Porosity enhancement of biochar derived from rubber sawdust using steam injection at low temperature

Biochar is extremely interesting for energy and environment applications such assoil amender, sorbent materials and biofuels. In this study, rubber sawdust (RS) was prepared through the pyrolysis at 400 and 600°C with low and high heating rate (7 and 20°C/min) for 60 minutes.The pyrolytic parameters have a strong influence on biochar properties. Biochar yield was decreased from 33.1 to 22.6 wt% due to increasing of pyrolytic temperature. The higest BET surface area of biochar previous enhanced porosity was found about 410 m2/g at 600°C with 20°C/min of heating rate with particle size 0.3-1 mm. Afterwards, biochar porosity was enhanced through the steam injection process. Furthermore, the physicochemical properties of biochar product (i.e. surface morphology, BET surface area, and N2adsorption isotherm) will be characterized. (Texte intégral

Mesoporous RF-Xerogels by Facile Hydrothermal Synthesis

Mesoporous resorcinol-formaldehyde (RF) xerogels were difficult to obtain by conventional sol-gel polymerization at atmospheric pressure because the resulting tenuous RF-gel structures tended to shrink or collapse during subsequent hot-air drying. To avoid this problem, costly and energy-intensive supercritical drying and freeze-drying are often used. In this work the main goal was to produce high-quality RF xerogels with good mesoporosity and high surface area by employing a hydrothermal process. The hydrogel synthesis was carried out in an autoclave at elevated temperature and pressure in order to sufficiently strengthen its network structure. The initial reactant ratio was held constant to search for most suitable hydrothermal temperature and initial pH. The experimental results showed that the reaction in the autoclave at 140ºC and initial pH of 6 could successfully produce RF xerogels with good mesoporosity (peaking pore radius rpeak = 2.38 nm), high specific surface area and large pore volume. The hydrothermal process was on the overall relatively simple, low-cost, and less time-consuming compared to the conventional atmospheric method

Recent advances in hydrothermal carbonisation:from tailored carbon materials and biochemicals to applications and bioenergy

Introduced in the literature in 1913 by Bergius, who at the time was studying biomass coalification, hydrothermal carbonisation, as many other technologies based on renewables, was forgotten during the "industrial revolution". It was rediscovered back in 2005, on the one hand, to follow the trend set by Bergius of biomass to coal conversion for decentralised energy generation, and on the other hand as a novel green method to prepare advanced carbon materials and chemicals from biomass in water, at mild temperature, for energy storage and conversion and environmental protection. In this review, we will present an overview on the latest trends in hydrothermal carbonisation including biomass to bioenergy conversion, upgrading of hydrothermal carbons to fuels over heterogeneous catalysts, advanced carbon materials and their applications in batteries, electrocatalysis and heterogeneous catalysis and finally an analysis of the chemicals in the liquid phase as well as a new family of fluorescent nanomaterials formed at the interface between the liquid and solid phases, known as hydrothermal carbon nanodots

Parametric Study on Microwave-Assisted Pyrolysis Combined KOH Activation of Oil Palm Male Flowers Derived Nanoporous Carbons

Oil palm male flowers (PMFs), an abundant agricultural waste from oil palm plantation in Thailand, have been utilized as an alternative precursor to develop nanoporous carbons (NPCs) via microwave-assisted pyrolysis combined potassium hydroxide (KOH) activation. The influences of relevant processing variables, such as activating agent ratio, microwave power, and activation time on the specific pore characteristics, surface morphology, and surface chemistry of PMFs derived nanoporous carbons (PMFCs) have been investigated to explore the optimum preparation condition. The optimum condition under a microwave radiation power of 700 W, activation holding time of 6 min, and activating agent ratio of 2:1 obtained the PMFC with the highest Brunauer–Emmett–Teller (BET) surface area and total pore volume approximately of 991 m2/g and 0.49 cm3/g, composed of a carbon content of 74.56%. Meanwhile, PMFCs have a highly microporous structure of about 71.12%. Moreover, activating agent ratio and microwave radiation power indicated a significant influence on the surface characteristics of PMFCs. This study revealed the potential of oil palm male flowers for the NPCs’ production via microwave-assisted KOH activation with a short operating-time condition

