11 research outputs found
Ion release from a composite resin after exposure to different 10% carbamide peroxide bleaching agents
OBJECTIVE: This in vitro study evaluated the influence of two 10% carbamide peroxide bleaching agents - a commercial product (Opalescence PF; Ultradent Products, Inc.) and a bleaching agent prepared in a compounding pharmacy - on the chemical degradation of a light-activated composite resin by determining its release of ions before and after exposure to the agents. MATERIAL AND METHODS: Thirty composite resin (Filtek Z250; 3M/ESPE) samples were divided into three groups: group I (exposed to Opalescence PF commercial bleaching agent), group II (exposed to a compounded bleaching agent) and group III (control - Milli-Q water). After 14 days of exposure, with a protocol of 8 h of daily exposure to the bleaching agents and 16 h of immersion in Milli-Q water, the analysis of ion release was carried out using a HP 8453 spectrophotometer. The values were analyzed statistically by ANOVA, Tukey's test and the paired t-tests. The significance level was set at 5%. RESULTS: After 14 days of the experiment, statistically significant difference was found between group II and groups I and III, with greater ion release from the composite resin in group II. CONCLUSIONS: The compounded bleaching agent had a more aggressive effect on the composite resin after 14 days of exposure than the commercial product and the control (no bleaching)
Intensidade de fluorescência em resina composta: influência do polimento superficial e dos meios de armazenagem
INTRODUÇÃO: A resina composta é um material versátil em Odontologia Estética, principalmente por suas propriedades ópticas, dentre as quais a fluorescência. Poucos são os estudos que avaliaram esta propriedade e a comparação dos resultados encontrados torna-se difícil em função da inexistência de padronização nas metodologias na confecção e na armazenagem dos corpos de prova. OBJETIVO: Verificar a influência do polimento superficial e do meio de armazenagem, em estudos in vitro, em que se avalia a propriedade óptica de fluorescência em resinas compostas. MATERIAL E MÉTODO: Foram preparados 70 corpos de prova circulares (10 mm × 2 mm ) com resina composta microhíbrida (Opallis,- A2E - FGM.) Os meios de armazenagem foram: água deionizada, água da torneira e saliva artificial. Os protocolos de polimento superficial, realizados em politriz após a obtenção dos corpos de prova, utilizaram lixas de granulações 600, 1200 e 2500. Os valores de intensidade de fluorescência foram avaliados através do espectrofotômetro Cary Eclipse, após 1, 7 e 21 dias. RESULTADO: Não houve diferença estatisticamente significativa na Intensidade de Fluorescência entre os grupos submetidos aos diferentes protocolos de polimento. Quanto aos meios de armazenagem, a partir do sétimo dia, a variação de fluorescência foi significativamente maior em água da torneira e deionizada, quando comparada à variação observada em saliva artificial, resultado que se manteve após 21 dias. CONCLUSÃO: O protocolo de polimento superficial não promoveu alterações significativas na fluorescência da resina composta avaliada. Quanto ao meio de armazenagem, a intensidade de fluorescência foi menos afetada quando em saliva artificial
AVALIAÇÃO DO PH DE REFRIGERANTES DO TIPO NORMAL E LIGHT
O objetivo foi determinar o pH de refrigerantes e comparar os valores do grupo normal com os valores do grupo light. Para a comparação foi realizada a medição do pH dos refrigerantes através de um pHmetro calibrado. Cada líquido teve seu pH medido 05 vezes consecutivas com um intervalo de três minutos entre cada medição, os valores encontrados foram submetidos à análise estatística. Os valores encontrados foram: Coca-cola pH= 1,78, Coca-cola Light pH= 2,36, Guaraná Kuat pH= 1,82, guaraná Kuat Light pH= 1,87, Sprite pH= 1,92, Sprite Zero pH= 1,86, Fanta Laranja pH= 2,22, Fanta laranja light pH=2,62. A Coca-cola, guaraná, Sprite, Sprite zero e guaraná light apresentaram maior potencial erosivo, Coca-cola light e Fanta laranja light apresentaram menor potencial erosivo e Fanta laranja apresentou potencial erosivo intermediário. Dentro da amostra a coca - cola e a fanta laranja apresentaram maior potenci al erosivo do que seus correspondentes light. Palavras-Chave: Erosão dentária, bebidas gasosas, esmalte dentári
Evaluation of the surface roughness of a nanofilled composite resin submitted to different smoothing and finishing techniques
Abstract Introduction: Controlling the surface smoothness characteristics of the composite resin when performing a direct restorative technique is one of the factors involved in achieving restorative success. Objective: The purpose of this study was to evaluate the surface roughness of a nanofilled composite resin submitted to different smoothing and finishing techniques. Material and method: Fifty test specimens were made with the Z350 XT composite resin (3M ESPE) and then divided into five study groups according to the smoothing and finishing method applied, as follows: G1 (control), polyester strip; G2, composite spatula; G3, brush cleaned with absolute alcohol and dried; G4, brush cleaned with absolute alcohol, dried and moistened with Single Bond (3M ESPE); and G5, brush cleaned with absolute alcohol, dried and moistened with Natural Glaze surface sealant (DFL). After fabrication, the specimens were stored for 24 h in deionized water. The surface roughness of the specimens was measured using a profilometer. Surface roughness means were compared by analysis of variance followed by Tukey’s test at a level of significance of 5%. Result: The lowest surface roughness was observed in G1 (control group) and the highest, in G3. G5 had lower surface roughness values compared to the other test groups, and presented values similar to those of the control group. Conclusion: The smoothing and finishing techniques influenced the surface roughness of the composite resin. Application of the surface sealant by the copolymerization technique resulted in lower roughness values. The use of a clean, dry brush promoted roughness values beyond the acceptable limit, and is therefore liable to compromise the performance of composite resin restorations
Evaluation of the surface roughness of a nanofilled composite resin submitted to different smoothing and finishing techniques
Abstract Introduction: Controlling the surface smoothness characteristics of the composite resin when performing a direct restorative technique is one of the factors involved in achieving restorative success. Objective: The purpose of this study was to evaluate the surface roughness of a nanofilled composite resin submitted to different smoothing and finishing techniques. Material and method: Fifty test specimens were made with the Z350 XT composite resin (3M ESPE) and then divided into five study groups according to the smoothing and finishing method applied, as follows: G1 (control), polyester strip; G2, composite spatula; G3, brush cleaned with absolute alcohol and dried; G4, brush cleaned with absolute alcohol, dried and moistened with Single Bond (3M ESPE); and G5, brush cleaned with absolute alcohol, dried and moistened with Natural Glaze surface sealant (DFL). After fabrication, the specimens were stored for 24 h in deionized water. The surface roughness of the specimens was measured using a profilometer. Surface roughness means were compared by analysis of variance followed by Tukey’s test at a level of significance of 5%. Result: The lowest surface roughness was observed in G1 (control group) and the highest, in G3. G5 had lower surface roughness values compared to the other test groups, and presented values similar to those of the control group. Conclusion: The smoothing and finishing techniques influenced the surface roughness of the composite resin. Application of the surface sealant by the copolymerization technique resulted in lower roughness values. The use of a clean, dry brush promoted roughness values beyond the acceptable limit, and is therefore liable to compromise the performance of composite resin restorations