Influence of concentration and pH of hexafluorozirconic acid on corrosion resistance of anodized AA7075-T6

7XXX aluminum alloys show high mechanical resistance and low weight, both required properties for aircraft industry. Anodizing is an electrolytical process typically used to improve the corrosion resistance of aluminum alloys, through which a thicker and porous oxide is formed. Boiling water is used as a common sealing method to the anodic layer; however, it implies energy expenditure. In this work, a two-step coating system was performed: anodizing in tartaric-sulphuric acid and a post-treatment with a Zr-based conversion coating, obtained at room temperature by immersion in hexafluorozirconic acid (H2 ZrF6 ). To establish the best condition for coating formation on the aluminum oxide layer, different concentration and pH values of the H2 ZrF6 solution were studied. Morphological and chemical analyses were performed respectively by SEM and EDS. The corrosion resistance evaluation was carried out by EIS in 0.5 M NaCl. Heterogeneity was observed in the obtained coatings. However, the samples treated with H2 ZrF6 had a higher corrosion resistance than unsealed samples. The best concentration and pH range observed for the H2 ZrF6 solution were 1 % and 3 to 3.5, respectively. Under these conditions, a greater corrosion resistance was evidenced in comparison to that obtained with boiling water sealing

RESISTÊNCIA A CORROSÃO EM DIFERENTES TRATAMENTOS DE SUPERFÍCIE SOBRE LIGAS DE ZINCO UTILIZADOS EM METAIS SANITÁRIOS

Entre as ligas não ferrosas, as ligas de zamac são as mais utilizadas para a fundição e vêm sendo aplicadas na substituição de peças de latão, utilizadas industrialmente em metais sanitários. O zamac apresenta propriedades mecânicas semelhantes às do latão, porém com custo inferior. Entretanto, a alta porosidade destas ligas, impede que tratamentos superficiais garantam bom acabamento e resistência à corrosão. Visando melhorar o desempenho, frente à corrosão de peças de zamac, o objetivo do presente trabalho é avaliar o processo de diferentes tratamentos de superfície dos metais sanitários produzidos em zamac. As amostras foram injetadas sobre pressão e submetidas a diferentes tratamentos superficiais (tratamento mecânico, tratamento químico, cobre alcalino, cobre ácido, níquel, cromo). Os corpos de prova foram expostos a um meio agressivo, por meio de nevoa salina a fim de analisar a resistência à corrosão das peças, além de análises de polarização, metalografia e microdureza. Observou-se que a maior incidência de corrosão ocorreu nas partes de injeção e solda da peça, as amostras tratadas com níquel e cromo demonstraram o melhor desemprenho frente a resistência a corrosão.Palavras-chave: Zamac. Metais sanitários. Corrosão.ABSTRACTAmong the non ferrous alloys, zamak are the most used for casting and have been applied to substitute brass parts, industrially utilized in sanitary metals. The zamak presents mechanical properties similar to brass, however with lower cost. Meanwhile, the high porosity of these alloys hinders the superficial treatments ensure good finishing and corrosion resistance. Aiming to improve the performance against corrosion of zamak parts, this work evaluates the process of different superficial treatments of sanitary metals produced with zamak. The samples were injected under pressure and submitted to different superficial treatments (mechanical, chemical, alkaline copper, acid copper, nickel and chromium). The specimens were exposed to an aggressive medium through salt spray test to evaluate the corrosion resistance, and the following analysis: polarization, metallography and microhardness. It was observed that the higher corrosion incidence occurred on the injection and weld regions. The samples treated with nickel and chromium demonstrated better performance of corrosion resistance. Keywords: Zamak. Sanitary materials. Corrosion

