Investigation of strain rate sensitivity of Gum Metal under tension using digital image correlatio
Mechanical behavior of a multifunctional titanium alloy Gum Metal was investigated by conducting tensile tests at various strain rates and applying digital image correlation (DIC) technique. Stress–strain curves confirmed low Young’s modulus and high strength of the alloy. The determined values of yield strength had a tendency to increase, whereas the elongation to the specimen rupture tended to decrease with increasing strain rate. True stress versus strain curves were analyzed using selected lengths of virtual extensometer (VE) placed in the strain localization area. When the initial length of the VE was the same as the gauge length, work hardening was observed macroscopically at lower strain rates, and a softening was seen at higher strain rates. However, the softening effect was not observed at the shorter VE lengths. Evolution of the Hencky strain and rate of deformation tensor component fields were analyzed for various strain rates at selected stages of Gum Metal load-ing. The DIC analysis demonstrated that for lower strain rates the deformation is macroscopically uniform up to the higher average Hencky strains, whereas for higher strain rates the strain localization occurs at the lower average Hencky strains of the deformation process and takes place in the smaller area. It was also found that for all strain rates applied, the maximal values of Hencky strain immediately before rupture of Gum Metal samples were similar for each of the applied strain rates, and the maximal local values of deformation rate were two orders higher when compared to applied average strain rate values
Nanomaterials by severe plastic deformation: review of historical developments and recent advances
International audienceSevere plastic deformation (SPD) is effective in producing bulk ultrafine-grained and nanostructured materials with large densities of lattice defects. This field, also known as NanoSPD, experienced a significant progress within the past two decades. Beside classic SPD methods such as high-pressure torsion, equal-channel angular pressing, accumulative roll-bonding, twist extrusion, and multi-directional forging, various continuous techniques were introduced to produce upscaled samples. Moreover, numerous alloys, glasses, semiconductors, ceramics, polymers, and their composites were processed. The SPD methods were used to synthesize new materials or to stabilize metastable phases with advanced mechanical and functional properties. High strength combined with high ductility, low/room-temperature superplasticity, creep resistance, hydrogen storage, photocatalytic hydrogen production, photocatalytic CO2 conversion, superconductivity, thermoelectric performance, radiation resistance, corrosion resistance, and biocompatibility are some highlighted properties of SPD-processed materials. This article reviews recent advances in the NanoSPD field and provides a brief history regarding its progress from the ancient times to modernity
Dynamic recrystallization and recovery during high-pressure torsion : Experimental evidence by torque measurement using ring specimens
訂正:反応焼結法で作製した高強度TiC<sub>(1−</sub><i><sub>X</sub></i><sub>)</sub>粒子強化型Ti基複合材料の高比抵抗化と高剛性化に及ぼすCとAl元素の影響
Development of ultrahigh strength and high ductility in nanostructured iron alloys with lattice softening and nanotwins
チテキ ショウガイ ヨウゴ ガッコウ コウトウブ セイト ノ ガクブ ジュギョウ エノ サンカ ニ カンスル ケンキュウ : ソウゴウ エンシュウ ニオケル ジュギョウ カイハツ ジレイ ヨリ
An exploratory study of the development of a "Sogo Enshu" class was planned and implemented for the purpose of (1) providing university students in teacher training courses opportunities to learn in a shared environment with the mentally challenged and, (2) providing opportunities for high school students of a school for the mentally handicapped (SMH) to experience a class held at a university so as to expand their future learning options.Class participation involved twenty-one university students and nine high school students of the SMH. The topic of the class was the culture and education of the handicapped in India and Sri Lanka. It was observed that high school students of the SMH took part in the class with a more positive attitude compared with university students, and also openly expressed their ideas with regard to their handicap, which may change the image of university students towards the learning needs of the mentally challenged
Thermomechanical Studies of Yielding and Strain Localization Phenomena of Gum Metal under Tension
This paper presents results of investigation of multifunctional β-Ti alloy Gum Metal subjected to tension at various strain rates. Digital image correlation was used to determine strain distributions and stress-strain curves, while infrared camera allowed for us to obtain the related temperature characteristics of the specimen during deformation. The mechanical curves completed by the temperature changes were applied to analyze the subsequent stages of the alloy loading. Elastic limit, recoverable strain, and development of the strain localization were studied. It was found that the maximal drop in temperature, which corresponds to the yield limit of solid materials, was referred to a significantly lower strain value in the case of Gum Metal in contrast to its large recoverable strain. The temperature increase proves a dissipative character of the process and is related to presence of ω and α″ phases induced during the alloy fabrication and their exothermic phase transformations activated under loading. During plastic deformation, both the strain and temperature distributions demonstrate that strain localization for higher strain rates starts nucleating just after the yield limit leading to specimen necking and rupture. Macroscopically, it is exhibited as softening of the stress-strain curve in contrast to the strain hardening observed at lower strain rates