Tailoring flame-retardancy and strength of papers via layer-by-layer treatment of cellulose fibers
The layer-by-layer (LbL) technology was used to adsorb polyelectrolyte multilayers consisting of cationic polyethylenimine (PEI) and anionic sodium hexametaphosphate (SHMP) onto cellulose fibers in order to enhance the flame-retardancy and tensile strength of paper sheets made from these fibers. The fundamental effect of PEI molecular mass on the build-up of the multilayer film was investigated using model cellulose surfaces and a quartz crystal microbalance technique. The adsorption of a low (LMw) and a high molecular weight (HMw) PEI onto cellulose fibers and carboxymethylated (CM) cellulose fibers was investigated using polyelectrolyte titration. The fibers were consecutively treated with PEI and SHMP to deposit 3.5 bilayers (BL) on the fiber surfaces, and the treated fibers were then used to prepare sheets. In addition, a wet-strength paper sheet was prepared and treated with the same LbL coatings. Thermal gravimetric analysis of LbL-treated fibers showed that the onset temperature for cellulose degradation was lowered and that the amount of residue at 800 °C increased. A horizontal flame test and a vertical flame test were used to evaluate the combustion behavior of the paper sheets. Papers prepared from both cellulose fibers and CM-cellulose fibers treated with HMw-PEI/SHMP LbL-combination self-extinguished in a horizontal configuration despite the rather low amounts of adsorbed polymer which form very thin films (wet thickness of ca. 17 nm). The tensile properties of handsheets showed that 3.5 BL of HMw-PEI and SHMP increased the stress at break by 100% compared to sheets prepared from untreated cellulose fibers
Sequential Monte Carlo Methods for System Identification
One of the key challenges in identifying nonlinear and possibly non-Gaussian
state space models (SSMs) is the intractability of estimating the system state.
Sequential Monte Carlo (SMC) methods, such as the particle filter (introduced
more than two decades ago), provide numerical solutions to the nonlinear state
estimation problems arising in SSMs. When combined with additional
identification techniques, these algorithms provide solid solutions to the
nonlinear system identification problem. We describe two general strategies for
creating such combinations and discuss why SMC is a natural tool for
implementing these strategies.Comment: In proceedings of the 17th IFAC Symposium on System Identification
(SYSID). Added cover pag
Does Lipoprotein(a) Inhibit Elastolysis in Abdominal Aortic Aneurysms?
AbstractPurpose: to test the hypothesis that there is a negative association between serum levels of lipoprotein(a) (Lp(a)) and elastin-derived peptides (EDP) as well as matrix metalloproteinase (MMP)-9 activation in the aneurysm wall in patients with asymptomatic abdominal aortic aneurysms (AAA).Material and Methods: from 30 patients operated for asymptomatic AAAs, preoperative serum samples and AAA biopsies were collected. Lp(a) (mg/L) and EDP (ng/ml) in serum were measured by enzyme linked immunosorbent assays. MMP-9 activity (arbitrary units) in the AAA wall was measured by gelatin zymography and the ratio: active MMP-9/total MMP-9 were calculated.Results: there was a significant negative correlation (Spearman's rho) between serum levels of Lp(a) and EDP (r=−0.707, p<0.001), as well as the share of activated MMP-9 (r=−0.461, p=0.01) in the AAA wall.Conclusion: this preliminary study indicate that Lp(a) inhibit elastolysis in asymptomatic AAA
All-natural and highly flame-resistant freeze-cast foams based on phosphorylated cellulose nanofibrils
Pure cellulosic foams suffer from low thermal stability and high flammability, limiting their fields of application
The use of model cellulose gel beads to clarify flame-retardant characteristics of layer-by-layer nanocoatings.
