Phonon-plasmon coupling in Si doped GaN nanowires
The vibrational properties of silicon doped GaN nanowires with diameters comprised between 40 and 100 nm are studied by Raman spectroscopy through excitation with two different wavelengths: 532 and 405 nm. Excitation at 532 nm does not allow the observation of the coupled phonon-plasmon upper mode for the intentionally doped samples. Yet, excitation at 405 nm results in the appearance of a narrow peak at frequencies close to that of the uncoupled A1(LO) mode for all samples. This behavior points to phonon-plasmon scattering mediated by large phonon wave-vector in these thin and highly doped nanowires
Synthesis and characterization of aps/pdms organic-inorganic hybrid materials
[ES] El uso de 3-aminopropiltrietoxi silano (APS) como precursor inorgánico en la síntesis de materiales híbridos, en sustitución
de otros alcóxidos tradicionales como el tetraetilortosilicato (TEOS), abre la posibilidad de incorporar grupos amino reactivos
en la red tridimensional. Estos grupos pueden ser utilizados para anclar diferentes compuestos orgánicos al material. Por
otro lado, la rápida velocidad de hidrólisis del APS, así como su autocatálisis permite trabajar en condiciones de síntesis muy
suaves, tales como medios no ácidos y temperatura ambiente, evitando así la descomposición de los compuestos orgánicos
activos. El objetivo de este trabajo es la síntesis y caracterización de nanocomposites en los que los alcóxidos tradicionales
han sido sustituidos por APS. Los grupos amino primarios incorporados a la red inorgánica y presentes en la superficie del
material se determinan mediante reacciones con cromóforos específicos.[EN] The use of 3- aminopropyltriethoxy silane (APS) as inorganic precursor in the synthesis of hybrid materials in substitution of
traditional alkoxides such as tetraethylorthosilicate (TEOS), opens up the possibility of incorporate reactive amine groups
into the three-dimensional network. These groups can be used in order to link different organic compounds to the material.
On the other hand, the short times of APS hydrolysis, allow to work under very soft conditions, such us non acid media and
room temperature, hence avoiding the decomposition of the organic active compounds. The aim of this work is the synthesis
and characterization of nanocomposites in which traditional alkoxides are replace by APS. Primary amine groups incorporated
into the inorganic network and present on the material surface are determined by reaction with specific chromophores.IGP agradece al CSIC la concesión de una beca I3P para la
realización de este trabajo.Peer reviewe
Surface and Structural Features of Pt/Pd-Loaded Mesoporous Silica-Delaminated Zirconium Phosphate Systems
Análisis no destructivo de vidrieras de la catedral de Ávila mediante espectroscopía microraman mapping y confocal
Las Palmas de Gran Canaria, 4-9 Julio, 2004Parcialmente financiado por la Comunidad de Madrid, Proyecto 06/0134/2003N
Non-destructive characterisation of glasses and grisailles from Segovia Cathedral Stained glass windows
Espectroscoía vibracional (IR y Raman) en problemas relacionados con la conservación y restauración del patrimonio artístico
Las Palmas de Gran Canaria, 4-9 Julio, 2004Proyecto 06/0134/2003N