Flight service evaluation of advanced composite ailerons on the L-1011 transport aircraft

This report covers flight evaluation of composite inboard ailerons on the L-1011 under Contract NAS 1-15069 for a period of five years. This is the fourth annual report of the maintenance evaluation program, and covers the period from May 1985 when the third yearly inspections were completed, through July 1986. Four shipsets of graphite/epoxy composite inboard ailerons were installed on L-1011 aircraft for this maintenance evaluation program. These include two Delta aircraft and two TWA aircraft. A fifth shipset of composite ailerons was installed in 1980 on Lockheed's flight test L-1011. One instance of minor damage was observed on one of the composite ailerons and was repaired. No other maintenance actions have occurred on any of the composite parts except for repainting of areas with paint loss. Flight hours on the airline components at the time of inspection ranged from 12,051]en1] to 14,046 hours, after approximately 4 years of service

On the effects of flight on jet engine exhaust noise

Differences between flight data and predictions of jet engine exhaust noise were reconciled by considering the combined effects of jet mixing noise and internally generated engine exhaust noise. The source strength of the internally generated noise was assumed to be unaffected by flight, as experiments demonstrated. The directivity of the internally generated noise was assumed to be the same statically as that given in the NASA interim prediction method for core engine noise. However, it was assumed that in flight internally generated noise is subject to the convective amplification effect of a simple source. The absolute levels of internally generated noise were obtained from an empirical fit of some typical engine data. The static and flight jet noise were predicted using the above prediction method. It was shown that in many cases much of the flyover noise signature is dominated by internally generated noise

An empirical model for inverted-velocity-profile jet noise prediction

An empirical model for predicting the noise from inverted-velocity-profile coaxial or coannular jets is presented and compared with small-scale static and simulated flight data. The model considered the combined contributions of as many as four uncorrelated constituent sources: the premerged-jet/ambient mixing region, the merged-jet/ambient mixing region, outer-stream shock/turbulence interaction, and inner-stream shock/turbulence interaction. The noise from the merged region occurs at relatively low frequency and is modeled as the contribution of a circular jet at merged conditions and total exhaust area, with the high frequencies attenuated. The noise from the premerged region occurs at high frequency and is modeled as the contribution of an equivalent plug nozzle at outer stream conditions, with the low frequencies attenuated

Development of graphite/polyimide honeycomb core materials

Honeycomb panel constructions consisting entirely of graphite/polyimide composites were developed and evaluated. Graphite/polyimide composites, were used in the honeycomb core webs and in pre-cured sandwich skins. Polyimide adhesives were also developed and evaluated for use in skin-core bonding. The purpose of this program was to develop light weight sandwich constructions for high temperature applications which could provide comparable shear strength and stiffness to metallic honeycomb constructions

Flight service evaluation of Kevlar-49 epoxy composite panels in wide-bodies commercial transport aircraft

Kevlar-49 fairing panels, installed as flight service components on three L-1011s, were inspected after 9 years of service. There are six Kevlar-49 panels on each aircraft: a left hand and right hand set of a wing body sandwich fairing; a solid laminate under wing fillet panel; and a 422 K (300 F) service aft engine fairing. The fairings have accumulated a total of 70,000 hours, with one ship set having over 24,000 hours service. The Kevlar-49 components were found to be performing satisfactorily in service with no major problems, or any condition requiring corrective action. The only defects noted were minor impact damage, a few minor disbonds and a minor degree of fastener hole fraying and elongation. These are for the most part comparable to damage noted on fiberglass fairings. The service history to date indicates that Kevlar-49 epoxy composite materials have satisfactory service characteristics for use in aircraft secondary structure

Flight service evaluation of Kevlar-49/epoxy composite panels in wide-bodied commercial transport aircraft

Kevlar-49 fairing panels, installed as flight service components on three L-1011s, were inspected after three years' service, and found to be performing satisfactorily. There are six Kevlar-49 panels on each aircraft, including sandwich and solid laminate wing-body panels, and 150 C service aft engine fairings. The service history to date indicates that Kevlar-49 epoxy composite materials have satisfactory service characteristics for use in aircraft secondary structure