Clustering of vacancy defects in high-purity semi-insulating SiC
Positron lifetime spectroscopy was used to study native vacancy defects in
semi-insulating silicon carbide. The material is shown to contain (i) vacancy
clusters consisting of 4--5 missing atoms and (ii) Si vacancy related
negatively charged defects. The total open volume bound to the clusters
anticorrelates with the electrical resistivity both in as-grown and annealed
material. Our results suggest that Si vacancy related complexes compensate
electrically the as-grown material, but migrate to increase the size of the
clusters during annealing, leading to loss of resistivity.Comment: 8 pages, 5 figure
Investigation of the chemical vicinity of crystal defects in ion-irradiated Mg and AZ31 with coincident Doppler broadening spectroscopy
Crystal defects in magnesium and magnesium based alloys like AZ31 are of
major importance for the understanding of their macroscopic properties. We have
investigated defects and their chemical surrounding in Mg and AZ31 on an atomic
scale with Doppler broadening spectroscopy of the positron annihilation
radiation. In these Doppler spectra the chemical information and the defect
contribution have to be thoroughly separated. For this reason samples of
annealed Mg were irradiated with Mg-ions in order to create exclusively
defects. In addition Al- and Zn-ion irradiation on Mg-samples was performed in
order to create samples with defects and impurity atoms. The ion irradiated
area on the samples was investigated with laterally and depth resolved positron
Doppler broadening spectroscopy (DBS) and compared with preceding
SRIM-simulations of the vacancy distribution, which are in excellent agreement.
The investigation of the chemical vicinity of crystal defects in AZ31 was
performed with coincident Doppler broadening spectroscopy (CDBS) by comparing
Mg-ion irradiated AZ31 with Mg-ion irradiated Mg. No formation of
solute-vacancy complexes was found due to the ion irradiation, despite the high
defect mobility.Comment: Submitted to Physical Review B on March 20 20076. Revised version
submitted on September 28 2007. Accepted on October 19 200
Defect identification in GaAs grown at low temperatures by positron annihilation
We use positron annihilation to study vacancy defects in GaAs grown at low temperatures (LT-GaAs). The vacancies in as-grown LT-GaAs can be identified to be Ga monovacancies, V-Ga, according to their positron lifetime and annihilation momentum distribution. The charge state of the vacancies is neutral. This is ascribed to the presence of positively charged As-Ga(+) antisite defects in vicinity to the vacancies. Theoretical calculations of the annihilation parameters show that this assignment is consistent with the data. The density of V-Ga is related to the growth stoichiometry in LT-GaAs, i.e., it increases with the As/Ga beam equivalent pressure (BEP) and saturates at 2x10(18) cm(-3) for a BEP greater than or equal to 20 and a low growth temperature of 200 degrees C. Annealing at 600 degrees C removes V-Ga. Instead, larger vacancy agglomerates with a size of approximately four vacancies are found. It will be shown that these vacancy clusters are associated with the As precipitates formed during annealing. (C) 2000 American Institute of Physics. [S0021- 8979(00)02812-7]