Background and Purpose: Antioxidant enzymes like copper/ zinc superoxide dismutase (SOD), catalase and gluthatione peroxidase (GSHPx) are part of intracellular protection mechanisms to overcome oxidative stress and are known to be activated in vascular diseases and acute stroke. We investigated the differences of antioxidant capacity in acute stroke and stroke risk patients to elucidate whether the differences are a result of chronic low availability in arteriosclerosis and stroke risk or due to changes during acute infarction. Methods: Antioxidant enzymes were examined in 11 patients within the first hours and days after acute ischemic stroke and compared to risk- and age-matched patients with a history of stroke in the past 12 months ( n = 17). Antioxidant profile was determined by measurement of glutathione (GSH), malondialdehyde (MDA), SOD, GSHPx and minerals known to be involved in antioxidant enzyme activation like selenium, iron, copper and zinc. Results: In comparison to stroke risk patients, patients with acute ischemic stroke had significant changes of the GSH system during the first hours and days after the event: GSH was significantly elevated in the first hours (p < 0.01) and GSHPx was elevated 1 day after the acute stroke (p < 0.05). Selenium, a cofactor of GSHPx, was decreased (p < 0.01). GSHPx levels were negatively correlated with National Institutes of Health Stroke Scale (NIHSS) scores on admission (r = - 0.84, p < 0.001) and NIHSS scores after 7 days ( r = - 0.63, p < 0.05). MDA levels showed a trend for elevation in the first 6 h after the acute stroke ( p = 0.07). No significant differences of SOD, iron, copper nor zinc levels could be identified. Conclusions: Differences of antioxidant capacity were found for the GSH system with elevation of GSH and GSHPx after acute stroke, but not for other markers. The findings support the hypothesis that changes of antioxidant capacity are part of acute adaptive mechanisms during acute stroke. Copyright (C) 2004 S. Karger AG, Basel
Influence of fly ash blending on hydration and physical behavior of Belite-Alite-Ye'elimite cements
A cement powder, composed of belite, alite and ye’elimite, was blended with 0, 15 and 30 wt% of fly ash and the resulting lended cements were further characterized. During hydration, the presence of fly ash caused the partial inhibition of both AFt degradation and belite reactivity, even after 180 days. The compressive strength of the corresponding mortars increased by increasing the fly ash content (68, 73 and 82 MPa for mortars with 0, 15 and 30 wt% of fly ash, respectively, at 180 curing days), mainly due to the diminishing porosity and pore size values. Although pozzolanic reaction has not been directly proved there are indirect evidences.This work is part of the Ph.D. of D. Londono-Zuluaga funded by Beca Colciencias 646—Doctorado en el exterior and Enlaza Mundos 2013 program grant. Cement and Building materials group (CEMATCO) from National University of Colombia is acknowledged for providing the calorimetric measurements. Funding from Spanish MINECO BIA2017-82391-R and I3 (IEDI-2016-0079) grants, co-funded by FEDER, are acknowledged
Accelerated swell testing of artificial sulfate bearing lime stabilised cohesive soils
This paper reports on the physico-chemical response of two lime stabilised sulfate bearing artificial soils subject to the European Accelerated Volumetric Swell Test (EN13286-49). At various intervals during the test, a specimen was removed and subject to compositional and microstructural analysis. Ettringite was formed by both soils types, but with significant differences in crystal morphology. Ettringite crystals formed from kaolin based soils were very small, colloidal in size and tended to form on the surface of other particles. Conversely, those formed from montmorillonite were relatively large and typically formed away from the surface in the pore solution. It was concluded that the mechanism by which ettringite forms is determined by the hydroxide ion concentration in the pore solution and the fundamental structure of the bulk clay. In the kaolin soil, ettringite forms by a topochemical mechanism and expands by crystal swelling. In the montmorillonite soil, it forms by a through-solution mechanism and crystal growth
Identification of New Genes Involved in Human Adipogenesis and Fat Storage
