compared to data for similar samples flown on previous MISSE missions to determine fluence or solar radiation effects on erosion yield
Erosion Data from the MISSE 8 Polymers Experiment After 2 Years of Space Exposure on the International Space Station
The Polymers Experiment was exposed to the low Earth orbit (LEO) space environment for 2.14 and 2.0 years as part of the Materials International Space Station Experiment 8 (MISSE 8) and the Optical Reflector Materials Experiment-III (ORMatE-III), respectively. The experiment contained 42 samples, which were flown in either ram, wake, or zenith orientations. The primary objective was to determine the effect of solar exposure on the atomic oxygen erosion yield (Ey) of fluoropolymers. This paper provides an overview of the experiment with details on the polymers flown, the characterization techniques used, the atomic oxygen fluence for each exposure orientation, and the LEO Ey results. The Ey values for the fluoropolymers range from 1.45 x 10(exp -25) cm(exp 3)/atom for white Tedlar Registered Trademark (polyvinyl fluoride with white titanium dioxide pigment) flown in the ram orientation to 6.32 x 10(exp -24) cm(exp 3)/atom for aluminized-Teflon Registered Trademark fluorinated ethylene propylene (Al-FEP) flown in the zenith orientation. Erosion yield data for FEP flown in ram, wake and zenith orientations are compared, and the Ey was found to be highly dependent on orientation, hence environmental exposure. Teflon FEP had an order of magnitude higher Ey when flown in the zenith direction (6.32 x10(exp -24) cm(exp3)/atom) as compared to the ram direction (2.37 x 10(exp -25) cm(exp 3)/atom). The Ey of FEP was found to increase with a direct correlation to the solar exposure/AO fluence ratio showing the effect of solar radiation and/or heating due to solar exposure on FEP erosion. In addition, back-surface carbon painted FEP (C-FEP) flown in the zenith orientation had a significantly higher Ey than clear FEP or Al-FEP further indicating that heating has a significant impact on the erosion of FEP, particularly in the zenith orientation
Vacancy-Mediated Magnetism in Pure Copper Oxide Nanoparticles
Room temperature ferromagnetism (RTF) is observed in pure copper oxide (CuO) nanoparticles which were prepared by precipitation method with the post-annealing in air without any ferromagnetic dopant. X-ray photoelectron spectroscopy (XPS) result indicates that the mixture valence states of Cu1+ and Cu2+ ions exist at the surface of the particles. Vacuum annealing enhances the ferromagnetism (FM) of CuO nanoparticles, while oxygen atmosphere annealing reduces it. The origin of FM is suggested to the oxygen vacancies at the surface/or interface of the particles. Such a ferromagnet without the presence of any transition metal could be a very good option for a class of spintronics
Expanded RNA-binding activities of mammalian Argonaute 2
Mammalian Argonaute 2 (Ago2) protein associates with microRNAs (miRNAs) or small interfering RNAs (siRNAs) forming RNA-induced silencing complexes (RISCs/miRNPs). In the present work, we characterize the RNA-binding and nucleolytic activity of recombinant mouse Ago2. Our studies show that recombinant mouse Ago2 binds efficiently to miRNAs forming active RISC. Surprisingly, we find that recombinant mouse Ago2 forms active RISC using pre-miRNAs or long unstructured single stranded RNAs as guides. Furthermore, we demonstrate that, in vivo, endogenous human Ago2 binds directly to pre-miRNAs independently of Dicer, and that Ago2:pre-miRNA complexes are found both in the cytoplasm and in the nucleus of human cells
Rituximab for Children with Immune Thrombocytopenia: A Systematic Review
BACKGROUND: Rituximab has been widely used off-label as a second line treatment for children with immune thrombocytopenia (ITP). However, its role in the management of pediatric ITP requires clarification. To understand and interpret the available evidence, we conducted a systematic review to assess the efficacy and safety of rituximab for children with ITP. METHODOLOGY/PRINCIPAL FINDINGS: We searched MEDLINE, EMBASE, Cochrane Library, CBM, CNKI, abstract databases of American Society of Hematology, American Society of Clinical Oncology and Pediatric Academic Society. Clinical studies published in full text or abstract only in any language that met predefined inclusion criteria were eligible. Efficacy analysis was restricted to studies enrolling 5 or more patients. Safety was evaluated from all studies that reported data of toxicity. 14 studies (323 patients) were included for efficacy assessment in children with primary ITP. The pooled complete response (platelet count ≥ 100 × 10(9)/L) and response (platelet count ≥ 30 × 10(9)/L) rate after rituximab treatment were 39% (95% CI, 30% to 49%) and 68% (95%CI, 58% to 77%), respectively, with median response duration of 12.8 month. 4 studies (29 patients) were included for efficacy assessment in children with secondary ITP. 11 (64.7%) of 17 patients associated with Evans syndrome achieved response. All 6 patients with systemic lupus erythematosus associated ITP and all 6 patients with autoimmune lymphoproliferative syndrome associated ITP achieved response. 91 patients experienced 108 adverse events associated with rituximab, among that, 91 (84.3%) were mild to moderate, and no death was reported. CONCLUSIONS/SIGNIFICANCE: Randomized controlled studies on effect of rituximab for children with ITP are urgently needed, although a series of uncontrolled studies found that rituximab resulted in a good platelet count response both in children with primary and children secondary ITP. Most adverse events associated with rituximab were mild to moderate, and no death was reported
