223 research outputs found
Sensing Characteristics of Flame-Spray-Made Pt/ZnO Thick Films as H2 Gas Sensor
Hydrogen sensing of thick films of nanoparticles of pristine, 0.2, 1.0 and 2.0 atomic percentage of Pt concentration doped ZnO were investigated. ZnO nanoparticles doped with 0.2–2.0 at.% Pt were successfully produced in a single step by flame spray pyrolysis (FSP) technique using zinc naphthenate and platinum(II) acetylacetonate as precursors dissolved in xylene. The particle properties were analyzed by XRD, BET, SEM and TEM. Under the 5/5 (precursor/oxygen) flame condition, ZnO nanoparticles and nanorods were observed. The crystallite sizes of ZnO spheroidal and hexagonal particles were found to be ranging from 5 to 20 nm while ZnO nanorods were seen to be 5–20 nm wide and 20–40 nm long. ZnO nanoparticles paste composed of ethyl cellulose and terpineol as binder and solvent respectively was coated on Al2O3 substrate interdigitated with gold electrodes to form thin films by spin coating technique. The thin film morphology was analyzed by SEM technique. The gas sensing properties toward hydrogen (H2) was found that the 0.2 at.% Pt/ZnO sensing film showed an optimum H2 sensitivity of ∼164 at hydrogen concentration in air of 1 volume% at 300 °C and a low hydrogen detection limit of 50 ppm at 300 °C operating temperature
Flame-Spray-Made Undoped Zinc Oxide Films for Gas Sensing Applications
Using zinc naphthenate dissolved in xylene as a precursor undoped ZnO nanopowders were synthesized by the flame spray pyrolysis technique. The average diameter and length of ZnO spherical and hexagonal particles were in the range of 5 to 20 nm, while ZnO nanorods were found to be 5–20 nm wide and 20–40 nm long, under 5/5 (precursor/oxygen) flame conditions. The gas sensitivity of the undoped ZnO nanopowders towards 50 ppm of NO2, C2H5OH and SO2 were found to be 33, 7 and 3, respectively. The sensors showed a great selectivity towards NO2 at high working temperature (at 300 °C), while small resistance variations were observed for C2H5OH and SO2, respectively
Microwave-Enhanced Asymmetric Transfer Hydrogenation of N-(tert-Butylsulfinyl)imines
Microwave irradiation has considerably enhanced the efficiency of the asymmetric transfer hydrogenation of N-(tert-butylsulfinyl)imines in isopropyl alcohol catalyzed by a ruthenium complex bearing the achiral ligand 2-amino-2-methylpropan-1-ol. In addition to shortening reaction times for the transfer hydrogenation processes to only 30 min, the amounts of ruthenium catalyst and isopropyl alcohol can be considerably reduced in comparison with our previous procedure assisted by conventional heating, which diminishes the environmental impact of this new protocol. This methodology can be applied to aromatic, heteroaromatic and aliphatic N-(tert-butylsulfinyl)ketimines, leading, after desulfinylation, to the expected primary amines in excellent yields and with enantiomeric excesses of up to 96 %.This work was generously supported by the Spanish Ministerio de Ciencia e Innovación (MICINN) (grant numbers CONSOLIDER INGENIO 2010, CSD2007-00006, CTQ2007-65218 and CTQ2011-24151) and the Generalitat Valenciana (PROMETEO/2009/039 and FEDER). O. P. thanks the Spanish Ministerio de Educación for a predoctoral fellowship (grant number AP-2008-00989)
Erratum to: Synthesis and Magnetic Properties of Nearly Monodisperse CoFe2O4 Nanoparticles Through a Simple Hydrothermal Condition
<p>Abstract</p> <p>Nearly monodisperse cobalt ferrite (CoFe<sub>2</sub>O<sub>4</sub>) nanoparticles without any size-selection process have been prepared through an alluring method in an oleylamine/ethanol/water system. Well-defined nanospheres with an average size of 5.5 nm have been synthesized using metal chloride as the law materials and oleic amine as the capping agent, through a general liquid–solid-solution (LSS) process. Magnetic measurement indicates that the particles exhibit a very high coercivity at 10 K and perform superparamagnetism at room temperature which is further illuminated by ZFC/FC curves. These superparamagnetic cobalt ferrite nanomaterials are considered to have potential application in the fields of biomedicine. The synthesis method is possible to be a general approach for the preparation of other pure binary and ternary compounds.</p
ChemInform Abstract: Magnetically Recoverable Supported Ruthenium Catalyst for Hydrogenation of Alkynes and Transfer Hydrogenation of Carbonyl Compounds.
High Value Products from Waste: Grape Pomace ExtractâA Three-in-One Package for the Synthesis of Metal Nanoparticles
- …