Influence of compositionally induced defects on the vibrational properties of device grade Cu2ZnSnSe4 absorbers for kesterite based solar cells
This work presents a detailed analysis of the impact of compositionally induced defects on the vibrational properties of Cu2ZnSnSe4 absorbers for kesterite based solar cells. Systematic changes in the intensity of the E and B modes located around the 170, 220, and 250 cm-1 frequency regions, which involve mostly cation vibrations, were observed and analyzed in relation to the occurrence of different kinds of defect clusters involving VCu, ZnCu, ZnSn, CuZn, and SnZn point defects. Additional changes are also interpreted in terms of the appearance of SnSe, ZnSe, and CuSe-like contributions at the 185 and 250 cm-1 spectral regions, respectively. The sensitivity of the Raman measurements to the presence of these kinds of defects corroborates the potential of Raman scattering for point defect assessment in these systems. © 2015 AIP Publishing LLCPeer ReviewedPostprint (published version
Influence of compositionally induced defects on the vibrational properties of device grade Cu2ZnSnSe4 absorbers for kesterite based solar cells
This work presents a detailed analysis of the impact of compositionally induced defects on the vibrational properties of Cu2ZnSnSe4 absorbers for kesterite based solar cells. Systematic changes in the intensity of the E and B modes located around the 170, 220, and 250 cm 1 frequency regions, which involve mostly cation vibrations, were observed and analyzed in relation to the occurrence of different kinds of defect clusters involving VCu, ZnCu, ZnSn, CuZn, and SnZn point defects. Additional changes are also interpreted in terms of the appearance of SnSe, ZnSe, and CuSe-like contributions at the 185 and 250 cm 1 spectral regions, respectively. The sensitivity of the Raman measurements to the presence of these kinds of defects corroborates the potential of Raman scattering for point defect assessment in these systems
Progress and perspectives of thin film kesterite photovoltaic technology: a critical review
The latest progress and future perspectives of thin film photovoltaic kesterite technology are reviewed herein. Kesterite is currently the most promising emerging fully inorganic thin film photovoltaic technology based on critical raw-material-free and sustainable solutions. The positioning of kesterites in the frame of the emerging inorganic solar cells is first addressed, and the recent history of this family of materials briefly described. A review of the fast progress achieved earlier this decade is presented, toward the relative slowdown in the recent years partly explained by the large open circuit voltage (VOC) deficit recurrently observed even in the best solar cell devices in the literature. Then, through a comparison with the close cousin Cu(In,Ga)Se2 technology, doping and alloying strategies are proposed as critical for enhancing the conversion efficiency of kesterite. In the second section herein, intrinsic and extrinsic doping, as well as alloying strategies are reviewed, presenting the most relevant and recent results, and proposing possible pathways for future implementation. In the last section, a review on technological applications of kesterite is presented, going beyond conven tional photovoltaic devices, and demonstrating their suitability as potential candidates in advanced tandem concepts, photocatalysis, thermoelectric, gas sensing, etc
Resonant Raman scattering based approaches for the quantitative assessment of nanometric ZnMgO layers in high efficiency chalcogenide solar cells
This work reports a detailed resonant Raman scattering analysis of ZnMgO solid solution nanometric layers that are being developed for high efficiency chalcogenide solar cells. This includes layers with thicknesses below 100 nm and compositions corresponding to Zn/(Zn + Mg) content rations in the range between 0% and 30%. The vibrational characterization of the layers grown with different compositions and thicknesses has allowed deepening in the knowledge of the sensitivity of the different Raman spectral features on the characteristics of the layers, corroborating the viability of resonant Raman scattering based techniques for their non-destructive quantitative assessment. This has included a deeper analysis of different experimental approaches for the quantitative assessment of the layer thickness, based on (a) the analysis of the intensity of the ZnMgO main Raman peak; (b) the evaluation of the changes of the intensity of the main Raman peak from the subjacent layer located below the ZnMgO one; and (c) the study of the changes in the relative intensity of the first to second/third order ZnMgO peaks. In all these cases, the implications related to the presence of quantum confinement effects in the nanocrystalline layers grown with different thicknesses have been discussed and evaluated
Raman microprobe characterization of electrodeposited S-rich CuIn(S,Se)2 for photovoltaic applications: Microstructural analysis