Biomass Nanoporous Carbon-Supported Pd Catalysts for Partial Hydrogenation of Biodiesel: Effects of Surface Chemistry on Pd Particle Size and Catalytic Performance

Two types of cattail flower-derived nanoporous carbon (NPC), i.e., NPC activated with KOH and H3PO4, were produced and characterized using several techniques (e.g., Raman spectroscopy, nitrogen adsorption, and X-ray photoelectron spectroscopy). The influence of the carbon support characteristics on the particle sizes and chemical states of Pd in the synthesized Pd/NPC catalysts, which affect the catalytic activity and product selectivity, was analyzed. The surface chemistry properties of NPC were the main factors influencing the Pd particle size; by contrast, the textural properties did not significantly affect the size of the Pd particles on NPC supports. The use of Pd nanoparticles supported on the rich-functionalized surface carbons obtained by H3PO4 activation led to superior catalytic activity for the polyunsaturated fatty acid methyl ester (poly-FAME) hydrogenation, which could achieve 90% poly-FAME conversion and 84% selectivity towards monounsaturated FAME after a 45-min reaction time. This is due to the small Pd nanoparticle size and the high acidity of the catalysts, which are beneficial for the partial hydrogenation of poly-FAME in biodiesel. Conversely, the Pd nanoparticles supported on the high-surface-area carbon by KOH activation, with large Pd particle size and low acidity, required a longer reaction time to reach similar conversion and product selectivity levels

Palm Oil Conversion to Bio-Jet and Green Diesel Fuels over Cobalt Phosphide on Porous Carbons Derived from Palm Male Flowers

Porous carbon was successfully synthesized from palm male flowers (PMFs), using microwave-assisted potassium hydroxide (KOH) activation and was used as a catalyst support for the conversion of palm oil into bio-hydrocarbons, in fractions of green diesel and bio-jet fuel. Palm male flower-derived porous carbon (PC), consolidated with well dispersed cobalt phosphide (CoP) nanoparticles, was synthesized by simple wet-impregnation with subsequent thermal treatment. The physicochemical properties of the synthesized CoP/PC catalysts were evaluated by various techniques including proximate and ultimate elemental analysis, FTIR, XRD, N2 sorption, SEM, TEM–EDS, and NH3-temperature programmed desorption (TPD). The effects of the pyrolysis temperatures (600−900 °C), used for the impregnated samples before the reduction process, on catalyst properties and catalytic performance were investigated. Moreover, the effect of a liquid hourly space velocity of 0.5–1.5 h−1 and reaction temperatures of 340–420 °C was studied in the palm oil conversion. The catalyst pyrolyzed at 600 °C possessed the greatest particle dispersion and surface area, and showed the highest yield of liquid hydrocarbon product (C9–C18). We also found that the high pyrolysis temperature above 800 °C partially transformed the Co2P phase into CoP one which significantly exhibited higher cracking activity and bio-jet selectivity, due to the improved acidity of the catalyst

Nanoporous Carbon from Oil Palm Leaves via Hydrothermal Carbonization-Combined KOH Activation for Paraquat Removal

In this study, nano-porous carbon was completely obtained from oil palm leaves (OPL) by hydrothermal pretreatment with chemical activation, using potassium hydroxide (KOH) as an activating agent. Potassium hydroxide was varied, with different ratios of 1:0.25, 1:1, and 1:4 (C: KOH; w/w) during activation. The physical morphology of nano-porous carbon has a spongy, sponge-like structure indicating an increase in specific surface area and porosity with the increasing amount of KOH activating agent. The highest specific surface area of OPL nano-porous carbon is approximately 1685 m2·g−1, with a total pore volume of 0.907 cm3·g−1. Moreover, the OPL nano-porous carbon significantly showed a mesoporous structure designed specifically to remove water pollutants. The adsorptive behavior of OPL nano-porous carbon was quantified by using paraquat as the target pollutant. The equilibrium analyzes were explained by the Langmuir model isotherm and pseudo-second-order kinetics. The maximum efficiency of paraquat removal in wastewater was 79%, at a paraquat concentration of 400 mg·L−1, for 10 min in the adsorption experiment. The results of this work demonstrated the practical application of nano-porous carbon derived from oil palm leaves as an alternative adsorbent for removing paraquat and other organic matter in wastewater