Accurate quantitative EDS-TEM analysis of precipitates and matrix in equilibrium (α+β) Zr–1Nb alloys with Ta addition

The (α+β) phase microstructure in Zr-1.05Nb, Zr-0.85Nb-0.20Ta and Zr-0.85Nb-0.40Ta (wt.%) alloys annealed at 570 °C for 3840 h after β-quenching were observed at different scales by optical, SEM and TEM microscopies. A quantitative study of phase chemical compositions was carried out by EDS-TEM with experimental Cliff-Lorimer factors. The α matrix was measured on thin films and the β particle on carbon extractive replicas. The Ta addition showed a continuous increase of (Nb + Ta) solubility in α-Zr and (Zr + Ta) solubility in the β-Nb phase. The increase of Ta in the nominal composition of the Zr-1(Nb, Ta) alloy causes the decrease of the mass fraction of β-Nb phase.Fil: Ferreirós, Pedro Antonio. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Unidad de Actividad de Materiales (CAC); Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Universidad Nacional de San Martín. Instituto Sabato; Argentina. Universidad Tecnológica Nacional. Facultad Regional Haedo; ArgentinaFil: Alonso, P. R.. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Unidad de Actividad de Materiales (CAC); Argentina. Universidad Nacional de San Martín. Instituto Sabato; ArgentinaFil: Quirós, D. P.. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Unidad de Actividad de Materiales (CAC); ArgentinaFil: Zelaya, E.. Comisión Nacional de Energía Atómica. Centro Atómico Bariloche; ArgentinaFil: Rubiolo, Gerardo Hector. Universidad Nacional de San Martín. Instituto Sabato; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Unidad de Actividad de Materiales (CAC); Argentin