Thermal expansion of graphite-epoxy between 116 K and 366 K

A Priest laser interferometer was developed to measure the thermal strain of composite laminates. The salient features of this interferometer are that: (1) it operates between 116 K and 366 K; (2) it is easy to operate; (3) minimum specimen preparation is required; (4) coefficients of thermal expansion in the range of 0-5 micro epsilon/K can be measured; and (5) the resolution of thermal strain is on the order of micro epsilon. The thermal response of quasi-isotropic, T300/5208, grahite-epoxy composite material was studied with this interferometer. The study showed that: (1) for the material tested, thermal cycling effects are negligible; (2) variability of thermal response from specimen to specimen may become significant at cryogenic temperatures; and (3) the thermal response of 0.6 cm and 2.5 cm wide specimens are the same above room temperature

Development of a Priest interferometer for measurement of the thermal expansion of a graphite epoxy in the temperature range 116-366 K

The thermal expansion behavior of graphite epoxy laminates between 116 and 366 degrees Kelvin was investigated using as implementation of the Priest interferometer concept. The design, construction and use of the interferometer along with the experimental results it was used to generate are described. The experimental program consisted of 25 tests on 25.4 mm and 6.35 mm wide, 8 ply pi/4 quasi-isotropic T300-5208 graphite/epoxy specimens and 3 tests on a 25.4 mm wide unidirectional specimen. Experimental results are presented for all tests along with a discussion of the interferometer's limitations and some possible improvements in its design

Child Psychosocial Adjustment and Parenting in Families Affected by Maternal HIV/AIDS

Child adjustment and parenting were examined in 23 9-through 16-year-old youth from families affected by maternal HIV infection and 20 same-age peers whose mothers were not infected. Children whose mothers were seropositive reported significantly more externalizing problems. Infected mothers reported less age-appropriate supervision/monitoring relative to non-infected mothers. Better mother-child relationship quality and less impairment in parental supervision/monitoring of age-appropriate youth behaviors were associated with fewer externalizing difficulties among the HIV-positive group only. Similarly, only among HIV-infected mothers was refraining from engaging in inconsistent disciplinary tactics associated with lower reports of internalizing and externalizing problems. These data highlight the promise of programs targeting parenting skills to prevent or ameliorate child difficulties

Mineralogy of the Mafic Anomaly in the South Pole-Aitken Basin: Implications for excavation of the lunar mantle

Mineralogy of South Pole-Aitken Basin (SPA) (the largest confirmed impact basin on the Moon) is evaluated using five-color images from Clementine. Although olivine-rich material as well as basalts rich in clinopyroxene are readily identified elsewhere on the farside, the dominant rock type observed across the interior of SPA is of a very noritic composition. This mineralogy suggests that lower crust rather than the mantle is the dominant source of the mafic component at SPA. The lack of variation in observed noritic composition is probably due to basin formation processes, during which extensive melting and mixing of target materials are likely to occur

Disclosure of Maternal HIV Status to Children: To Tell or Not To Tell . . . That Is the Question

HIV-infected mothers face the challenging decision of whether to disclose their serostatus to their children. From the perspective of both mother and child, we explored the process of disclosure, providing descriptive information and examining the relationships among disclosure, demographic variables, and child adjustment. Participants were 23 mothers and one of their noninfected children (9 to 16 years of age). Sixty-one percent of mothers disclosed. Consistent with previous research, disclosure was not related to child functioning. However, children sworn to secrecy demonstrated lower social competence and more externalizing problems. Differential disclosure, which occurred in one-third of the families, was associated with higher levels of depressive and anxiety symptoms. Finally, knowing more than mothers had themselves disclosed was related to child maladjustment across multiple domains. Clinical implications and the need for future research are considered

Development and geometry of isotropic and directional shrinkage crack patterns

We have studied shrinkage crack patterns which form when a thin layer of an alumina/water slurry dries. Both isotropic and directional drying were studied. The dynamics of the pattern formation process and the geometric properties of the isotropic crack patterns are similar to what is expected from recent models, assuming weak disorder. There is some evidence for a gradual increase in disorder as the drying layer become thinner, but no sudden transition, in contrast to what has been seen in previous experiments. The morphology of the crack patterns is influenced by drying gradients and front propagation effects, with sharp gradients having a strong orienting and ordering effect.Comment: 8 pages, 11 figures, 8 in jpg format, 3 in postscript. See also http://mobydick.physics.utoronto.ca/mud.htm

On the true optical properties of zinc nitride

Copyright (2011) American Institute of Physics. The following article appeared in Applied Physics Letters 99.23 (2011): 232112-3 and may be found at http://apl.aip.org