Since the worldwide increase in obesity represents a growing challenge for health care systems, new approaches are needed to effectively treat obesity and its associated diseases. One prerequisite for advances in this field is the identification of genes involved in adipogenesis and/or lipid storage. To provide a systematic analysis of genes that regulate adipose tissue biology and to establish a target-oriented compound screening, we performed a high throughput siRNA screen with primary (pre)adipocytes, using a druggable siRNA library targeting 7,784 human genes. The primary screen showed that 459 genes affected adipogenesis and/or lipid accumulation after knock-down. Out of these hits, 333 could be validated in a secondary screen using independent siRNAs and 110 genes were further regulated on the gene expression level during adipogenesis. Assuming that these genes are involved in neutral lipid storage and/or adipocyte differentiation, we performed InCell-Western analysis for the most striking hits to distinguish between the two phenotypes. Beside well known regulators of adipogenesis and neutral lipid storage (i.e. PPARγ, RXR, Perilipin A) the screening revealed a large number of genes which have not been previously described in the context of fatty tissue biology such as axonemal dyneins. Five out of ten axonemal dyneins were identified in our screen and quantitative RT-PCR-analysis revealed that these genes are expressed in preadipocytes and/or maturing adipocytes. Finally, to show that the genes identified in our screen are per se druggable we performed a proof of principle experiment using an antagonist for HTR2B. The results showed a very similar phenotype compared to knock-down experiments proofing the “druggability”. Thus, we identified new adipogenesis-associated genes and those involved in neutral lipid storage. Moreover, by using a druggable siRNA library the screen data provides a very attractive starting point to identify anti-obesity compounds targeting the adipose tissue
Reactivity tests for supplementary cementitious materials: RILEM TC 267-TRM phase 1
A primary aim of RILEM TC 267-TRM: “Tests for Reactivity of Supplementary Cementitious Materials (SCMs)” is to compare and evaluate the performance of conventional and novel SCM reactivity test methods across a wide range of SCMs. To this purpose, a round robin campaign was organized to investigate 10 different tests for reactivity and 11 SCMs covering the main classes of materials in use, such as granulated blast furnace slag, fly ash, natural pozzolan and calcined clays. The methods were evaluated based on the correlation to the 28 days relative compressive strength of standard mortar bars containing 30% of SCM as cement replacement and the interlaboratory reproducibility of the test results. It was found that only a few test methods showed acceptable correlation to the 28 days relative strength over the whole range of SCMs. The methods that showed the best reproducibility and gave good correlations used the R3 model system of the SCM and Ca(OH)2, supplemented with alkali sulfate/carbonate. The use of this simplified model system isolates the reaction of the SCM and the reactivity can be easily quantified from the heat release or bound water content. Later age (90 days) strength results also correlated well with the results of the IS 1727 (Indian standard) reactivity test, an accelerated strength test using an SCM/Ca(OH)2-based model system. The current standardized tests did not show acceptable correlations across all SCMs, although they performed better when latently hydraulic materials (blast furnace slag) were excluded. However, the Frattini test, Chapelle and modified Chapelle test showed poor interlaboratory reproducibility, demonstrating experimental difficulties. The TC 267-TRM will pursue the development of test protocols based on the R3 model systems. Acceleration and improvement of the reproducibility of the IS 1727 test will be attempted as well
A Novel, Non-Apoptotic Role for Scythe/BAT3: A Functional Switch between the Pro- and Anti-Proliferative Roles of p21 during the Cell Cycle
BACKGROUND: Scythe/BAT3 is a member of the BAG protein family whose role in apoptosis has been extensively studied. However, since the developmental defects observed in Bat3-null mouse embryos cannot be explained solely by defects in apoptosis, we investigated whether BAT3 is also involved in cell-cycle progression. METHODS/PRINCIPAL FINDINGS: Using a stable-inducible Bat3-knockdown cellular system, we demonstrated that reduced BAT3 protein level causes a delay in both G1/S transition and G2/M progression. Concurrent with these changes in cell-cycle progression, we observed a reduction in the turnover and phosphorylation of the CDK inhibitor p21, which is best known as an inhibitor of DNA replication; however, phosphorylated p21 has also been shown to promote G2/M progression. Our findings indicate that in Bat3-knockdown cells, p21 