Internal plate fixation of fractures: short history and recent developments

Metal plates for internal fixation of fractures have been used for more than 100 years. Although initial shortcomings such as corrosion and insufficient strength have been overcome, more recent designs have not solved all problems. Further research is needed to develop a plate that accelerates fracture healing while not interfering with bone physiology

Supraspinatus tendon transosseous vs anchor repair surgery: a comparative study of mechanical recovery in the rabbit

Background: Supraspinatus (SSP) tendon ruptures requiring surgical repair are common. Arthroscopic suture anchor fixation has gradually replaced transosseous repair in supraspinatus tendon tear. Our objective was to compare mechanical properties between transosseous and anchor supraspinatus repair in the first 6 postoperative weeks in a rabbit model. Methods: One hundred and fifty-two rabbits had one supraspinatus tendon repaired either with an anchor suture 1 week after detachment or with transosseous sutures. Rabbits were euthanized at 0, 1, 2, 4 or 6 postoperative weeks. Experimental and contralateral tendons (304 tendons) were mechanically tested to failure. Data are expressed as percent of contralateral. Results: Anchor repair had higher loads to failure compared to transosseous repair, at immediate repair (week 0, 52 ± 21% vs 25 ± 17%, respectively; p = 0.004) and at 1 postoperative week (64 ± 32% vs 28 ± 10%; p = 0.003) with no difference after 2 weeks. There was no difference in stiffness. Transosseous repairs showed higher rates of midsubstance failures compared to anchor repairs at 1 (p = 0.004) and 2 postoperative weeks (p < 0.001). Both transosseous and anchor repairs restored supraspinatus mechanical properties after 4 postoperative weeks. Conclusion: Anchor repair provided better initial tensile strength while transosseous repair led to a faster normalization (namely, midsubstance) of the mode of failure. Research to optimize supraspinatus repair may need to consider the advantages from both surgical approache

Zur Siderosis retinae et bulbi. Ein Beitrag zu den Eisensplitterverletzungen des Auges 1 )

n/

Quantitative analysis of bone reactions to relative motions at implant-bone interfaces

Connective soft tissues at the interface between implants and bone, such as in human joint replacements, can endanger the stability of the implant fixation. The potential of an implant to generate interface bone resorption and form soft tissue depends on many variables, including mechanical ones. These mechanical factors can be expressed in terms of relative motions between bone and implant at the interface or deformation of the interfacial material.\ud \ud The purpose of this investigation was to determine if interface debonding and subsequent relative interface motions can be responsible for interface degradation and soft tissue interposition as seen in experiments and clinical results. A finite element computer program was augmented with a mathematical description of interface debonding, dependent on interface stress criteria, and soft tissue interface interposition, dependent on relative interface motions. Three simplified models of orthopaedic implants were constructed: a cortical bone screw for fracture fixation plates, a femoral resurfacing prosthesis and a straight stem model, cemented in a bone. The predicted computer configurations were compared with clinical observations. The computer results showed how interface disruption and fibrous tissue interposition interrelate and possibly enhance each other, whereby a progressive development of the soft tissue layer can occur.\ud \ud Around the cortical bone screw, the predicted resorption patterns were relatively large directly under the screw head and showed a pivot point in the opposite cortex. The resurfacing cup model predicted some fibrous tissue formation under the medial and lateral cup rim, whereby the medial layer developed first because of higher initial interface stresses. The straight stem model predicted initial interface failure at the proximal parts. After proximal resorption and fibrous tissue interposition, the medial interface was completely disrupted and developed an interface layer. The distal and mid lateral side maintained within the strength criterion.\ud \ud Although the applied models were relatively simple, the results showed reasonable qualitative agreement with resorption patterns found in clinical studies concerning bone screws and the resurfacing cup. The hypothesis that interface debonding and subsequent relative (micro)motions could be responsible for bone resorption and fibrous tissue propagation is thereby sustained by the results

Pulsed Radiofrequency Lesioning of the Axillary and Suprascapular Nerve in Calcific Tendinitis

The patient was a 45-year-female who presented with pain at right shoulder and right upper arm. The patient suffered from right shoulder and arm pain for 3 years and had pain management which was performed using medication and conservative management after she had been diagnosed with calcific tendinitis. However, substantial pain relief was not consistently achieved, and recurrence of pain was reported. Therefore, we performed right axillary nerve and suprascapular nerve block through pulsed radiofrequency. Two months after the procedure, the shoulder pain gradually subsided with the size reduction of the calcified nodule and she needed no more pain management

