Compatibilização de blendas de poliamida 6/ABS usando os copolímeros acrílicos reativos MMA-GMA e MMA-MA. Parte 2: Comportamento termomecânico e morfológico das blendas Compatibilization of Polyamide 6/ABS blends using MMA-GMA and MMA-MA reactive acrylic copolymers. Part 2. Thermal-mechanical and morphological behavior of blends

Blendas poliméricas de poliamida 6 (PA6) com acrilonitrila-butadieno-estireno (ABS) foram preparadas em extrusora de rosca dupla, utilizando-se os copolímeros metacrilato de metila - metacrilato de glicidila (MMA-GMA) e metacrilato de metila-anidrido maléico (MMA-MA) como agentes de compatibilização. O ABS, por si só, não foi capaz de tenacificar a PA6, apresentando uma morfologia de fases com grandes e pequenos aglomerados na matriz PA6. A introdução do copolímero MMA-GMA, como compatibilizante do sistema, não melhorou significativamente as propriedades de impacto da blenda PA6/ABS. As fotomicrografias obtidas por microscopia eletrônica de transmissão (MET) indicaram uma morfologia com duas populações distintas de ABS: aglomerados e pequenas partículas dispersas, resultando em uma distribuição não-uniforme de domínios de ABS. A blenda compatibilizada com MMA-MA foi supertenaz (> 800 J/m) na temperatura ambiente e em baixas temperaturas (~ -10 °C), com baixas concentrações de compatibilizante e baixos teores de MA no copolímero. As blendas PA6/ABS compatibilizadas com MMA-MA apresentaram uma morfologia de partículas bem dispersas e adequadamente distribuídas na matriz, evidenciando a presença efetiva do copolímero como agente de compatibilização reativo deste sistema.<br>Blends of Polyamide 6 (PA6) with acrylonitrile-butadiene-styrene (ABS) were prepared in a corotating twin-screw extruder, using the poly(methyl methacrylate-co-glycidyl methacrylate) (MMA-GMA) and poly(methyl methacrylate-co-maleic anhydride) (MMA-MA) copolymers as compatibilizing agents. The ABS by itself was not capable to toughen PA6 and showed a phase morphology with large and small agglomerates in the PA6 matrix. The introduction of MMA-GMA copolymer as a compatibilizing agent in the system did not significantly improve the impact properties of PA6/ABS blend. Transmission electron microscope (TEM) photomicrographs indicated a morphology with two distinct populations of ABS: agglomerates and small dispersed particles resulting in a non-uniform distribution of ABS domains. The compatibilized blend with MMA-MA was super-tough (> 800 J/m) at room temperature and low temperature (~ -10 °C) with small amounts of MA in the copolymer and small amounts of compatibilizer in the blend. The PA6/ABS compatibilized blends with MMA-MA showed a morphology of well dispersed and distributed rubber particles in PA6 matrix, thus demonstrating the effective presence of the copolymer as a compatibilizing reactive agent of this system

ZnO homoepitaxy on the O polar face of hydrothermal and melt-growth substrates by pulsed laser deposition

2 cm diameter hydrothermal ZnO crystals were grown and then made into substrates using both mechanical and chemical-mechanical polishing (CMP). CMP polishing showed superior results with an (0002) Ω scan full width half maximum (FWHM) of 67 arcsec and an root mean square (RMS) roughness of 2 Å. In comparison, commercial melt-grown substrates exhibited broader X-ray diffraction (XRD) linewidths with evidence of sub-surface crystal damage due to polishing, including a downward shift of c-lattice parameter..