Tailoring functional properties of Zr-V thin films by competitive self-separation of crystalline and amorphous phases during sputtering
Deposition rate controls nucleation and growth during amorphous/nanocrystalline competition in sputtered Zr-Cr thin films
Dual-phase Zr-based thin films synthesized by magnetron co-sputtering and
showing competitive growth between amorphous and crystalline phases have been
reported recently. In such films, the amorphous phase grows as columns, while
the crystalline phase grows as separated cone-shaped crystalline regions made
of smaller crystallites. In this paper, we investigate this phenomenon and
propose a model for the development of the crystalline regions during thin film
growth. We evidence using X-ray diffraction (XRD), scanning electron microscopy
(SEM) and transmission electron microscopy (TEM), that this competitive
selfseparation also exists in co-sputtered Zr-Cr thin films with Cr contents of
~84-86 at.%, corresponding to the transition between the amorphous and
crystalline compositions, and in the Zr-V system. Then, to assess the
sturdiness of this phenomenon, its existence and geometrical characteristics
are evaluated when varying the film composition and the deposition rate. The
variation of geometrical features, such as the crystalline cone angle, the size
and density of crystallites, is discussed. Is it shown that a variation in the
deposition rate changes the nucleation and growth kinetics of the crystallites.
The surface coverage by the crystalline phase at a given thickness is also
calculated for each deposition rate. Moreover, comparison is made between
Zr-Cr, Zr-V, Zr-Mo and Zr-W dual-phase thin films to compare their nucleation
and growth kinetics
Multi-component Transparent Conducting Oxides: Progress in Materials Modelling
Transparent conducting oxides (TCOs) play an essential role in modern
optoelectronic devices through their combination of electrical conductivity and
optical transparency. We review recent progress in our understanding of
multi-component TCOs formed from solid-solutions of ZnO, In2O3, Ga2O3 and
Al2O3, with a particular emphasis on the contributions of materials modelling,
primarily based on Density Functional Theory. In particular, we highlight three
major results from our work: (i) the fundamental principles governing the
crystal structures of multi-component oxide structures including (In2O3)(ZnO)n,
named IZO, and (In2O3)m(Ga2O3)l(ZnO)n, named IGZO; (ii) the relationship
between elemental composition and optical and electrical behaviour, including
valence band alignments; (iii) the high-performance of amorphous oxide
semiconductors. From these advances, the challenge of the rational design of
novel electroceramic materials is discussed.Comment: Part of a themed issue of Journal of Physics: Condensed Matter on
"Semiconducting Oxides". In Press (2011
The effect of changing the magnetic field strength on HiPIMS deposition rates
The marked difference in behaviour between HiPIMS and conventional dc or pulsed-dc magnetron sputtering discharges with changing magnetic field strengths is demonstrated through measurements of deposition rate. To provide a comparison between techniques the same circular magnetron was operated in the three excitation modes at a fixed average power of 680 W and a pressure of 0.54 Pa in the non-reactive sputtering of titanium. The total magnetic field strength B at the cathode surface in the middle of the racetrack was varied from 195 to 380 G. DC and pulsed-dc discharges show the expected behaviour that deposition rates fall with decreasing B (here by ~25–40%), however the opposite trend is observed in HiPIMS with deposition rates rising by a factor of 2 over the same decrease in B.
These observations are understood from the stand point of the different composition and transport processes of the depositing metal flux between the techniques. In HiPIMS, this flux is largely ionic and slow post-ionized sputtered particles are subject to strong back attraction to the target by a retarding plasma potential structure ahead of them. The height of this potential barrier is known to increase with increasing B.
