6 research outputs found
Superconducting ceramics in the Bi1.5SrCaCu2O sub x system by melt quenching technique
Bi sub 1.5 SrCaCu sub 2 O sub x has been prepared in the glassy state by rapid quenching of the melt. The kinetics of crystallization of various phases in the glass have been evaluated by a variable heating rate differential scanning calorimetry method. The formation various phases on thermal treatments of the glass has been investigated by powder X-ray diffraction and electrical resistivity measurements. Heating at 450 C formed Bi sub 2 Sr sub 2 CuO sub 6, which disappeared on further heating at 765 C, where Bi sub 2 Sr sub 2 CaCu sub 2 O sub 8 formed. Prolonged heating at 845 C resulted in the formation of a small amount of a phase with T sub c onset of approx. 108 K, believed to be Bi sub 2 Sr sub 2 Ca sub 2 Cu sub 3 O sub 10. This specimen showed zero resistivity at 54 K. The glass ceramic approach could offer several advantages in the fabrication of the high-T sub c superconductors in desired practical shapes such as continuous fibers, wires, tapes, etc
Ultrasonic evaluation of oxidation and reduction effects on the elastic behavior and global microstructure of YBa2Cu3O7-x
Ultrasonic velocity measurement techniques were used to evaluate the effects of oxidation and reduction on the elastic properties, global microstructure and oxygen content of the YBa2Cu3O(7-x) ceramic superconductor for samples ranging from 70 to 90 pct. of theoretical density. Bulk density, velocity, and elastic modulus generally increased with increasing oxygen content upon oxidation, and this behavior was reversible. Velocity image patterns were similar after oxidation and reduction treatments for a 90 pct. dense sample, although the velocity value at any given point on the sample was changed following the treatments. The unchanging pattern correlated with destructive measurements showing that the spatial pore distribution (fraction and size) was not measurably altered after the treatments. Changes in superconducting behavior, crystal structure, and grain structure were observed consistent with changes in oxygen content
Electrical Conductivity, Relaxation and the Glass Transition: A New Look at a Familiar Phenomenon
Annealed samples from a single melt of a 10 mol% K2O-90SiO2 glass were reheated to temperatures ranging from 450 to 800 C, held isothermally for 20 min, and then quenched in either air or a silicon oil bath. The complex impedance of both the annealed and quenched samples was measured as a function of temperature from 120 to 250 C using ac impedance spectroscopy from 1 Hz to 1 MHz. The dc conductivity, sigma(sub dc), was measured from the low frequency intercept of depressed semicircle fits to the complex impedance data. When the sigma(sub dc) at 150 C was plotted against soak temperature, the results fell into three separate regions that are explained in terms of the glass structural relaxation time, tau(sub S). This sigma(sub dc) plot provides a new way to look the glass transition range, Delta T(sub r). In addition, sigma(sub dc) was measured for different soak times at 550 C, from which an average relaxation time of 7.3 min was calculated. It was found that the size and position of the Delta T(sub r) is controlled by both the soak time and cooling rate
The series Bi2Sr2Ca(n-1) Cu(n)O(2n+4) (1 less than or equal to n less than or equal to 5): Phase stability and superconducting properties
Phase relations at 850 and 870 C, melting transitions in air, oxygen, and helium were studied for Bi(2.1)Sr(1.9) CuO6 and for the Bi2Sr2Ca(n-1) Cu(n)O(2n+4) for n = 1, 2, 3, 4, 5, and infinity (CaCuO2). Up to 870 C, the n = 2 composition resides in the compatibility tetrahedron bounded by Bi(2+x)(Sr,Ca)(3-y) Cu2O8, (Sr,Ca)14 Cu24O41, Ca2CuO3, and a Bi-Sr-Ca-O phase. The n is greater than or equal to 3 compositions reside in the compatibility tetrahedron Bi(2+x)(Sr,Ca)(3-y) Cu2O8 - (Sr,Ca)14 Cu24O41 - Ca2CuO3 - CuO up to 850 C. However, Bi(2+x)Sr(4-y) Cu3O10 forms for n is greater than or equal to 3 after extended heating at 870 C. Bi(2+x)Sr(2-y) CuO6 and Bi(2+x)(Sr,Ca)(3-y) Cu2O8 melt in air at 914 C and 895 C respectively. During melting, all of the compositions studied lose 1 to 2 percent by weight of oxygen from the reduction of copper. Bi(2+x)Sr(2-y) CuO6, Bi(2+n)(Sr,Ca)(3-y) Cu2O8, and Bi(2+x)(Sr,Ca)(4-y) Cu3O10 exhibit crystallographic alignment in a magnetic field, with the c-axes orienting parallel to the field