Preparation, structural characterisation and antibacterial properties of Ga-doped sol-gel phosphate-based glass

A sol-gel preparation of Ga-doped phosphate-based glass with potential application in antimicrobial devices has been developed. Samples of composition (CaO)(0.30)(Na2O)(0.20-x) (Ga2O3) (x) (P2O5)(0.50) where x = 0 and 0.03 were prepared, and the structure and properties of the gallium-doped sample compared with those of the sample containing no gallium. Analysis of the P-31 MAS NMR data demonstrated that addition of gallium to the sol-gel reaction increases the connectivity of the phosphate network at the expense of hydroxyl groups. This premise is supported by the results of the elemental analysis, which showed that the gallium-free sample contains significantly more hydrogen and by FTIR spectroscopy, which revealed a higher concentration of -OH groups in that sample. Ga K-edge extended X-ray absorption fine structure and X-ray absorption near-edge structure data revealed that the gallium ions are coordinated by six oxygen atoms. In agreement with the X-ray absorption data, the high-energy XRD results also suggest that the Ga3+ ions are octahedrally coordinated with respect to oxygen. Antimicrobial studies demonstrated that the sample containing Ga3+ ions had significant activity against Staphylococcus aureus compared to the control

Mechanical Activation of Al-Oxyhydroxide Minerals – Physicochemical Changes, Reactivity and Relevance to Bayer Process

Overview of our research on ‘structure and reactivity’ of gibbsite and boehmite under varied conditions of mechanical activation, e.g. milling energy and presence of a second phase is presented. Bulk and surface changes induced in the solids by milling are characterized in terms of morphology, particle size distribution, specific surface area and nature of porosity, crystallite size and zeta potential. Results on enhanced amorphisation of gibbsite in presence of a second phase (quartz, hematite etc), changes in zeta potential of gibbsite due to loss of texture during milling and anomalous decrease in surface area of boehmite during milling are reported. Reactivity of the activated solids in sodium hydroxide and variation in thermal transformation temperatures is correlated with physicochemical characteristics of the samples and plausible explanation for the observed correlations presented. Significance of the results with specific reference to bauxite and alumina processing in Bayer process is highlighted

Characterization of supplementary cementitious materials by thermal analysis

Working Group 1 of RILEM TC 238-SCM ‘Hydration and microstructure of concrete with supplementary cementitious materials (SCMs)’ is defining best practices for the physical and chemical characterization of SCMs, and this paper focusses on their thermal analysis. Thermogravimetric analysis (TGA) can provide valuable data on the chemical and mineralogical composition of SCMs. Loss-on-ignition (LOI) testing is a commonly used, standardized, but less sophisticated version of TGA that measures mass at endpoints only, with heating generally in air. In this paper we describe the use of TGA and LOI to characterize Portland cement with limestone additions, coal combustion fly ashes, ground-granulated blast furnace slag, calcined clays, and natural pozzolans. This paper outlines the value and limitations of TGA and LOI (in the formats defined in different standards regimes) for material characterization, and describes testing methods and analysis. TGA testing parameters affect the mass loss recorded at temperatures relevant for LOI measurements (700–1000 °C) of slags and fly ashes, mainly associated with oxidation reactions taking place upon heating. TGA of clays and natural pozzolans is utilized to identify optimal calcination conditions leading to dehydroxylation and consequent structural amorphization, particularly for kaolinite. However, dehydroxylation and amorphization do not occur at similar temperatures for all clays, limiting the applicability of TGA for this purpose. Although TGA is widely utilized for characterization of SCMs, the testing parameters significantly affect the results obtained, and TGA results require careful interpretation. Therefore, standardization of TGA testing conditions, particularly for LOI determination of slags and fly ashes, is required