In situ generation of Ag nanoparticles on polyester fabrics by photoreduction using TiO2 nanoparticles

This study discusses the possibility of in situ generation of Ag nanoparticles on polyester fabric by photoreduction of Ag+ ions with deposited TiO2 nanoparticles in the presence of amino acid alanine and methyl alcohol. The presence of TiO2/Ag nanoparticles on the polyester fiber surface was confirmed by XRD, XPS, and SEM analyses. Such nanocomposite textile material provides excellent antimicrobial activity against Gram-negative bacterium E. coli, Gram-positive bacterium S. aureus, and fungus C. albicans. Maximum microbial reduction was preserved even after ten washing cycles. In spite of satisfactory laundering durability, the release of silver occurred during washing. The leaching of silver was also present when the fabrics were exposed to artificial sweat at pH 5.5 and pH 8.0 for 24 h. In addition to excellent antimicrobial properties, TiO2/Ag nanoparticles imparted maximum UV protection to polyester fabrics

In situ photoreduction of Ag+-ions by TiO2 nanoparticles deposited on cotton and cotton/PET fabrics

The possibility of in situ photoreduction of Ag+-ions using TiO2 nanoparticles deposited on cotton and cotton/PET fabrics in the presence of amino acid alanine and methyl alcohol has been discussed. The possible interaction between TiO2, alanine and Ag+-ions was evaluated by FTIR analysis. The fabrication of TiO2/Ag nanoparticles on both fabrics was confirmed by SEM, EDX, XRD, XPS and AAS analyses. Cotton and cotton/PET fabrics impregnated with TiO2/Ag nanoparticles provided maximum reduction of Gram-negative bacteria Escherichia coli and Gram-positive bacteria Staphylococcus aureus. Although excellent antibacterial activity was preserved after ten washing cycles, a significant amount of silver leached out from the fabrics into the washing bath. The perspiration fastness assessment revealed that smaller amounts of silver were also released from the fabrics into artificial sweat at pH 5.50 and 8.00. In addition, deposited TiO2/Ag nanoparticles imparted maximum UV protection to fabrics