Advanced synchrotron studies of ye'elimite-based cement pastes
Synchrotron characterization techniques [1] are being used to study Portland-based cements and recently also CSA and related cements. A key property of these techniques is that they do not require sample preparation, so the microstructures of the pastes can be preserved. The classical application of synchrotron tools is powder diffraction used to determine the crystalline phase content evolution with hydration including the overall amorphous fraction. Furthermore, other most advanced techniques are being applied to ye'elimite-containing pastes such as i) Total Scattering Synchrotron Powder Diffraction (TS-SXPD), and ii) Ptychographic Synchrotron X-ray Computed Tomography (PSXCT). All these applications will be reviewed here.
TS-SXPD data coupled with the Pair Distribution Function (PDF) analysis methodology [2] allows having a better insight about the nanocrystalline/amorphous atomic arrangements in the gels. It has been very recently shown that nanogibbsite with very small particles, 3nm, is the main constituent of ye'elimite-gypsum hydration paste [2]. Nanogibbsite particles being smaller than those originated from the hydration of monocalcium aluminate. In addition, PSXCT is a tomographic technique that profits from the partly coherent nature of the synchrotron beam to provide better (smaller) resolution, which can be lower than 100 nm. It also provides the mass densities if the chemical stoichiometries are known. This technique has been applied to ye'elimite hydration to determine the microstructure and chiefly the bulk densities of nanogibbsite [3]. The microstructure evolution at early age was also followed [4]. Figure 1 shows an example of a slide of the electron density tomogram for a ye'elimite paste at 8 days of hydration and the corresponding histogram for the full volume with all phases identified.Universidad de MĂĄlaga. Campus de Excelencia Internacional AndalucĂa Tech.This work has been supported by Spanish MINECO through BIA2014-57658-C2 and BIA2017-82391-R, which are co-funded by FEDER
In-situ hydration studies of yeâelemite at early ages for understanding eco-cement performances'
PĂłster; ALBA User Meeting and VI AUSE Conferenc
Applications of synchrotron x-ray powder diffraction in hydrated cements: high-resolution and high-pressure studies
The main aim of this study is to apply synchrotron radiation techniques for the study of hydrated cement pastes. In particular, the tetracalcium aluminoferrite phase, C4AF in cement nomenclature, is the major iron-containing phase in Ordinary Portland Cement (OPC) and in iron rich belite calcium sulfoaluminate cements.
In a first study, the hydration mechanism of pure tetracalcium aluminoferrite phase with water-to-solid ratio of 1.0 has been investigated by HR-SXRPD (high resolution synchrotron X-ray powder diffraction). C4AF in the presence of water hydrates to form mainly an iron-containing hydrogarnet-type (katoite) phase, C3A0.84F0.16H6, as single crystalline phase. Its crystal structure and stoichiometry were determined by the Rietveld method and the final disagreement factors were RWP=8.1% and RF=4.8% [1]. As the iron content in the product is lower than that in C4AF, it is assumed that part of the iron also goes to an amorphous iron rich gel, like the hydrated alumina-type gel, as hydration proceeds. Further results from the high-resolution study will be discussed.
In a second study, the behavior of pure and iron-containing katoites (C3AH6 and C3A0.84F0.16H6) under pressure have been analyzed by SXRPD using a diamond anvil cell (DAC) and then their bulk moduli were determined. The role of the pressure transmitting medium (PTM) has also been studied. In this case, silicone oil as well as methanol/ethanol mixtures have been used as PTM. Some ânew peaksâ were detected in the pattern for C3A0.84F0.16H6 as pressure increases, when using ethanol/methanol as PTM. These new peaks were still present at ambient pressure after releasing the applied pressure. They may correspond to crystalline nordstrandite or doyleite from the crystallization of amorphous aluminium hydroxide. The results from the high-pressure study will also be discussed.Universidad de MĂĄlaga. Campus de Excelencia Internacional AndalucĂa Tech. Acknowledgments: We thank CELLS-ALBA (Barcelona, Spain) for providing synchrotron beam time. We also thank the financial support by BIA2014-57658-C2-1-R and BIA2014-57658-C2-2-R (FEDER)
Differential proteome profile of skin mucus of gilthead seabream (Sparus aurata) after probiotic intake and/or overcrowding stress
Author's accepted version (post-print)
Skin mucus proteome map of European sea bass (Dicentrarchus labrax)
Author's accepted version (post-print).This is the peer reviewed version of the following article: Cordero, H., Brinchmann, M.F., Cuesta, A., Meseguer, J. & Esteban, M.A. (2015). Skin mucus proteome map of European sea bass (Dicentrarchus labrax). Proteomics, 15(23-24), 4007-4020, which has been published in final form at http://dx.doi.org/10.1002/pmic.201500120. This article may be used for non-commercial purposes in accordance with Wiley Terms and Conditions for Self-Archiving (http://olabout.wiley.com/WileyCDA/Section/id-820227.html)
Early hydration study of standard and doped Alite-Belite-Yeâelimite (ABY) cements through Synchrotron Radiation
The manufacturing of ye'elimite-rich cements releases from 15 to 37%, depending on their
composition, less CO2 to the atmosphere than ordinary Portland cement (OPC). BYF cements
containing belite, yeâelimite and ferrite as main crystalline phases, are promising eco-friendly binders.
