Effect of carbide distribution on rolling-element fatigue life of AMS 5749

Endurance tests with ball bearings made of corrosion resistant bearing steel which resulted in fatigue lives much lower than were predicted are discussed. Metallurgical analysis revealed an undesirable carbide distribution in the races. It was shown in accelerated fatigue tests in the RC rig that large, banded carbides can reduce rolling element fatigue life by a factor of approximately four. The early spalling failures on the bearing raceways are attributed to the large carbide size and banded distribution

Plasma Relaxation and Topological Aspects in Hall Magnetohydrodynamics

Parker's formulation of isotopological plasma relaxation process in magnetohydrodynamics (MHD) is extended to Hall MHD. The torsion coefficient alpha in the Hall MHD Beltrami condition turns out now to be proportional to the "potential vorticity." The Hall MHD Beltrami condition becomes equivalent to the "potential vorticity" conservation equation in two-dimensional (2D) hydrodynamics if the Hall MHD Lagrange multiplier beta is taken to be proportional to the "potential vorticity" as well. The winding pattern of the magnetic field lines in Hall MHD then appears to evolve in the same way as "potential vorticity" lines in 2D hydrodynamics

The Apollo Auxiliary Power Supply System, Project Apollo

No abstract availabl

Border parasites: schistosomiasis control among Uganda's fisherfolk

Copyright @ 2012 Taylor & Francis. This article has been made publically available through the Brunel Open Access Publishing Fund.It is recognized that the control of schistosomisais in Uganda requires a focus on fisherfolk. Large numbers suffer from this water-borne parasitic disease; notably along the shores of lakes Albert and Victoria and along the River Nile. Since 2004, a policy has been adopted of providing drugs, free of charge, to all those at risk. The strategy has been reported to be successful, but closer investigation reveals serious problems. This paper draws upon long-term research undertaken at three locations in northwestern and southeastern Uganda. It highlights consequences of not engaging with the day to day realities of fisherfolk livelihoods; attributable, in part, to the fact that so many fisherfolk live and work in places located at the country’s international borders, and to a related tendency to treat them as "feckless" and "ungovernable". Endeavours to roll out treatment end up being haphazard, erratic and location-specific. In some places, concerted efforts have been made to treat fisherfolk; but there is no effective monitoring, and it is difficult to gauge what proportion have actually swallowed the tablets. In other places, fisherfolk are, in practice, largely ignored, or are actively harassed in ways that make treatment almost impossible. At all sites, the current reliance upon resident "community" drug distributors or staff based at static clinics and schools was found to be flawed.The Schistosomiasis Control Initiative, Imperial College, under the auspices of the Bill and Melinda Gates Foundation

In situ X-ray diffraction of CaO based CO2 sorbents

In situ X-ray diffraction coupled with Rietveld refinement has been used to study CO2 capture by CaO, Ca(OH)2 and partially hydrated CaO, as a function of temperature. Phase quantification by Rietveld refinement was performed to monitor the conversion to CaCO3 and the results were compared to those derived using thermogravimetric analysis (TGA). It was found that Ca(OH)2 converted directly to 100% CaCO3 without the formation of a CaO intermediate, at ca. 600 °C. Both pure CaO and partially hydrated CaO (33.6 wt% Ca(OH)2) reached the same capture capacity, containing approximately 65 wt% CaCO3 at 800 °C. It was possible to provide direct evidence of the capture mechanism. The stresses in the Ca(OH)2 phase of the partially hydrated CaO were found to be more than 20 times higher than its strength, leading to disintegration and the generation of nano-sized crystallites. The crystallite size determined using diffraction (75 × 16 nm) was in good agreement with the average crystallite size observed using TEM (of 83 × 16 nm). Electron diffraction patterns confirmed coexistence of CaO and Ca(OH)2. The analysis provides an explanation of the enhanced capture/disintegration observed in CaO in the presence of steam

Instabilities leading to vortex lattice formation in rotating Bose-Einstein condensates

We present a comprehensive theoretical study of vortex lattice formation in atomic Bose-Einstein condensates confined by a rotating elliptical trap. We consider rotating solutions of the classical hydrodynamic equations, their response to perturbations, as well as time-dependent simulations. We discriminate three distinct, experimentally testable, regimes of instability: {\em ripple}, {\em interbranch}, and {\em catastrophic}. Under symmetry-breaking perturbations these instabilities lead to lattice formation even at zero temperature. While our results are consistent with previous theoretical and experimental results, they shed new light on lattice formation.Comment: 5 pages, 2 figure

Bounds on higher-order Lorentz-violating photon sector coefficients from an asymmetric optical ring resonator experiment

Optical resonators provide a powerful tool for testing aspects of Lorentz invariance. Here, we present a reanalysis of an experiment where a path asymmetry was created in an optical ring resonator by introducing a dielectric prism in one arm. The frequency difference of the two fundamental counter-propagating modes was then recorded as the apparatus was orientation-modulated in the laboratory. By assuming that the minimal Standard-Model Extension coefficients vanish we are able to place bounds on higher-order parity-odd Lorentz-violating coefficients of the Standard-Model Extension. The results presented in this work set the first constraints on two previously unbounded linear combinations of d=8 parity-odd nonbirefringent nondispersive coefficients of the photon sector.Comment: 6 pages, 4 figures, 3 tables, accepted for publication in Physics Letters

Flexural fatigue of hollow rolling elements

Hollow cylindrical bars were tested in the rolling-contact fatigue tester to determine the effects of material and outside diameter to inside diameter (OD/ID) ratios of 2.0, 1.6, 1.4, and 1.2 on fatigue failure mode and subsequent failure propagation. The range of applied loads with these OD/ID ratios resulted in maximum tangential tensile stresses ranging from 165 to 655 megapascals (24,000 to 95,000 psi) at the bore surface. Flexural failures of the hollow test bars occurred when this bore stress was 490 megapascals (71,000 psi) or greater with AISI 52100 hollow bars and 338 megapascals (49,000 psi) or greater with AISI M-50 hollow bars. Good correlation was obtained in relating the failures of these hollow bars with flexural failures of drilled balls from previously published full scale bearing tests

Corrosion of simulated bearing components of three bearing steels in the presence of chloride-contaminated lubricant

Corrosion tests were run with AISI 52100, AISI M-50 and AMS 5794 under conditions that simulate the crevice corrosion found in aircraft ball and roller bearings rejected at overhaul for corrosion. Test specimens were fabricated that simulated the contacts of balls or rollers and the raceways. Corrosion cells were assembled in the presence of a lubricant contaminated with water and chloride ions. The cell was then thermally cycled between 339 K (150 F) and 276 K (37 F). The corrosion observed after 14 cycles was that of crevice and pitting corrosion typically found in aircraft bearings. AMS 5749 showed a very slight amount of corrosion. No appreciable differences were noted between AISI 52100 and AISI M-50, but both showed much greater corrosion than AMS 5749. The corrosion pits observed in AISI M-50 appeared to be fewer in number but generally deeper and larger than in AISI 52100