Economic burden of neural tube defects and impact of prevention with folic acid: a literature review
Neural tube defects (NTDs) are the second most common group of serious birth defects. Although folic acid has been shown to reduce effectively the risk of NTDs and measures have been taken to increase the awareness, knowledge, and consumption of folic acid, the full potential of folic acid to reduce the risk of NTDs has not been realized in most countries. To understand the economic burden of NTDs and the economic impact of preventing NTDs with folic acid, a systematic review was performed on relevant studies. A total of 14 cost of illness studies and 10 economic evaluations on prevention of NTDs with folic acid were identified. Consistent findings were reported across all of the cost of illness studies. The lifetime direct medical cost for patients with NTDs is significant, with the majority of cost being for inpatient care, for treatment at initial diagnosis in childhood, and for comorbidities in adult life. The lifetime indirect cost for patients with spina bifida is even greater due to increased morbidity and premature mortality. Caregiver time costs are also significant. The results from the economic evaluations demonstrate that folic acid fortification in food and preconception folic acid consumption are cost-effective ways to reduce the incidence and prevalence of NTDs. This review highlights the significant cost burden that NTDs pose to healthcare systems, various healthcare payers, and society and concludes that the benefits of prevention of NTDs with folic acid far outweigh the cost. Further intervention with folic acid is justified in countries where the full potential of folic acid to reduce the risk of NTDs has not been realized
Antimicrobial resistance among migrants in Europe: a systematic review and meta-analysis
BACKGROUND: Rates of antimicrobial resistance (AMR) are rising globally and there is concern that increased migration is contributing to the burden of antibiotic resistance in Europe. However, the effect of migration on the burden of AMR in Europe has not yet been comprehensively examined. Therefore, we did a systematic review and meta-analysis to identify and synthesise data for AMR carriage or infection in migrants to Europe to examine differences in patterns of AMR across migrant groups and in different settings. METHODS: For this systematic review and meta-analysis, we searched MEDLINE, Embase, PubMed, and Scopus with no language restrictions from Jan 1, 2000, to Jan 18, 2017, for primary data from observational studies reporting antibacterial resistance in common bacterial pathogens among migrants to 21 European Union-15 and European Economic Area countries. To be eligible for inclusion, studies had to report data on carriage or infection with laboratory-confirmed antibiotic-resistant organisms in migrant populations. We extracted data from eligible studies and assessed quality using piloted, standardised forms. We did not examine drug resistance in tuberculosis and excluded articles solely reporting on this parameter. We also excluded articles in which migrant status was determined by ethnicity, country of birth of participants' parents, or was not defined, and articles in which data were not disaggregated by migrant status. Outcomes were carriage of or infection with antibiotic-resistant organisms. We used random-effects models to calculate the pooled prevalence of each outcome. The study protocol is registered with PROSPERO, number CRD42016043681. FINDINGS: We identified 2274 articles, of which 23 observational studies reporting on antibiotic resistance in 2319 migrants were included. The pooled prevalence of any AMR carriage or AMR infection in migrants was 25·4% (95% CI 19·1-31·8; I2 =98%), including meticillin-resistant Staphylococcus aureus (7·8%, 4·8-10·7; I2 =92%) and antibiotic-resistant Gram-negative bacteria (27·2%, 17·6-36·8; I2 =94%). The pooled prevalence of any AMR carriage or infection was higher in refugees and asylum seekers (33·0%, 18·3-47·6; I2 =98%) than in other migrant groups (6·6%, 1·8-11·3; I2 =92%). The pooled prevalence of antibiotic-resistant organisms was slightly higher in high-migrant community settings (33·1%, 11·1-55·1; I2 =96%) than in migrants in hospitals (24·3%, 16·1-32·6; I2 =98%). We did not find evidence of high rates of transmission of AMR from migrant to host populations. INTERPRETATION: Migrants are exposed to conditions favouring the emergence of drug resistance during transit and in host countries in Europe. Increased antibiotic resistance among refugees and asylum seekers and in high-migrant community settings (such as refugee camps and detention facilities) highlights the need for improved living conditions, access to health care, and initiatives to facilitate detection of and appropriate high-quality treatment for antibiotic-resistant infections during transit and in host countries. Protocols for the prevention and control of infection and for antibiotic surveillance need to be integrated in all aspects of health care, which should be accessible for all migrant groups, and should target determinants of AMR before, during, and after migration. FUNDING: UK National Institute for Health Research Imperial Biomedical Research Centre, Imperial College Healthcare Charity, the Wellcome Trust, and UK National Institute for Health Research Health Protection Research Unit in Healthcare-associated Infections and Antimictobial Resistance at Imperial College London
- …