Layer-by-Layer (LbL) assembled nanocoatings are exploited to impart flame-retardant properties to cellulosic substrates. A model cellulose material can make it possible to investigate an optimal bilayer (BL) range for the deposition of coating while elucidating the main flame-retardant action thus allowing for an efficient design of optimized LbL formulations. Model cellulose gel beads were prepared by dissolving cellulose-rich fibers followed by precipitation. The beads were LbL-treated with chitosan (CH) and sodium hexametaphosphate (SHMP). The char forming properties were studied using thermal gravimetric analysis. The coating increased the char yield in nitrogen to up to 29 % and showed a distinct pattern of micro intumescent behavior upon heating. An optimal range of 10-20 BL is observed. The well-defined model cellulose gel beads hence introduce a new scientific route both to clarify the fundamental effects of different film components and to optimize the composition of the films
Вплив попиту на процес ціноутворення
The creep behavior of nanocellulose films and aerogels are studied in a dynamic moisture environment, which is crucial to their performance in packaging applications. For these materials, the creep rate under cyclic humidity conditions exceeds any constant humidity creep rate within the cycling range, a phenomenon known as mechanosorptive creep. By varying the sample thickness and relative humidity ramp rate, it is shown that mechanosorptive creep is not significantly affected by the through-thickness moisture gradient. It is also shown that cellulose nanofibril aerogels with high porosity display the same accelerated creep as films. Microstructures larger than the fibril diameter thus appear to be of secondary importance to mechanosorptive creep in nanocellulose materials, suggesting that the governing mechanism is found between molecular scales and the length-scales of the fibril diameter.funding agencies|BiMaC Innovation|
Soft and rigid core latex nanoparticles prepared by RAFT-mediated surfactant-free emulsion polymerization for cellulose modification – a comparative study
Latex nanoparticles comprising cationically charged coronas and hydrophobic cores with different glass transition temperatures (Tg) have been prepared by surfactant-free, RAFT-mediated emulsion polymerization, where the particles form through a polymerization-induced self-assembly (PISA) type mechanism. Poly(2-dimethylaminoethyl methacrylate-co-methacrylic acid) (P(DMAEMA-co-MAA)) was utilized as a hydrophilic macroRAFT agent for the polymerization of methyl methacrylate (MMA) or n-butyl methacrylate (nBMA), respectively, resulting in two different latexes, with either a core of high (PMMA) or low (PnBMA) Tg polymer. By varying the molar mass of the hydrophobic block, latexes of different sizes were obtained (DHca. 40–120 nm). The adsorption of the latexes to cellulose model surfaces and cellulose nanofibrils (CNF) was studied using quartz crystal microbalance with dissipation monitoring (QCM-D). The surfaces with adsorbed PnBMA latexes yielded hydrophobic surfaces both before and after annealing, whereas surfaces with adsorbed PMMA latex became hydrophobic only after annealing, clearly showing the influence of the Tg of the core. The latexes were also used to modify macroscopic cellulose in the form of filter papers. Similar to the CNF surfaces, no annealing was required to achieve hydrophobic surfaces with PnBMA latexes. Finally, nanocomposites of CNF and the polymer nanoparticles were prepared through a one-pot mixing procedure. It was found that the largest synthesized PMMA latex (120 nm) facilitated a more strainable CNF network at 50% relative humidity, with a nearly 200% increase in strain at break compared to the neat CNF reference film as well as to the composite films with PnBMA latexes or to the smaller sized PMMA latexes. This difference was attributed to the spherical shape and rigidity of the large PMMA latex nanoparticles during composite formation. This highly interesting result should indeed be considered in the future design of novel biocomposites.</p
Hard and transparent films formed by nanocellulose-TiO2 nanoparticle hybrids
T he formation of hybrids of nanofibrillated cellulose and titania nanoparticles in aqueous media has been studied. Their transparency and mechanical behavior have been assessed by spectrophotometry and nanoindentation. The results show that limiting the titania nanoparticle concentration below 16 vol% yields homogeneous hybrids with a very high Young's modulus and hardness, of up to 44 GPa and 3.4 GPa, respectively, and an optical transmittance above 80%. Electron microscopy shows that higher nanoparticle contents result in agglomeration and an inhomogeneous hybrid nanostructure with a concomitant reduction of hardness and optical transmittance. Infrared spectroscopy suggests that the nanostructure of the hybrids is controlled by electrostatic adsorption of the titania nanoparticles on the negatively charged nanocellulose surfaces
- …