Enhancing Osteoconduction of PLLA-Based Nanocomposite Scaffolds for Bone Regeneration Using Different Biomimetic Signals to MSCs

In bone engineering, the adhesion, proliferation and differentiation of mesenchymal stromal cells rely on signaling from chemico-physical structure of the substrate, therefore prompting the design of mimetic “extracellular matrix”-like scaffolds. In this study, three-dimensional porous poly-L-lactic acid (PLLA)-based scaffolds have been mixed with different components, including single walled carbon nanotubes (CNT), micro-hydroxyapatite particles (HA), and BMP2, and treated with plasma (PT), to obtain four different nanocomposites: PLLA + CNT, PLLA + CNTHA, PLLA + CNT + HA + BMP2 and PLLA + CNT + HA + PT. Adult bone marrow mesenchymal stromal cells (MSCs) were derived from the femur of orthopaedic patients, seeded on the scaffolds and cultured under osteogenic induction up to differentiation and mineralization. The release of specific metabolites and temporal gene expression profiles of marrow-derived osteoprogenitors were analyzed at definite time points, relevant to in vitro culture as well as in vivo differentiation. As a result, the role of the different biomimetic components added to the PLLA matrix was deciphered, with BMP2-added scaffolds showing the highest biomimetic activity on cells differentiating to mature osteoblasts. The modification of a polymeric scaffold with reinforcing components which also work as biomimetic cues for cells can effectively direct osteoprogenitor cells differentiation, so as to shorten the time required for mineralization

Biodegradable Composites : Processing of thermoplastic polymers for medical applications.

Despite the recent development in PLA and PLGA based medical devices, there are still needs to further improve the mechanical performance of bioresorbable medical implants and their bioactivity. This is normally done by optimizing the filler compositions in selected groups ofbiodegradable polymer matrices. In this study, the effects of various filler levels on mechanical strength and thermal properties of PLA and PLGA composites were investigated. Composites containing different dosage of osteoconductive HAp with various particles size (0-5μm, 0-50 μm, nano size), β-TCP, bioactive glass and biodegradable Poly-L-lactide and Polylactide-glycolic acid was manufactured with melt blending, using a twin-screw extruder.The samples were investigated by Differential Scanning Calorimetry (DSC), thermo gravimetric analysis (TGA), Scanning Electron Microscopy (SEM), viscometer, three points bending machine, and Optical Microscopy (OM). The Extruder produced a porous profile. The result from TGA and SEM indicated that there was homogenous filler dispersion in the matrix after compounding.The result from DSC and Viscometer shows that there was some degradation duringcompounding. Mechanical properties of composites were modified by adding filler to matrix. The addition of Bioactive glass, as a filler, increases the degradation of the polymer matrix. The best filler that was applied is 0-5μm and nano HAp. Also in in-vitro degradation part of this thesis work, the effects of calcium phosphate materialsare investigated on degradation process

Biodegradable Composites : Processing of thermoplastic polymers for medical applications.

Despite the recent development in PLA and PLGA based medical devices, there are still needs to further improve the mechanical performance of bioresorbable medical implants and their bioactivity. This is normally done by optimizing the filler compositions in selected groups ofbiodegradable polymer matrices. In this study, the effects of various filler levels on mechanical strength and thermal properties of PLA and PLGA composites were investigated. Composites containing different dosage of osteoconductive HAp with various particles size (0-5μm, 0-50 μm, nano size), β-TCP, bioactive glass and biodegradable Poly-L-lactide and Polylactide-glycolic acid was manufactured with melt blending, using a twin-screw extruder.The samples were investigated by Differential Scanning Calorimetry (DSC), thermo gravimetric analysis (TGA), Scanning Electron Microscopy (SEM), viscometer, three points bending machine, and Optical Microscopy (OM). The Extruder produced a porous profile. The result from TGA and SEM indicated that there was homogenous filler dispersion in the matrix after compounding.The result from DSC and Viscometer shows that there was some degradation duringcompounding. Mechanical properties of composites were modified by adding filler to matrix. The addition of Bioactive glass, as a filler, increases the degradation of the polymer matrix. The best filler that was applied is 0-5μm and nano HAp. Also in in-vitro degradation part of this thesis work, the effects of calcium phosphate materialsare investigated on degradation process

Development and characterization of a PLGA-HA composite material to fabricate 3D-printed scaffolds for bone tissue engineering

Additive manufacturing is a rising field in bone tissue engineering. Additive fabrication offers reproducibility, high precision and rapid manufacture of custom patient-specific scaffolds. The development of appropriate composite materials for biomedical applications is critical to reach clinical application of these novel biomaterials. In this work, medical grade poly(lactic-co-glycolic) acid (PLGA) was mixed with hydroxyapatite nanoparticles (nHA) to fabricate 3D porous scaffolds by Fused Deposition Modeling. We have first confirmed that the composite material could be printed in a reproductive manner. Physical characterization demonstrated a low degradation of the material during manufacturing steps and an expected loading and homogeneous distribution of nHA. In vitro biodegradation of the scaffolds showed modifications of morphological and physicochemical properties over time. The composite scaffolds were biocompatible and high cell viability was observed in vitro, as well as a maintain of cell proliferation. As expected, the addition of nHA displayed a positive impact on osteodifferentiation in vitro. Furthermore, a limited inflammatory reaction was observed after subcutaneous implantation of the materials in the rat. Overall, this study suggests that this composite material is suitable for bone tissue engineering applications.Fabrication d'un substitut osseux pour la chirurgie orale par assemblage multi-couches de membranes cellularisée