1,216 research outputs found
Graphite formation in cast iron, phase 2
Several types of cast irons are directionally solidified aboard the KC-135 aircraft. Also, control samples are run on Earth for comparison. Some of these samples are unusable because of various mechanical problems; the analysis and the interpretation of results on the samples that are run successfully is discussed
Directional solidification of flake and nodular cast iron during KC-135 low-g maneuvers
Alloys solidified in a low-gravity environment can, due to the elimination of sedimentation and convection, form unique and often desirable microstructures. One method of studying the effects of low-gravity (low-g) on alloy solidification was the use of the NASA KC-135 aircraft flying repetitive low-g maneuvers. Each maneuver gives from 20 to 30 seconds of low-g which is between about 0.1 and 0.001 gravity. A directional solidification furnace was used to study the behavior of off eutectic composition case irons in a low-g environment. The solidification interface of hypereutectic flake and spheroidal graphite case irons was slowly advanced through a rod sample, 5 mm in diameter. Controlled solidification was continued through a number of aircraft parabolas. The known solidification rate of the sample was then correlated with accelerometer data to determine the gravity level during solidification for any location of the sample. The thermal gradient and solidification rate were controlled independently. Samples run on the KC-135 aircraft exhibited bands of coarser graphite or of larger nodules usually corresponding to the regions solidified under low-g. Samples containing high phosphorous (used in order to determine the eutectic cell) exhibited larger eutectic cells in the low-g zone, followed by a band of coarser graphite
Preliminary science report on the directional solidification of hypereutectic cast iron during KC-135 low-G maneuvers
An ADSS-P directional solidification furnace was reconfigured for operation on the KC-135 low-g aircraft. The system offers many advantages over quench ingot methods for study of the effects of sedimentation and convection on alloy formation. The directional sodification furnace system was first flown during the September 1982 series of flights. The microstructure of the hypereutectic cast iron sample solidified on one of these flights suggests a low-g effect on graphite morphology. Further experiments are needed to ascertain that this effect is due to low-gravity and to deduce which of the possible mechanisms is responsible for it
Strong, Long-Term Temporal Dynamics of an Ecological Network
Nature is organized into complex, dynamical networks of species and their interactions, which may influence diversity and stability. However, network research is, generally, short-term and depict ecological networks as static structures only, devoid of any dynamics. This hampers our understanding of how nature responds to larger disturbances such as changes in climate. In order to remedy this we studied the long-term (12-yrs) dynamics of a flower-visitation network, consisting of flower-visiting butterflies and their nectar plants. Global network properties, i.e. numbers of species and links, as well as connectance, were temporally stable, whereas most species and links showed a strong temporal dynamics. However, species of butterflies and plants varied bimodally in their temporal persistance: Sporadic species, being present only 1–2(-5) years, and stable species, being present (9-)11–12 years, dominated the networks. Temporal persistence and linkage level of species, i.e. number of links to other species, made up two groups of species: Specialists with a highly variable temporal persistence, and temporally stable species with a highly variable linkage level. Turnover of links of specialists was driven by species turnover, whereas turnover of links among generalists took place through rewiring, i.e. by reshuffling existing interactions. However, in spite of this strong internal dynamics of species and links the network appeared overall stable. If this global stability-local instability phenomenon is general, it is a most astonishing feature of ecological networks
Advancement of Solidification Processing Technology Through Real Time X-Ray Transmission Microscopy: Sample Preparation
Two types of samples were prepared for the real time X-ray transmission microscopy (XTM) characterization. In the first series directional solidification experiments were carried out to evaluate the critical velocity of engulfment of zirconia particles in the Al and Al-Ni eutectic matrix under ground (l-g) conditions. The particle distribution in the samples was recorded on video before and after the samples were directionally solidified. In the second series samples of the above two type of composites were prepared for directional solidification runs to be carried out on the Advanced Gradient Heating Facility (AGHF) aboard the space shuttle during the LMS mission in June 1996. X-ray microscopy proved to be an invaluable tool for characterizing the particle distribution in the metal matrix samples. This kind of analysis helped in determining accurately the critical velocity of engulfment of ceramic particles by the melt interface in the opaque metal matrix composites. The quality of the cast samples with respect to porosity and instrumented thermocouple sheath breakage or shift could be easily viewed and thus helped in selecting samples for the space shuttle experiments. Summarizing the merits of this technique it can be stated that this technique enabled the use of cast metal matrix composite samples since the particle location was known prior to the experiment
Ceramics for Molten Materials Containment, Transfer and Handling on the Lunar Surface