This article reports a detailed Raman scattering and microstructural characterization of S-rich CuIn(S,Se)2 absorbers produced by electrodeposition of nanocrystalline CuInSe2 precursors and subsequent reactive annealing under sulfurizing conditions. Surface and in-depth resolved Raman microprobe measurements have been correlated with the analysis of the layers by optical and scanning electron microscopy, x-ray diffraction, and in-depth Auger electron spectroscopy. This has allowed corroboration of the high crystalline quality of the sulfurized layers. The sulfurizing conditions used also lead to the formation of a relatively thick MoS2 intermediate layer between the absorber and the Mo back contact. The analysis of the absorbers has also allowed identification of the presence of In-rich secondary phases, which are likely related to the coexistence in the electrodeposited precursors of ordered vacancy compound domains with the main chalcopyrite phase, in spite of the Cu-rich conditions used in the growth. This points out the higher complexity of the electrodeposition and sulfurization processes in relation to those based in vacuum deposition techniques
Vibrational properties of sulfoselenide solid solutions
In this work, Raman spectroscopy and X-ray diffraction were applied together
to evaluate the crystal structure and the phonon modes of photovoltaic grade
Cu 2ZnSn(SxSe1−x)4 thin films, leading to a complete characterization of their
structural and vibrational properties. Vibrational characterization has been
based on Raman scattering measurements performed with different excitation
wavelengths and polarization configurations. Analysis of the experimental
spectra has permitted identification of 19 peaks, which positions are in good
accord with theoretical predictions. Besides, the observation of Cu
2ZnSnS4-like A symmetry peaks related to S vibrations and Cu 2ZnSnSe4-like A
symmetry peaks related to Se vibrations, additional Raman peaks,
characteristic of the solid solution and previously not reported, are
observed, and are attributed to vibrations involving both S and Se anions
Polarized Raman scattering study of kesterite type Cu2ZnSnS4 single crystals
A non-destructive Raman spectroscopy has been widely used as a complimentary method to X-ray diffraction characterization of Cu2ZnSnS4 (CZTS) thin films, yet our knowledge of the Raman active fundamental modes in this material is far from complete. Focusing on polarized Raman spectroscopy provides important information about the relationship between Raman modes and CZTS crystal structure. In this framework the zone-center optical phonons of CZTS, which is most usually examined in active layers of the CZTS based solar cells, are studied by polarized resonant and non-resonant Raman spectroscopy in the range from 60 to 500 cm(-1) on an oriented single crystal. The phonon mode symmetry of 20 modes from the 27 possible vibrational modes of the kesterite structure is experimentally determined. From in-plane angular dependences of the phonon modes intensities Raman tensor elements are also derived. Whereas a strong intensity enhancement of the polar E and B symmetry modes is induced under resonance conditions, no mode intensity dependence on the incident and scattered light polarization configurations was found in these conditions. Finally, Lyddane-Sachs-Teller relations are applied to estimate the ratios of the static to high-frequency optic dielectric constants parallel and perpendicular to c-optical axis
Chemical bath deposition route for the synthesis of ultra-thin CuIn(S,Se)2 based solar cells.
CuIn(S,Se)2 (CISSe) photovoltaic grade thin films are usually grown by expensive vacuum based methods or chemical routes that require highly toxic precursors. In this work, we present the synthesis of CISSe absorbers by a simple chemical bath deposition (CBD) route. In the first step, In2S3/Cu2 − xS stack was deposited as a precursor by CBD on Mo-coated soda lime glass substrates, using respectively thioacetamide and N,N′ dimethylthiourea as S source. Then the CISSe thin films were synthesized by the precursor's selenization at 450 °C. The obtained films were characterized by X-ray diffraction (XRD), Raman spectroscopy and scanning electron microscopy (SEM). The tetragonal chalcopyrite structure of CISSe was identified by XRD and Raman, confirming that the major part of S was replaced by Se. SEM images show a compact and homogeneous film and by cross-section the thickness was estimated to be around 700 nm. Solar cells prepared with these absorbers exhibit an open circuit voltage of 369 mV, a short circuit current density of 13.7 mA/cm2 , a fill factor of 45% and an efficiency of 2.3%
Point defects, compositional fluctuations, and secondary phases in non-stoichiometric kesterites
The efficiency of kesterite-based solar cells is limited by various non-ideal recombination paths, amongst others by a high density of defect states and by the presence of binary or ternary secondary phases within the absorber layer. Pronounced compositional variations and secondary phase segregation are indeed typical features of non-stoichiometric kesterite materials. Certainly kesterite-based thin film solar cells with an off-stoichiometric absorber layer composition, especially Cu-poor/Zn-rich, achieved the highest efficiencies, but deviations from the stoichiometric composition lead to the formation of intrinsic point defects (vacancies, anti-sites, and interstitials) in the kesterite-type material. In addition, a non-stoichiometric composition is usually associated with the formation of an undesirable side phase (secondary phases). Thus the correlation between off-stoichiometry and intrinsic point defects as well as the identification and quantification of secondary phases and compositional fluctuations in non-stoichiometric kesterite materials is of great importance for the understanding and rational design of solar cell devices. This paper summarizes the latest achievements in the investigation of identification and quantification of intrinsic point defects, compositional fluctuations, and secondary phases in non-stoichiometric kesterite-type materials
- …