37 research outputs found
Eugenol: A Promising Building Block for Synthesis of Radically Polymerizable Monomers
Eugenol, a natural phenol currently mainly obtained from clove oil, is an interesting aromatic building block for the synthesis of novel biobased monomers. It can also be obtained from lignin depolymerization, becoming a promising building block due to lignin availability as biomass feedstock. The synthesis of eight monomers derived from eugenol containing polymerizable functional groups is achieved. The (meth)acrylation of eugenol, isoeugenol, and dihydroeugenol is performed and the solution homopolymerization of these biobased monomers is studied. Moreover, aiming to prepare functional polymers, the introduction of epoxy and cyclic carbonate groups is executed via modification of the allylic double bond present in eugenol derived methacrylate. Thus, a novel platform of versatile biobased monomers derived from eugenol is presented, opening the opportunity to use them in a wide range of polymerization processes and applications
Properties of Undoped and (Al, In) Doped ZnO Thin Films Prepared by Ultrasonic Spray Pyrolysis for Solar Cell Applications
Zinc oxide (ZnO) is an n-type semiconductor with a large optical gap (3.4 eV) belonging to the transparent
conductive oxides family (TCO). Strongly present as optical window in the chalcopyrite based structures
CIGS and CIS.
The structural, morphological, optical and electrical properties of ZnO thin films deposited onto glass
substrates by ultrasonic spray pyrolysis (USP) technique have been investigated. For comparison and a
better understanding of physical properties of undoped and (Al, In) doped ZnO thin films, a number of
techniques, including XRD, SEM, optical absorption method (UV) and four-point probe technique were
used to characterize the obtained ZnO thin films. Structural analysis shows that all the films were found
to be polycrystalline with a wurtzite structure and show a (1 0 1) preferential growth. Besides, we noted
that the preferred orientation does not depend on the nature of dopant. The band gaps (Eg) varied from
3.35 to 3.37 eV by Al and In dopants
Mrk 421, Mrk 501, and 1ES 1426+428 at 100 GeV with the CELESTE Cherenkov Telescope
We have measured the gamma-ray fluxes of the blazars Mrk 421 and Mrk 501 in
the energy range between 50 and 350 GeV (1.2 to 8.3 x 10^25 Hz). The detector,
called CELESTE, used first 40, then 53 heliostats of the former solar facility
"Themis" in the French Pyrenees to collect Cherenkov light generated in
atmospheric particle cascades. The signal from Mrk 421 is often strong. We
compare its flux with previously published multi-wavelength studies and infer
that we are straddling the high energy peak of the spectral energy
distribution. The signal from Mrk 501 in 2000 was weak (3.4 sigma). We obtain
an upper limit on the flux from 1ES 1426+428 of less than half that of the Crab
flux near 100 GeV. The data analysis and understanding of systematic biases
have improved compared to previous work, increasing the detector's sensitivity.Comment: 15 pages, 14 figures, accepted to A&A (July 2006) August 19 --
corrected error in author lis
The First VERITAS Telescope
The first atmospheric Cherenkov telescope of VERITAS (the Very Energetic
Radiation Imaging Telescope Array System) has been in operation since February
2005. We present here a technical description of the instrument and a summary
of its performance. The calibration methods are described, along with the
results of Monte Carlo simulations of the telescope and comparisons between
real and simulated data. The analysis of TeV -ray observations of the
Crab Nebula, including the reconstructed energy spectrum, is shown to give
results consistent with earlier measurements. The telescope is operating as
expected and has met or exceeded all design specifications.Comment: Accepted by Astroparticle Physic
Вплив товщини пластини та кількості сіток трафаретного друку на Al-BSF у кристалічних кремнієвих сонячних елементах
У роботі були проведені експериментальні дослідження процесу легування алюмінієвих (Al) паст,
надрукованих трафаретним друком на кремнієвих поверхнях для сонячних елементів. Досліджений
вплив товщини пластини та кількості сіток трафаретного друку на властивості поля задньої поверхні
Al (Al-BSF) кремнієвих сонячних елементів Чохральського (Cz-Si). Використовувалися екрани з різною кількістю сіток (150, 200 і 400 меш) для друку різної кількості пасти Al (7, 9,4 та 12 мг/см2). Швидкий термічний відпал (RTP) при 750 °C і 800 °C протягом 60 с був застосований для формування ALBSF. SEM показав утворення шорсткої поверхні з шаром легуючого шару товщиною 4,31 мкм на
об’ємній кремнієвій пластині. Аналіз ECV та SIMS показав, що пікова температура відпалу 750 °C і
кількість пасти Al 12 мг/см2 підходять для створення оптимального Al-BSF. Ця робота виявила, що на
властивості Al-BSF сильно впливає кількість меш, яка використовується для трафаретного друку пасти Al. Однак не було помічено монотонного зв’язку з товщиною пластини. Маска з 150 меш дозволила