INFLUÊNCIA DOS PARÂMETROS DE ELETRODEPOSIÇÃO DE COBRE E NÍQUEL SOBRE O ZAMAC

A camada de cobre alcalino confere proteção ao zamac nos processos químicos posteriores, enquanto que a camada de cobre ácido confere nivelamento bem como a camada de níquel que confere brilho e proteção à peça. Neste sentido, esse trabalho tem por objetivo avaliar a influência dos parâmetros do processo de eletrodeposição das camadas de cobre e níquel na resistência à corrosão do zamac 5. Para tanto, camadas de cobre foram eletrodepositadas em amostras de zamac, com aplicação de 2V por 30 minutos e de 1V por 5 minutos + 2V por 40 minutos. Em cima desses depósitos, camadas de cobre ácido foram eletrodepositadas com aplicação de 2V por 30 minutos. Por último, sobre as camadas de cobre foram eletrodepositadas camadas de níquel com aplicação de 4V por 8 minutos e 4V por 20 minutos. O zamac sem e com revestimentos foi avaliado por Microscopia Eletrônica de Varredura (MEV), e quanto ao desempenho corrosivo por testes eletroquímicos (polarização). Os resultados mostraram que a diferença de tensão aplicada na eletrodeposição (1V e 2V) e o aumento de tempo (5min. e 40 min.), possibilitaram a obtenção de uma camada de cobre alcalino mais homogênea e uniforme e consequentemente mais resistente à corrosão do zamac em relação à camada de cobre alcalino com voltagem e tempo constante (2V por 30 min.). Palavras-chave: Corrosão. Eletrodeposição. Zamac. Cobre. Cristais. Porosidade.ABSTRACTThe alkaline copper layer provides zamac protection for subsequent chemical processes, while the acidic copper layer imparts leveling and the nickel layer imparts luster and protection to the part. In this sense, this work has the objective of evaluating the influence of the parameters of the electrodeposition process of copper and nickel layers on the resistance to the corrosion of zamac 5. For this, copper layers were electrodeposited in zamac samples, applying 2V by 30 minutes and 1V for 5 minutes + 2V for 40 minutes. On top of these deposits, layers of acid copper were electrodeposited with 2V application for 30 minutes. Finally, on the copper layers were electrodeposited layers of nickel with application of 4V for 8 minutes and 4V for 20 minutes. Zamac without and with coatings was evaluated by Scanning Electron Microscopy (SEM), and for the corrosive performance by electrochemical tests (polarization). The results showed that the voltage difference applied in the electrodeposition (1V and 2V) and the increase of time (5min and 40min) allowed to obtain a more homogeneous and uniform alkaline copper layer and consequently more corrosion resistant zamac in relation to the alkaline copper layer with voltage and constant time (2V for 30 min.).Keywords: Corrosion. Electrodeposition. Zamac. Copper. Crystals. Porosity

RESPOSTAS COMPORTAMENTAIS E ESTRATÉGIAS DE ENFRENTAMENTO DE IDOSOS NO TRATAMENTO DA INSUFICIÊNCIA CARDÍACA

Objetivo: conhecer as respostas comportamentais e as estratégias de enfrentamento de idosos no tratamento da insuficiência cardíaca. Método: estudo qualitativo, descritivo, fundamentado no referencial teórico de Callista Roy. Foram entrevistados 10 idosos acompanhados em um ambulatório de cardiologia em junho de 2015. Resultados: na categoria respostas comportamentais dos idosos frente ao tratamento, encontrou-se problemas adaptáveis nos modos fisiológicos (oxigenação, atividade/repouso e nutrição), de autoconceito (desmotivação, tristeza, solidão e medo), de desempenho de papéis (perda do papel primário de pai, trabalhador) e de interdependência (apoio familiar e dos pares). Todavia, apresentaram alguns mecanismos de adaptação, como uso de lembretes ou caixa organizadora para as medicações, redução de alimentos industrializados e diminuição de sódio nos alimentos, redução de custos com o cadastro em farmácias populares. Conclusão: os idosos, apesar de criarem alguns mecanismos de adaptação, ainda demonstraram falhas na condução do tratamento da insuficiência cardíaca, principalmente em relação à dieta e ao uso de medicamentos. Descritores: Idoso. Adaptação. Insuficiência Cardíaca. Assistência Integral a Saúde. Comportamento e Mecanismos Comportamentais

