X-ray determination of compressive residual Stresses in spring steel generated by high-speed water Quenching

Automotive components manufacturers use the 5160 steel in leaf and coil springs. The industrial heat treatment process consists in austenitizing followed by the oil quenching and tempering process. Typically, compressive residual stresses are induced by shot peening on the surface of automotive springs to bestow compressive residual stresses that improve the fatigue resistance and increase the service life of the parts after heat treatment. In this work, a high-speed quenching was used to achieve compressive residual stresses on the surface of AISI/SAE 5160 steel samples by producing high thermal gradients and interrupting the cooling in order to generate a case-core microstructure. A special laboratory equipment was designed and built, which uses water as the quenching media in a high-speed water chamber. The severity of the cooling was characterized with embedded thermocouples to obtain the cooling curves at different depths from the surface. Samples were cooled for various times to produce different hardened case depths. The microstructure of specimens was observed with a scanning electron microscope (SEM). X-ray diffraction (XRD) was used to estimate the magnitude of residual stresses on the surface of the specimens. Compressive residual stresses at the surface and sub-surface of about -700 MPa were obtained.Peer ReviewedPostprint (published version

Cabbage and fermented vegetables : From death rate heterogeneity in countries to candidates for mitigation strategies of severe COVID-19

Large differences in COVID-19 death rates exist between countries and between regions of the same country. Some very low death rate countries such as Eastern Asia, Central Europe, or the Balkans have a common feature of eating large quantities of fermented foods. Although biases exist when examining ecological studies, fermented vegetables or cabbage have been associated with low death rates in European countries. SARS-CoV-2 binds to its receptor, the angiotensin-converting enzyme 2 (ACE2). As a result of SARS-CoV-2 binding, ACE2 downregulation enhances the angiotensin II receptor type 1 (AT(1)R) axis associated with oxidative stress. This leads to insulin resistance as well as lung and endothelial damage, two severe outcomes of COVID-19. The nuclear factor (erythroid-derived 2)-like 2 (Nrf2) is the most potent antioxidant in humans and can block in particular the AT(1)R axis. Cabbage contains precursors of sulforaphane, the most active natural activator of Nrf2. Fermented vegetables contain many lactobacilli, which are also potent Nrf2 activators. Three examples are: kimchi in Korea, westernized foods, and the slum paradox. It is proposed that fermented cabbage is a proof-of-concept of dietary manipulations that may enhance Nrf2-associated antioxidant effects, helpful in mitigating COVID-19 severity.Peer reviewe

Nrf2-interacting nutrients and COVID-19 : time for research to develop adaptation strategies

There are large between- and within-country variations in COVID-19 death rates. Some very low death rate settings such as Eastern Asia, Central Europe, the Balkans and Africa have a common feature of eating large quantities of fermented foods whose intake is associated with the activation of the Nrf2 (Nuclear factor (erythroid-derived 2)-like 2) anti-oxidant transcription factor. There are many Nrf2-interacting nutrients (berberine, curcumin, epigallocatechin gallate, genistein, quercetin, resveratrol, sulforaphane) that all act similarly to reduce insulin resistance, endothelial damage, lung injury and cytokine storm. They also act on the same mechanisms (mTOR: Mammalian target of rapamycin, PPAR gamma:Peroxisome proliferator-activated receptor, NF kappa B: Nuclear factor kappa B, ERK: Extracellular signal-regulated kinases and eIF2 alpha:Elongation initiation factor 2 alpha). They may as a result be important in mitigating the severity of COVID-19, acting through the endoplasmic reticulum stress or ACE-Angiotensin-II-AT(1)R axis (AT(1)R) pathway. Many Nrf2-interacting nutrients are also interacting with TRPA1 and/or TRPV1. Interestingly, geographical areas with very low COVID-19 mortality are those with the lowest prevalence of obesity (Sub-Saharan Africa and Asia). It is tempting to propose that Nrf2-interacting foods and nutrients can re-balance insulin resistance and have a significant effect on COVID-19 severity. It is therefore possible that the intake of these foods may restore an optimal natural balance for the Nrf2 pathway and may be of interest in the mitigation of COVID-19 severity

X-ray Determination of Compressive Residual Stresses in Spring Steel Generated by High-Speed Water Quenching

Automotive components manufacturers use the 5160 steel in leaf and coil springs. The industrial heat treatment process consists in austenitizing followed by the oil quenching and tempering process. Typically, compressive residual stresses are induced by shot peening on the surface of automotive springs to bestow compressive residual stresses that improve the fatigue resistance and increase the service life of the parts after heat treatment. In this work, a high-speed quenching was used to achieve compressive residual stresses on the surface of AISI/SAE 5160 steel samples by producing high thermal gradients and interrupting the cooling in order to generate a case-core microstructure. A special laboratory equipment was designed and built, which uses water as the quenching media in a high-speed water chamber. The severity of the cooling was characterized with embedded thermocouples to obtain the cooling curves at different depths from the surface. Samples were cooled for various times to produce different hardened case depths. The microstructure of specimens was observed with a scanning electron microscope (SEM). X-ray diffraction (XRD) was used to estimate the magnitude of residual stresses on the surface of the specimens. Compressive residual stresses at the surface and sub-surface of about --700 MPa were obtained