As part of a project on Molten Materials Transfer and Handling on the Lunar Surface, molten materials containment samples of various ceramics were tested to determine their performance in contact with a melt of lunar regolith simulant. The test temperature was 1600 C with contact times ranging from 0 to 12 hours. Regolith simulant was pressed into cylinders with the approximate dimensions of 1.25 dia x 1.25cm height and then melted on ceramic substrates. The regolith-ceramic interface was examined after processing to determine the melt/ceramic interaction. It was found that the molten regolith wetted all oxide ceramics tested extremely well which resulted in chemical reaction between the materials in each case. Alumina substrates were identified which withstood contact at the operating temperature of a molten regolith electrolysis cell (1600 C) for eight hours with little interaction or deformation. This represents an improvement over alumina grades currently in use and will provide a lifetime adequate for electrolysis experiments lasting 24 hours or more. Two types of non-oxide ceramics were also tested. It was found that they interacted to a limited degree with the melt resulting in little corrosion. These ceramics, Sic and BN, were not wetted as well as the oxides by the melt, and so remain possible materials for molten regolith handling. Tests wing longer holding periods and larger volumes of regolith are necessary to determine the ultimate performance of the tested ceramics
A 10B-based neutron detector with stacked Multiwire Proportional Counters and macrostructured cathodes
We present the results of the measurements of the detection efficiency for a
4.7 \r{A} neutron beam incident upon a detector incorporating a stack of up to
five MultiWire Proportional Counters (MWPC) with Boron-coated cathodes. The
cathodes were made of Aluminum and had a surface exhibiting millimeter-deep
V-shaped grooves of 45{\deg}, upon which the thin Boron film was deposited by
DC magnetron sputtering. The incident neutrons interacting with the converter
layer deposited on the sidewalls of the grooves have a higher capture
probability, owing to the larger effective absorption film thickness. This
leads to a higher overall detection efficiency for the grooved cathode when
compared to a cathode with a flat surface. Both the experimental results and
the predictions of the GEANT4 model suggests that a 5-counter detector stack
with coated grooved cathodes has the same efficiency as a 7-counter stack with
flat cathodes. The reduction in the number of counters in the stack without
altering the detection efficiency will prove highly beneficial for large-area
position-sensitive detectors for neutron scattering applications, for which the
cost-effective manufacturing of the detector and associated readout electronics
is an important objective. The proposed detector concept could be a
technological option for one of the new chopper spectrometers and other
instruments planned to be built at the future European Spallation Source in
Sweden. These results with macrostructured cathodes generally apply not just to
MWPCs but to other gaseous detectors as well.Comment: 14 pages, 9 figure
Experimental Performance of a Micromachined Heat Flux Sensor
Steady-state and frequency response calibration of a microfabricated heat-flux sensor have been completed. This sensor is batch fabricated using standard, micromachining techniques, allowing both miniaturization and the ability to create arrays of sensors and their corresponding interconnects. Both high-frequency and spatial response is desired, so the sensors are both thin and of small cross-sectional area. Thin-film, temperature-sensitive resistors are used as the active gauge elements. Two sensor configurations are investigated: (1) a Wheatstone-bridge using four resistors; and (2) a simple, two-resistor design. In each design, one resistor (or pair) is covered by a thin layer (5000 A) thermal barrier; the other resistor (or pair) is covered by a thick (5 microns) thermal barrier. The active area of a single resistor is 360 microns by 360 microns; the total gauge area is 1.5 mm square. The resistors are made of 2000 A-thick metal; and the entire gauge is fabricated on a 25 microns-thick flexible, polyimide substrate. Heat flux through the surface changes the temperature of the resistors and produces a corresponding change in resistance. Sensors were calibrated using two radiation heat sources: (1) a furnace for steady-state, and (2) a light and chopper for frequency response
Host specialization by Cotesia wasps (Hymenoptera: Braconidae) parasitizing species-rich Melitaeini (Lepidoptera: Nymphalidae) communities in north-eastern Spain
In order to investigate parasitoids of the genus Cotesia (Hymenoptera: Braconidae), larvae of a speciose group of butterflies, the tribe Melitaeini (Lepidoptera: Nymphalidae), were collected from several sites in Catalonia, northern Spain, a region that harbours ten out of the 20 European species of Melitaeini. New information on the natural history of the butterflies is presented, and the structure of their communities and patterns of larval parasitism are described. On the basis of mtDNA sequence data (COI gene), microsatellite data (ten loci) and behavioural experiments, we recognize seven biologically distinct species of Cotesia parasitizing the Melitaeini communities within this relatively small geographical area. In particular, the notional species C. melitaearum and C. acuminata each represents a series of cryptic species with narrow host associations. The possibility of direct competition among the parasitoids and/or indirect interactions between butterflies mediated by Cotesia parasitoids is explored
- …