Nevertheless, belite, its main phase, shows a slow hydrating behaviour and the mechanical strengths
are lower than OPC at early ages. Some alternatives to solve this problem are: i) forming alite jointly
with belite and yeâelimite during clinkering, Alite Belite Yeâelimite (ABY) clinkers. The hydration of alite
and yeâelimite would develop high mechanical strengths at early ages, and belite contributes to later
curing times; ii) a second alternative is the stabilisation of alpha forms of belite using dopants such as
boron named here after dABY.
In this work, two different types of ABY clinkers (standard and doped) have been prepared and
characterized to understand their different hydration mechanisms at the same water-to-cement (w/c)
ratio. The clinkers have been prepared using CaF2 and ZnO as mineralizers, and borax as dopant
agent to stabilize alpha forms of belite (âH-C2S). Afterwards, 14 wt% of anhydrite (as soluble sulphate
source) was added to prepare the corresponding cements. Finally, the hydration study was performed
at w/c ratio of 0.5. Here, an in-situ hydration study using synchrotron X-ray powder diffraction (SXRPD)
for the first 14 hours of hydration is reported. Moreover, these results will be combined with the ex-situ
laboratory X-ray powder diffraction study (LXRPD) at 1 day of hydration and calorimetric results.
Rietveld quantitative phase analysis has been used to establish the phase evolution across the time.Universidad de MĂĄlaga. Campus de Excelencia Internacional AndalucĂa Tech.
MINECO ( BIA2017-82391-R), co-funded by FEDER, and I3 [IEDI-2016-0079]
Water-to-cement ratio influence on low-carbon cements performances
Portland Cement (PC) is the most important active ingredient in most of the construction concrete. However, the PC production is associated with a high carbon dioxide release (around 1 ton of CO2 per ton of PC). One approach to reduce CO2 emissions consists on the reformulation of the clinker with less calcite demanding phases, such as, belite rich clinkers. The drawback of this kind of clinkers is the low reactivity of belite (beta-belite). In order to compensate this problem, belite rich clinkers can be prepared with yeâelimite and ferrite or with alite [known as belite-yeâelimite-ferrite (BYF) and belite-alite-yeâelimite (BAY), respectively]. In addition, it can be improved by using a high reactive belite polymorph, such as alpha-belite.
In this work, the hydration and mechanical behaviour of BYF and BAY cements (with beta and/or alpha-belite) with different water-to-cement ratios have been studied. The clinkers were produced using natural raw materials, and were mixed with anhydrite (CaSO4) to prepare the corresponding cements. At early ages, the main hydration products of these cements were ettringite, calcium monosulfoaluminate and amorphous aluminium hydroxide. At later ages, stratlingite, katoite and amorphous C-S-H were found. The compressive strength values of the corresponding mortars were correlated with the mineralogy evolution of the pastes (mainly obtained by XRD and TGA).Universidad de MĂĄlaga. Campus de Excelencia Internacional AndalucĂa Tech.
I3-RamĂłn y Cajal
Universidad de Malag
Synchrotron x-ray pair distribution function: A tool to characterize cement gels
Cement matrices contain large amounts of crystalline phases jointly with amorphous and/or nanocrystalline phases. Consequently, their analyses are very challenging. Synchrotron powder diffraction in combination with the pair distribution function (PDF) methodology is very useful to characterize such complex cement pastes. This work is focused on the study of the short and medium range atomic arrangement(s) in the different nanocrystalline gels which are present in the cement pastes through total scattering Pair Distribution Function quantitative phase analyses.Universidad de MĂĄlaga. Campus de Excelencia Internacional AndalucĂa Tech. Acknowledgments: We thank CELLS-ALBA (Barcelona, Spain) for providing synchrotron beam time and the financial support by BIA2014-57658-C2-1-R and BIA2014-57658-C2-2-R, which is co-funded by FEDER. We also thank Dr. Monica Dapiaggi for her contribution with the PDF study of Ca(OH)2 monolayer
Rietveld Quantitative Phase Analysis of Oil Well Cement: in Situ Hydration Study at 150 Bars and 150 °C
Oil and gas well cements are multimineral materials that hydrate under high pressure
and temperature. Their overall reactivity at early ages is studied by a number of techniques
including through the use of the consistometer. However, for a proper understanding of the
performance of these cements in the field, the reactivity of every component, in realâworld
conditions, must be analysed. To date, in situ high energy synchrotron powder diffraction studies
of hydrating oil well cement pastes have been carried out, but the quality of the data was not
appropriated for Rietveld quantitative phase analyses. Therefore, the phase reactivities were
followed by the inspection of the evolution of nonâoverlapped diffraction peaks. Very recently, we
have developed a new cell specially designed to rotate under high pressure and temperature. Here,
this spinning capillary cell is used for in situ studies of the hydration of a commercial oil well
cement paste at 150 bars and 150 °C. The powder diffraction data were analysed by the Rietveld
method to quantitatively determine the reactivities of each component phase. The reaction degree
of alite was 90% after 7 hours, and that of belite was 42% at 14 hours. These analyses are accurate,
as the in situ measured crystalline portlandite content at the end of the experiment, 12.9 wt%,
compares relatively well with the value determined ex situ by thermal analysis, i.e., 14.0 wt%. The
crystalline calcium silicates forming at 150 bars and 150 °C are also discussed.This research was funded by Spanish MINECO, grant number BIA2017â82391âR which is coâfunded
by FEDER.
We thank Marc Malfois for his help during the experiment performed at NCDâSWEET
beamline at ALBA synchrotron. We also thank Marcus Paul (Dyckerhoff GmbH) for providing the OWC
sample with its characterization and helpful discussions