Chemical, morphological and functional properties of Brazilian jackfruit (Artocarpus heterophyllus L.) seeds starch

AbstractStarches used in food industry are extracted from roots, tubers and cereals. Seeds of jackfruit are abundant and contain high amounts of starch. They are discarded during the fruit processing or consumption and can be an alternative source of starch. The starch was extract from the jackfruit seeds and characterised to chemical, morphological and functional properties. Soft and hard jackfruit seeds showed starch content of 92.8% and 94.5%, respectively. Starch granules showed round and bell shape and some irregular cuts on their surface with type-A crystallinity pattern, similar to cereals starches. The swelling power and solubility of jackfruit starch increased with increasing temperature, showing opaque pastes. The soft seeds starch showed initial and final gelatinisation temperature of 36°C and 56°C, respectively; while hard seeds starch presented initial gelatinisation at 40°C and final at 61°C. These results suggest that the Brazilian jackfruit seeds starches could be used in food products

EFEITO DA MODIFICAÇÃO QUÍMICA POR REAÇÃO DE CROSS-LINKING NAS PROPRIEDADES DO AMIDO DE SEMENTE DE ABACATE (Persea americana Mill)

O objetivo deste trabalho foi obter informações a respeito das propriedades do amido da semente de abacate cv. “Manteiga” e submetê-lo à modificação química por cross-linking, visando obter características reológicas aplicáveis à elaboração de produtos alimentícios. O amido nativo extraído das sementes apresentou teor de amido de 74,47 % e rendimento para o processo de extração utilizado de 11,36 %. O grau de substituição (GS) do amido nativo por cross-linking foi de 0,006. Os grânulos de amido nativo e modificado apresentaram formato oval e circular, cujas dimensões variaram de 26 a 26,34 µm para o diâmetro menor e de 35,75 a 36,85 µm para o diâmetro maior. Verificou-se padrão de cristalinidade do tipo C, mostrado por difratometria de raios X. O amido modificado por cross-linking apresentava melhores caracteristicas reológicas que os grânulos do amido nativo, podendo ser aplicado em alimentos para bebês, semi-prontos para serem levados ao forno de micro-ondas, produtos esterilizados, doces e alimentos congelados

EFEITO DA MODIFICAÇÃO QUÍMICA POR REAÇÃO DE CROSS-LINKING NAS PROPRIEDADES DO AMIDO DE SEMENTE DE ABACATE (Persea americana Mill)

O objetivo deste trabalho foi obter informações a respeito das propriedades do amido da semente de abacate cv. “Manteiga” e submetê-lo à modificação química por cross-linking, visando obter características reológicas aplicáveis à elaboração de produtos alimentícios. O amido nativo extraído das sementes apresentou teor de amido de 74,47 % e rendimento para o processo de extração utilizado de 11,36 %. O grau de substituição (GS) do amido nativo por cross-linking foi de 0,006. Os grânulos de amido nativo e modificado apresentaram formato oval e circular, cujas dimensões variaram de 26 a 26,34 µm para o diâmetro menor e de 35,75 a 36,85 µm para o diâmetro maior. Verificou-se padrão de cristalinidade do tipo C, mostrado por difratometria de raios X. O amido modificado por cross-linking apresentava melhores caracteristicas reológicas que os grânulos do amido nativo, podendo ser aplicado em alimentos para bebês, semi-prontos para serem levados ao forno de micro-ondas, produtos esterilizados, doces e alimentos congelados

Caracterização do extrato amiláceo nativo e modificado quimicamente da semente de abacate (Persea americana Mill)

Recent years have seen a significant increase in demand for starches with specific properties, leading to the modification of these properties in order to get ideal for your application. The objective of this study was to obtain information about the properties of starch from avocado seed cv. "Butter" and submit it to the modification by acetylation and cross-linking, to provide rheological characteristics applicable in obtaining food. The native starch showed starch content of 74.47 % in the physical-chemical analysis and performance of the extraction process used in 11.36%. The degree of substitution (GS) of native starch by acetylation was 0.007 and 0.006 for cross-linking. The native starch granules and had modified oval and circular, their dimensions ranging from 26 to 26.34 μm for the smaller diameter and 35.75 to 36.85 μm for the larger diameter. The pattern of crystallinity shown by X-ray diffraction was type C. The swelling power and solubility at temperatures 75, 85 and 95 °C was maximum for the native starch and modified by acetylation in relation to cross-linking. The changes reduced the ability of native starch hydrophilic and hydrophobic increased their capacity. The native starch gel showed an opaque folder, and with a tendency to retrogradation, modified with acetic anhydride showed no difference compared to the native whereas modification by cross-linking improved the clarity of the folder and decreased the tendency to retrogradation. Stability to freezing and thawing all samples released water in the first cycle, but with each passing day there was a decrease in syneresis. The acetylated starch did not differ from native in the analysis of viscosity has low viscosity and a greater tendency to retrogradation. The starch is modified by cross-linking showed efficacy by introducing cross-links in native starch granule and its peak viscosity was well below the value obtained in native, just had a lower tendency to retrogradation. In Differential Scanning Calorimetry (DSC) was an initial decrease in temperature for starch modified by cross-linking, and all samples did not differ significantly in peak temperature.Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESNos últimos anos houve um aumento expressivo na procura por amidos com propriedades específicas, levando à modificação dos mesmos a fim de obter propriedades ideais para sua aplicação. O objetivo deste trabalho foi obter informações a respeito das propriedades do amido da semente de abacate cv. Manteiga e submetê-lo à modificação por acetilação e cross-linking, a fim de oferecer características reológicas aplicáveis na obtenção de produtos alimentares. O amido nativo apresentou teor de amido de 74,47 % na análise físico-química e rendimento para o processo de extração utilizado de 11,36 %. O grau de substituição (GS) do amido nativo por acetilação foi de 0,007 e por cross-linking de 0,006. Os grânulos de amido nativo e modificado apresentaram formato oval e circular, suas dimensões variam de 26 a 26,34 μm para o diâmetro menor e de 35,75 a 36,85 μm para o diâmetro maior. O padrão de cristalinidade mostrado por difratometria de raios-X foi do tipo C. O poder de intumescimento e a solubilidade nas temperaturas 75, 85 e 95 ºC foi máxima para o amido nativo e modificado por acetilação em relação ao cross-linking. As modificações reduziram a capacidade hidrofílica do amido nativo e aumentaram a sua capacidade hidrofóbica. O gel do amido nativo apresentou uma pasta opaca e com tendência a retrogradação, a modificação com anidrido acético não apresentou diferença em relação ao nativo enquanto que, a modificação por cross-linking melhorou a claridade da pasta e diminuiu a tendência a retrogradação. Na estabilidade ao congelamento e descongelamento todas as amostras liberaram água no primeiro ciclo, mas com o passar dos dias houve uma diminuição da sinérese. O amido acetilado não divergiu do nativo na análise de viscosidade apresentando baixa viscosidade e maior tendência a retrogradação. O amido modificado por cross-linking apresentou eficácia com a introdução de ligações cruzadas no grânulo de amido nativo e seu pico de viscosidade foi bem abaixo do valor obtido no nativo, logo teve menor tendência a retrogradação. Na Calorimetria Exploratória Diferencial (DSC) houve uma diminuição da temperatura inicial para o amido modificado por cross-linking, sendo que todas as amostras analisadas não diferiram significativamente na temperatura de pico