Limitations of the use of concrete resistivity as an indicator for the rate of chloride-induced macro-cell corrosion

An experimental setup was designed to study the impact of concrete resistivity on the rate of chloride-induced reinforcement corrosion. Small pieces of mild steel were used to simulate pits (anodes) that form when chlorides come into contact with the reinforcement. The galvanic current was measured between the simulated anodes and a cathode network. Comparisons were made between the galvanic current and the concrete bulk resistivity. The bulk resistivity was varied using two mortar mixes (made of plain Portland cement and a blended Fly ash cement) which were exposed in different temperature and moisture conditions. Despite a high scatter in the results, it was clear that the relationship between bulk resistivity and corrosion rate depended on the mortars tested. The findings presented in this paper and the accompanying work strongly indicate that concrete bulk resistivity alone does not provide sufficient information for assessment of the corrosion rate for chloride-induced macro-cell corrosio

Methods for characterising the steel–concrete interface to enhance understanding of reinforcement corrosion: a critical review by RILEM TC 262-SCI

The steel–concrete interface (SCI) is a complex, multi-phase and multi-scale system. It is widely known to influence the performance and long-term durability of concrete structures. However, a fundamental understanding of its properties and effects on corrosion initiation of embedded reinforcing steel remains elusive. This is attributed to its complicated heterogeneity and time-dependent nature, exacerbated by the lack of suitable techniques for systematic and detailed characterisation. This paper, prepared by members of the RILEM Technical Committee 262-SCI, critically reviews available information regarding current methods (laboratory or field-based) for characterising local properties of the SCI that have been identified as governing factors affecting corrosion initiation. These properties include characteristics of the steel such as mill scale and rust layers, and characteristics of the concrete such as interfacial voids, microstructure and moisture content. We evaluated over twenty methods and summarised their advantages, applications and limitations. The findings show a severe lack of well established, non-destructive techniques that are suitable for direct monitoring of the SCI at a representative scale with sufficiently high resolution (spatial, temporal), particularly for moisture related aspects. Several promising novel techniques with significant potential for further development and application were identified and discussed. Finally, we provide several recommendations for future research needs that are required to advance this critically important topic

Influence of slag composition on the stability of steel in alkali-activated cementitious materials

Among the minor elements found in metallurgical slags, sulfur and manganese can potentially influence the corrosion process of steel embedded in alkali-activated slag cements, as both are redox-sensitive. Particularly, it is possible that these could significantly influence the corrosion process of the steel. Two types of alkali-activated slag mortars were prepared in this study: 100% blast furnace slag and a modified slag blend (90% blast furnace slag? 10% silicomanganese slag), both activated with sodium silicate. These mortars were designed with the aim of determining the influence of varying the redox potential on the stability of steel passivation under exposure to alkaline and alkaline chloride-rich solutions. Both types of mortars presented highly negative corrosion potentials and high current density values in the presence of chloride. The steel bars extracted from mortar samples after exposure do not show evident pits or corrosion product layers, indicating that the presence of sulfides reduces the redox potential of the pore solution of slag mortars, but enables the steel to remain in an apparently passive state. The presence of a high amount of MnO in the slag does not significantly affect the corrosion process of steel under the conditions tested. Mass transport through the mortar to the metal is impeded with increasing exposure time; this is associated with refinement of the pore network as the slag continued to react while the samples were immersed