Mineralization can be an incidental ultrasonographic finding in equine tendons and ligaments

Tendon/ligament mineralization is recognized in horses but information regarding its clinical significance is limited. The aims of this observational study were to report the structures most commonly affected by ultrasonographically detectable mineralization and, for these, determine frequency of diagnosis and key clinical features. Cases presented at our hospital in April 1999–April 2013 and September 2014–November 2015 were included: a total of 27 horses (22 retrospective, five prospective). Mineralizations were most common in deep digital flexor tendons (10) and suspensory ligament branches (eight), representing 10% and 7% (estimated), respectively, of horses diagnosed with injuries to these structures during the study. Two deep digital flexor tendon and three suspensory ligament branch cases showed bilateral mineralization. Deep digital flexor tendon mineralization was restricted to the digital flexor tendon sheath, most commonly in the proximal sheath (±sesamoidean canal), and seven of 10 cases involved hindlimbs. Suspensory ligament branch mineralization was visible in the same ultrasound window as the proximal sesamoid bones in 10/11 limbs and six of eight cases involved forelimbs. Previous corticosteroid medication was a feature of one deep digital flexor tendon and one suspensory ligament branch case. Mineralization was associated with lameness in some but not all limbs. Mineralized foci within the deep digital flexor tendon preceded hypoechoic lesion formation in two limbs. Of the cases with deep digital flexor tendon or suspensory ligament branch injury only, one of three and two of three cases, respectively, became sound. Findings indicated that tendon/ligament mineralization can be associated with lameness in some horses, but can also be an incidental finding

Peak strain magnitudes and rates in the tibia exceed greatly those in the skull: An in vivo study in a human subject

Bone mass and architecture are the result of a genetically determined baseline structure, modified by the effect of internal hormonal/biochemical regulators and the effect of mechanical loading. Bone strain is thought to drive a feedback mechanism to regulate bone formation and resorption to maintain an optimal, but not excessive mass and organisation of material at each skeletal location. Because every site in the skeleton has different functions, we have measured bone strains induced by physiological and more unusual activities, at two different sites, the tibia and cranium of a young human male in vivo. During the most vigorous activities, tibial strains were shown to exceed 0.2%, when ground reaction exceeded 5 times body weight. However in the skull the highest strains recorded were during heading a heavy medicine/exercise ball where parietal strains were up to 0.0192%. Interestingly parietal strains during more physiological activities were much lower, often below 0.01%. Strains during biting were not dependent upon bite force, but could be induced by facial contortions of similar appearance without contact between the teeth. Rates of strain change in the two sites were also very different, where peak tibial strain rate exceeded rate in the parietal bone by more than 5 fold. These findings suggest that the skull and tibia are subject to quite different regulatory influences, as strains that would be normal in the human skull would be likely to lead to profound bone loss by disuse in the long bones

An Analytical Model for Rotator Cuff Repairs

Background: Currently, natural and synthetic scaffolds are being explored as augmentation devices for rotator cuff repair. When used in this manner, these devices are believed to offer some degree of load sharing; however, no studies have quantified this effect. Furthermore, the manner in which loads on an augmented rotator cuff repair are distributed among the various components of the repair is not known, nor is the relative biomechanical importance of each component. The objectives of this study are to (1) develop quasi-static analytical models of simplified rotator cuff repairs, (2) validate the models, and (3) predict the degree of load sharing provided by an augmentation scaffold. Methods: The individual components of the repair constructs were modeled as non-linear springs, and the model equations were formulated based on the physics of springs in series and parallel. The model was validated and used to predict the degree of load sharing provided by a scaffold. Parametric sensitivity analysis was used to identify which of the component(s)/parameter(s) most influenced the mechanical behavior of the augmented repair models. Findings: The validated models predict that load will be distributed ~70-80% to the tendon repair and ~20-30% to the augmentation component. The sensitivity analysis suggests that the greatest improvements in the force carrying capacity of a tendon repair may be achieved by improving the properties of the bone-suture-tendon interface. Future studies will perform parametric simulation to illustrate the manner in which changes to the individual components of the repair, representing different surgical techniques and scaffold devices, may influence the biomechanics of the repair construct