отримати високі концентрації Al на поверхні, максимальну глибину дифузії та більший середній час
життя носіїв заряду.In this study, experiments on the alloying process from screen-printed aluminum (Al) pastes on silicon
surfaces for solar cell applications were conducted. We investigated the effect of wafer thickness and
screen-printing mesh counts on the Al back surface field (Al-BSF) properties of Czochralski silicon (Cz-Si)
solar cells Screens with different mesh counts (150, 200 and 400 mesh) were used to print variable
amounts of Al paste (7, 9.4 and 12 mg/cm2). Rapid thermal annealing (RTP) annealing processes of 750 °C
and 800 °C for 60 s were applied to form AL-BSF. SEM micrographs showed the formation of a rough surface with 4.31 µm alloying layer over bulk Si wafer. ECV and SIMS analysis showed that an annealing
peak temperature of 750 °C and an amount of Al paste of 12 mg/cm2 are suitable for the creation of an optimal Al-BSF. This work revealed that Al-BSF properties are strongly affected by the mesh counts used in
screen-printing of Al paste. However, no monotonic relationship was noticed with the wafer thickness. The
mask with 150 meshes allowed to obtain high Al concentrations at the surface, maximum diffusion depth
and longer average lifetimes of charge carriers
Growth by the heat exchanger method of NaBiW2O8 and Na5B2P3O13 crystals
In this paper, we present the results of our attempt to grow NaBiW2O8 (NBW) and Na5B2P3O13 (NBP) crystals by the heat exchanger method (HEM). This method is slightly different from the Bridgman technique: the crucible is kept fixed in the setup and the center of the crucible bottom is cooled by a variable helium gas flow. It allows very good control of the growth rate and minimizes parasitic crystallization at the crucible walls. First experiments for growing these two materials by the HEM technique have shown very promising results with single-crystal sizes of few cubic centimetres.
Aluminium-induced crystallization of amorphous silicon films deposited by DC magnetron sputtering on glasses
Amorphous silicon (a-Si) and hydrogenated amorphous silicon (a-Si:H) films were deposited by DC magnetron sputtering technique with argon and hydrogen plasma mixture on Al deposited by thermal evaporation on glass substrates. The a-Si/Al and a-Si:H/Al thin films were annealed at different temperatures ranging from 250 to 550 °C during 4 h in vacuum-sealed bulb. The effects of annealing temperature on optical, structural and morphological properties of as-grown as well as the vacuum-annealed a-Si/Al and a-Si:H/Al thin films are presented in this contribution. The averaged transmittance of a-Si:H/Al film increases upon increasing the annealing temperature. XRD measurements clearly evidence that crystallization is initiated at 450 °C. The number and intensity of diffraction peaks appearing in the diffraction patterns are more important in a-Si:H/Al than that in a-Si/Al layers. Results show that a-Si:H films deposited on Al/glass crystallize above 450 °C and present better crystallization than the a-Si layers. The presence of hydrogen induces an improvement of structural properties of poly-Si prepared by aluminium-induced crystallization (AIC
Gorenflot, R. (1994). Biologie végétale. Plantes supérieures. 1. Appareil végétatif.
The synthesis of poly(vinylidene fluoride)-graft-oligomeric hexafluoropropylene oxide graft copolymers [poly[VDF-g-oligo(HFPO)-PIPE] is presented, where VDF, HFPO, and PIPE stand for vinylidene fluoride (CH2vCF2), hexafluoropropylene oxide (CF3CFCF2O) and, perfluoroisopropenylether (–OC(CF3)vCF2), respectively. First, an 82% isolated yield of oligo(HFPO)-PIPE macromonomer was achieved by using oligo(HFPO) primary iodide as the starting reagent. Then, the radical copolymerization of VDF with the PIPE comonomer, initiated by perfluoro-3-ethyl-2,4-dimethyl-3-pentyl persistent radical (PPFR), was studied under various conditions. The PPFR initiator, stable at room temperature, was able to release a •CF3 radical starting from 80 °C. The resulting poly[VDF-g-oligo(HFPO)-PIPE] graft copolymers were produced in good isolated yields (76 to 97%). The molar percentages and molar masses of such graft copolymers were assessed by 19F-NMR spectroscopy using the CF3– end-group label. The molar percentages of VDF and oligo(HFPO)-PIPE comonomers reached up to 99% and 20%, respectively, while the molar masses ranged between 7500 and 42 600 g mol−1. Their thermal properties showed: (i) fair to satisfactory thermostability (T5%d ) showing up to 271 °C under nitrogen, (ii) glass transition (Tg) ranged from −81 to −82 °C while (iii) their melting temperature (Tm) ranged between 150 and 163 °C. Moreover, the synthesized copolymers were demonstrated to be highly omniphobic (i.e., simultaneously hydrophobic and oleophobic), showing a water contact angle of ca. 133°, a hexadecane contact angle ca. 70°, and a surface energy as low as 12 mN m−1