Cement matrix containing lightweight aggregate based on Non-Metallic Fraction Printed Circuit Boards (NMFPCB'S)

Materials such as river sand, used in construction, have a high demand, and thus generate great environmental impacts while being extracted, such as erosion of the rivers banks and your siltation. With the increasing restriction of river sand extraction which can generate a reduction in the product's offer in the civil construction sector, it is necessary to develop waste recycling technologies for the production of sands with less environmental impact. One of the alternatives for the production of mortar for construction is the replacement of sands extracted from rivers by waste from other industries, such as the electronics industry that presents large and growing production worldwide, due to technological advances. Thus, this work aims to evaluate the influence of partial replacement of quartz sand by lightweight aggregate based non-metallic fraction of printed circuit boards (NMFPCB's) on the properties of cementitious matrix in the fresh and hardened states. For this, the electronic components of the printed circuit boards (PCBs) were removed, they were grinded and then through magnetic and electrostatic separation processes to separate the most valuable and abundant part of metals. The water to cement ratio was 0.48 in all the experiments, the Portland cement to sand ratio was 1:3 (in mass) for the control, and the mortars with NMFPCB's replacement of sand by volume of 25% and 50% were also made. These were characterized mechanically by axial compressive strength test at different ages. The partial results showed that with the increase of sand substitution by NMFPCB's there was a reduction of the mortar consistency index in the fresh state. Results showed that matrix that suffered the substitution of sand by light aggregate, decreased the compressive strength in relation to the reference, but have potential to use in construction industry as blocks or non-structural elements

Can contaminated waters or wastewater be alternative sources for technology-critical elements? The case of removal and recovery of lanthanides

Technology critical elements (TCE) are considered the vitamins of nowadays technology. Factors such as high demand, limited sources and geopolitical pressures, mining exploitation and its negative impact, point these elements as new emerging contaminants and highlight the importance for removal and recycling TCE from contaminated waters. This paper reports the synthesis, characterization and application of hybrid nanostructures to remove and recover lanthanides from water, promoting the recycling of these high value elements. The nanocomposite combines the interesting properties of graphite nanoplatelets, with the magnetic properties of magnetite, and exhibits good sorption properties towards La(III), Eu(III) and Tb(III). The sorption process was very sensitive to solution pH, evidencing that electrostatic interactions are the main binding mechanism involved. Removal efficiencies up to 80% were achieved at pH 8, using only 50 mg/L of nanocomposite. In ternary solution, occurred a preferential removal of Eu(III) and Tb(III). The equilibrium evidenced a rare but interesting behaviour, and as a proof-of-concept the recoveries and reutilization rates, at consecutive cycles, highlight the recyclability of the composite without loss of efficiency. This study evidences that surface charge and the number of active sites of the composite controls the removal process, providing new insights on the interactions between lanthanoids and magnetic-graphite-nanoplatelets.publishe

Novas ocorrências de cladóceros em ambientes aquáticos do Brasil Central: compreendendo a biodiversidade

As águas superficiais do domí­nio Cerrado do Brasil central abrigam elevada biodiversidade e endemismo. Esta revisão teve como objetivo realizar um levantamento de novas ocorrências de Cladocera nestas águas e verificar tendências atuais do tema. A pesquisa foi realizada por meio de busca em literatura (2008-2018). Houve registro de 26 novas ocorrências, com a maioria exclusiva a determinada área. Chydoridae foi dominante nestes registros, o que reflete a heterogeneidade ambiental nos ecossistemas aquáticos do Cerrado e o papel funcional desta famí­lia. Estudos taxonômicos foram indispensáveis para a obtenção de resultados mais acurados em biodiversidade e análise ecológica de Cladocera. Com base na potencialidade destes novos registros serem indicadores de áreas pristinas e endêmicas, esta revisão permite reconhecer a distribuição do grupo e também contribuiu para reduzir lacunas de amostragem. A partir destes registros nestas áreas, subsí­dios são gerados para proteção mais efetiva de mananciais em áreas de divisores de bacias e mais vulneráveis a alterações antrópicas no Cerrado do Brasil Central