Tribological Performance of CoCrMo Alloys with Boron Additions in As-Cast and Heat-Treated Conditions

The present study evaluates the effect of boron additions on the tribological performance of CoCrMo alloys. The alloys were prepared with boron ranging from 0.06 to 1 wt%. The materials were characterized using metallographic techniques, scanning electronic microscopy, and roughness and hardness tests. Tribological evaluation was made by means of ball-on-disc tests for sliding distances of 4, 8 and 12 km. The samples were in the as-cast condition and after a heat treatment at 1200 °C for 1 h, finished by water quenching. The results showed that wear resistance was influenced by the microstructure and the number of secondary phases. The volume loss decreased as the boron content increased. Due to hard phases, abrasion wear was observed. Delamination fatigue was also detected after long sliding distances. Both wear mechanisms diminished in higher boron content alloys

Influence of Boron Additions and Heat Treatments on the Fatigue Resistance of CoCrMo Alloys

Cobalt-based alloys are widely used in the manufacture of joint prostheses. In this study, the effect of boron additions and heat treatment on the ASTM F75 was evaluated by rotating bending fatigue. The boron ranged from 0.06–1 wt %. The alloys were tested in as-cast and heat-treated conditions. In the as-cast condition, the infinite life was observed at 380 MPa, improving to 433–615 MPa according to the amount of boron added. In the heat treatment condition, the fatigue resistance was improved only in the base alloy. The addition of 0.06 wt % boron and heat treatment led to the same resistance as in the as-cast condition. Adding large amounts of boron combined with heat treatment diminished the fatigue limit. The fracture analysis revealed primarily brittle behaviour with some ductile features even on the same sample; only the heat-treated alloy with 0.06 wt % boron was clearly ductile. This alloy also exhibited notably better toughness to crack propagation

X-ray determination of compressive residual Stresses in spring steel generated by high-speed water Quenching

Automotive components manufacturers use the 5160 steel in leaf and coil springs. The industrial heat treatment process consists in austenitizing followed by the oil quenching and tempering process. Typically, compressive residual stresses are induced by shot peening on the surface of automotive springs to bestow compressive residual stresses that improve the fatigue resistance and increase the service life of the parts after heat treatment. In this work, a high-speed quenching was used to achieve compressive residual stresses on the surface of AISI/SAE 5160 steel samples by producing high thermal gradients and interrupting the cooling in order to generate a case-core microstructure. A special laboratory equipment was designed and built, which uses water as the quenching media in a high-speed water chamber. The severity of the cooling was characterized with embedded thermocouples to obtain the cooling curves at different depths from the surface. Samples were cooled for various times to produce different hardened case depths. The microstructure of specimens was observed with a scanning electron microscope (SEM). X-ray diffraction (XRD) was used to estimate the magnitude of residual stresses on the surface of the specimens. Compressive residual stresses at the surface and sub-surface of about -700 MPa were obtained.Peer Reviewe

Immunohistochemical Classification of Ampullary Carcinomas: Critical Reappraisal Fails to Confirm Prognostic Relevance for Recently Proposed Panels, and Highlights MUC5AC as a Strong Prognosticator

Recently, immunohistochemistry-based classifications of ampullary carcinomas have been proposed (Ang and colleagues [PMID: 24832159]; Chang and colleagues [PMID: 23439753]). In this study, the prognostic value of Ang/Chang panel markers (CK20, MUC1, MUC2, CDX2) as well as other markers (CK7, MUC5AC, and MUC6) were tested on full-faced sections of 136 ampullary carcinoma resections with substantial (>5 mm) invasion. Immunohistochemistry was correlated with both histologic classification (intestinal [INT], pancreatobiliary [PB], or nontubular based on 3/5 observer agreement) and clinical outcome. No prognostic correlation was found with MUC1, CDX2, MUC2 or CK20 despite testing with different quantitative cutoffs. CK7 and CK20 were nonspecific. Ang classification had reasonable correlation with histologic subclassification of tubular cases as INT versus PB with high specificity but low sensitivity and ambiguous category was large (29%) and included also some classical cases. Prognostically, Ang classification approached but did not reach statistical significance, even when their large ambiguous group was eliminated and only tubular cases were analyzed (Ang-INT vs. Ang-PB; P=0.08). The Chang panel, in which the definition of the INT subcategory is not clearly defined, only marginally reached prognostic significance when tested as MUC1+/CDX2- versus MUC1-/CDX2+ and only by Wilcoxon test (P=0.0485) but 31% of the cases were unclassifiable. The only individual marker that was found to have direct and strong correlation with the clinical outcome was MUC5AC (not used in the Ang or Chang panels), with statistically significant survival differences found with various cutoffs tested (for 20% cutoff, 5-y survival, 68% vs. 31%; P=0.0002). In addition, MUC5AC significantly stratified the histologically PB and INT cases (P=0.01 and 0.03, respectively), as well as Ang's ambiguous and Chang's unclassified cases (P=0.006 and 0.007, respectively). In conclusion, the widely used putative lineage markers, MUC1/MUC2/CK7/CK20/CDX2, do not seem to have direct/significant prognostic correlation either individually or in combination of Ang and Chang panels. Ang panel is helpful as an adjunct in determining the cell lineage with a few caveats. MUC5AC proves to be a significant independent prognosticator and should be incorporated into evaluation of ampullary carcinomas