continues to be synthesized during cell-cycle phases that do not normally require p21, resulting in p21 protein accumulation and a subsequent delay in cell-cycle progression. Finally, we showed that BAT3 co-localizes with p21 during the cell cycle and is required for the translocation of p21 from the cytoplasm to the nucleus during the G1/S transition and G2/M progression. CONCLUSION: Our study reveals a novel, non-apoptotic role for BAT3 in cell-cycle regulation. By maintaining a low p21 protein level during the G1/S transition, BAT3 counteracts the inhibitory effect of p21 on DNA replication and thus enables the cells to progress from G1 to S phase. Conversely, during G2/M progression, BAT3 facilitates p21 phosphorylation by cyclin A/Cdk2, an event required for G2/M progression. BAT3 modulates these pro- and anti-proliferative roles of p21 at least in part by regulating cyclin A abundance, as well as p21 translocation between the cytoplasm and the nucleus to ensure that it functions in the appropriate intracellular compartment during each phase of the cell cycle.Dissertatio
Report of RILEM TC 267-TRM phase 3: validation of the R3 reactivity test across a wide range of materials
RILEM TC 267 TRM– “Tests for Reactivity of Supplementary Cementitious Materials” recommends the Rapid Reliable Relevant (R3) test as a method for determining the chemical reactivity of supplementary cementitious materials (SCMs) in Portland cement blends. In this paper, the R3 test was applied to 52 materials from a wide range of conventional and alternative SCMs with the aim to validate such test. An excellent correlation was found between the cumulative heat release and the bound water determined following the R3 test method. Comparison of the R3 test results to mortar compressive strength development showed that all conventional SCMs (e.g. blast furnace slag and fly ashes) followed the same trend, with the notable exception of very reactive calcined kaolinitic clays. It is discussed, through an in-depth statistical regression analysis of the R3 reactivity test results and the 28 days relative compressive strengths, how reactivity threshold values for classification of the chemical reactivity of SCMs could be proposed based on the R3 test results
Report of RILEM TC 267-TRM phase 2: optimization and testing of the robustness of the R3 reactivity tests for supplementary cementitious materials
The results of phase 1 of an interlaboratory test, coordinated by the RILEM TC 267-TRM “Tests for Reactivity of Supplementary Cementitious Materials” showed that the R3 (rapid, relevant, reliable) test method, by measurement of heat release or bound water, provided the most reliable and relevant determination of the chemical reactivity of supplementary cementitious materials (SCMs), compared to other test methods. The phase 2 work, described in this paper aimed to improve the robustness of the test procedure and to develop precision statements for the consolidated test procedure. The effect of the pre-mixing and mixing conditions, and the impact of the mix design on the test method robustness were assessed and fixed for optimal conditions to carry out the R3 heat release test. The effect of the drying step was evaluated to define the R3 bound water test procedure in more detail. Finally, the robustness of the consolidated final test methods was determined by an interlaboratory study to define the precision statements
Examination of alkali-activated material nanostructure during thermal treatment
The key nanostructural changes occurring in a series of alkali-activated materials (AAM) based on blends of slag and fly ash precursors during exposure to temperatures up to 1000 °C are investigated. The main reaction product in each AAM is a crosslinked sodium- and aluminium-substituted calcium silicate hydrate (C-(N)-A-S-H)-type gel. Increased alkali content promotes the formation of an additional sodium aluminosilicate hydrate (N-A-S-(H)) gel reaction product due to the structural limitations on Al substitution within the C-(N)-A-S-H gel. Heating each AAM to 1000 °C results in the crystallisation of the disordered gels and formation of sodalite, nepheline and wollastonite. Increased formation of N-A-S-(H) reduces binder structural water content after thermal treatment and correlates closely with previous observations of improved strength retention and reduced microcracking in these AAM after heating to 1000 °C. This provides new insight into thermally induced changes to gel atomic structure and thermal durability of C-(N)-A-S-H/N-A-S-H gel blends which are fundamental for the development of new fire-resistant construction materials
- …