From a simple phenomenological model of the sputtered particles fluxes, and using the measured deposition rates from the different techniques as inputs, the combined probabilities of ionization, α, and back attraction, β, of the metal species in HiPIMS has been calculated. There is a clear fall in αβ (from ~0.9 to ~0.7) with decreasing B-field strengths, we argue primarily due to a weakening of electrostatic ion back attraction, so leading to higher deposition rates. The results indicate that careful design of magnetron field strengths should be considered to optimise HiPIMS deposition rates
Deep oxidation of methane on particles derived from YSZ-supported Pd-Pt-(O) coatings synthesized by pulsed filtered cathodic arc
Methane conversion tests were performed on Pd, PdOy, Pd0.6Pt0.4Oy and Pd0.4Pt0.6Oy thin films deposited on yttria stabilized zirconia (YSZ) substrates. Pt containing films exhibited poor activity and high reducibility. As-deposited Pd and PdOy films showed good activity and transformed, during the cycling process, to particles dispersed on the YSZ substrates. The higher reaction rate of initially PdOy films was explained by a better dispersion of the catalyst. A drop of the reaction rate was observed when the temperature exceeded 735oC and 725oC for initially Pd and PdOy, respectively, which can be associated with the high-temperature reduction of PdO into Pd
Nanostructuration in Ag-Cu-O Sputtered Films by Controlling Their Oxygen and/or Their Silver Concentrations
Extended X-ray absorption fine structure (EXAFS) investigations of Ti bonding environment in sputter-deposited nanocomposite TiBC/a-C thin films
In this study, we have successfully used the extended X-ray absorption fine structure (EXAFS) technique at the Ti-K edge to extract the local structure in a set of nanocomposite TiBC/a-C coatings deposited by a combined d.c.-pulsed and r.f.-magnetron sputtering deposition process. The sequence of Fourier transform spectra in the deposited films shows that there is an increase in the number of Ti-C bonds in the films of higher carbon content in parallel with the increment of the total carbon content. In addition, Ti-K EXAFS spectra indicate that in all the deposited TiBC/a-C films, first-shell neighbours are in a nearer structural arrangement than the one expected for a bulk hexagonal TiB2, which could be due to the formation of mixed Ti-B-C compound in a structural unit similar to the one found in h-TiB2.Peer reviewe
Growth, interfacial microstructure and optical properties of NiO thin films with various types of texture
International audienceNiO thin films with random, fiber and in-plane textures have been successfully deposited at near room temperature by reactive magnetron sputtering on glass, silicon and Al 2 O 3 (0001) substrates. Self-texture related with the deposition conditions and crystallographic characters competes with the driving force from the matched substrate. Such a competition can be used to control the texture of thin films on matched substrates, especially when the promoting orientations from self-texture and substrate are different. Enhancing this competition tends to suppress the self-texture of NiO thin films on Al 2 O 3 (0001) substrates, whereas restricting the competition is beneficial to produce the in-plane textured NiO thin films. In addition, it is found that the optical transmittance of NiO thin films on Al 2 O 3 (0001) substrates can also be tuned by such competition. Interfacial microstructure analyses of NiO thin films on amorphous substrates clearly evidence the existence a nanocomposite layer at the initial growth, which is composed of NiO nanocrystals surrounded by amorphous matrix. In contrast, in-plane textured NiO thin films on Al 2 O 3 (0001) substrates exhibit sharp interface without nanocrystals or amorphous matrix. We believe these results provide a general framework of tuning the textures and properties of thin films on matched substrates
Thermochromic effect in NdNiO 3−δ thin films annealed in ambient air
International audienceThe synthesis of NdNiO3 perovskite structure was achieved by soft post deposition annealing of initially amorphous thin films reactively sputter deposited on silicon substrates. The physical measurements were fully consistent with the properties expected for the thermochromic NdNiO3 phase. Upon heating, the optical transmission that was correlated with the electrical properties decreased in the infrared domain showing a thermochromic effect in this optical region. The metal–insulator transition temperature was found to be −68 °C for the specimen tested and the jump in resistance at the transition was 1.4 orders of magnitude. The state-of-the-art methods that normally involve an annealing at a high oxygen pressure (200 × 105 Pa) or epitaxial stabilization were considerably improved in this work by the use of dc sputtering and the optimization of the deposition conditions. Therefore, the novel soft process proposed here opens up numerous research possibilities
- …