Nanoparticle Langmuir-Blodgett Arrays for Sensing of CO and NO2 Gases
Metal oxide sensors with active Fe2O3 and CoFe2O4 nanoparticle arrays were studied. Sensing nanoparticle films from 1, 2, 4 or 7 monolayers were deposited by Langmuir-Blodgett technique. Sensors are formed on the alumina substrates equipped with heating meander. Langmuir-Blodgett layers were heated or UV irradiated to remove the insulating surfactant. Sensing properties were studied towards CO or NO2 gases in concentrations between 0.5 and 100 ppm in mixture with the dry air. Best response values Igas/Iair were obtained with CoFe2O4 device being 3 for 100 ppm of CO and with Fe2O3 device being (38)-1 for 0.5 ppm of NO2
Effect of the crystallographic c-axis orientation on the tribological properties of the few-layer PtSe2
Two-dimensional (2D) transition metal dichalcogenides are potential
candidates for ultrathin solid-state lubricants in low-dimensional systems
owing to their flatness, high in-plane mechanical strength, and low shear
interlayer strength. Yet, the effects of surface topography and surface
chemistry on the tribological properties of 2D layers are still unclear. In
this work, we performed a comparative investigation of nanoscale tribological
properties of ultra-thin highly-ordered PtSe2 layers deposited on the sapphire
substrates with the in-plane and out-of-plane crystallographic orientation of
the PtSe2 c-axis flakes, and epitaxial PtSe2 layers. PtSe2 c-axis orientation
was found to has an impact on the nanotribological, morphological and
electrical properties of PtSe2, in particular the change in the alignment of
the PtSe2 flakes from vertical (VA) to horizontal (HA) led to the lowering of
the coefficient of friction from 0.21 to 0.16. This observation was accompanied
by an increase in the root-mean-square surface roughness from 1.0 to 1.7 nm for
the HA and VA films, respectively. The epitaxial films showed lower friction
caused by lowering adhesion when compared to other investigated films, whereas
the friction coefficient was similar to films with HA flakes. The observed
trends in nanoscale friction is attributed to a different distribution of PtSe2
structure
Polyethylene Glycol-Modified Poly(Styrene-co-Ethylene/Butylene-co-Styrene)/Carbon Nanotubes Composite for Humidity Sensing
Polymeric composites of the linear triblock copolymer poly(styrene-co-ethylene/butylene-co-styrene) grafted with maleic anhydride units (SEBS-MA) or MA modified by hydrophilic polyethylene glycol (PEG) and containing various amounts of multiwall carbon nanotubes (MWCNTs) as conducting fillerâwere prepared by solvent casting. The MWCNT surface was modified by a non-covalent approach with a pyrene-based surfactant to achieve a homogeneous dispersion of the conducting filler within the polymeric matrix. The dispersion of the unmodified and surfactant-modified MWCNTs within the elastomeric SEBS-MA and SEBS-MA-PEG matrices was characterized by studying the morphology by TEM and SAXS. Dynamical mechanical analysis was used to evaluate the interaction between the MWCNTs and copolymer matrix. The electrical conductivity of the prepared composites was measured by dielectric relaxation spectroscopy, and the percolation threshold was calculated. The prepared elastomeric composites were characterized and studied as humidity sensor. Our results demonstrated that at MWCNTs concentration slightly above the percolation threshold could result in large signal changes. In our system, good results were obtained for MWCNT loading of 2 wt% and an ~0.1 mm thin composite film. The thickness of the tested elastomeric composites and the source current appear to be very important factors that influence the sensing performance
Femtosecond time-resolved photoelectron spectroscopy in the extreme ultraviolet region
Siffalovic P. Femtosecond time-resolved photoelectron spectroscopy in the extreme ultraviolet region. Bielefeld (Germany): Bielefeld University; 2002.Eine experimentelle Apparatur fĂŒr Femtosekunden Pump-Probe-Studien reversibler Prozesse im EUV Bereich wurde aufgebaut. Photoelektronenspektren von Einzelkristallen, Adsorbaten und Gasen wurden gemessen. Die zeitaufgelösten Photoelektronenspektren des Pt(110) Valenzbandes zeigen die ultraschnelle Relaxation von heiĂen Elektronen an der KristalloberflĂ€che. Eine Pump-Probe-Kreuzkorrelation von 100 fs wurde gemessen. Die zeitaufgelösten Messungen des Ga-3d Rumpfniveaus an p- und n-GaAs(100) OberflĂ€chen zeigen den schnellen Elektronentransport im Femtosekunden-Bereich. Die anschlieĂende OberflĂ€chen-Rekombination wurde im Pikosekunden-Bereich beobachtet
2D Halide Perovskite Phase Formation Dynamics and Their Regulation by CoâAdditives for Efficient Solar Cells
Abstract The incorporation of large organic ammonium ions renders the crystallization dynamics and layer formation process of halide perovskites complex, difficult to control, and leads to problems of suppressed charge transport with the formation of tinyâsized grains. In this paper, the use of methylammonium chloride (MACl) and an excess of PbI2 is introduced as a coâadditives in the precursor solution for the control of phenylmethylammonium or benzylammonium (PMA+ spacer) and formamidinium (FA+)âbased quasiâ2D PMA2FAnâ1PbnI3n+1 (n = 5) perovskite layers formation. By this method, the morphology of the layer, the inner phase distribution, and the charge transport properties are improved. By employing glow dischargeâoptical emission spectroscopy (GDâOES) and other techniques, it is revealed that the quasiâ2D perovskites prepared in the presence of coâadditives exhibit uniform removal dynamics of the solvent across the film. Furthermore, the grain growth mode, upon thermal annealing, is lateral. It results in large, monolithic grains with lowâtrap state density and excellent substrate coverage. Particularly, coâadditives improve the cations dispersion upon the crystallization process, thus suppressing the lowân phase formed through the aggregation of spacer cations and accelerating the formation of the highân phase
Thickness effect on structural defect-related density of states and crystallinity in P3HT thin films on ITO substrates
We report on a study of thickness effect on the formation of structural defect-related density of states (DOS) in the band gap of poly(3-hexylthiophene-2,5-diyl) (P3HT) thin films spincoated on ITO substrates. The energy-resolved electrochemical impedance spectroscopy and grazing-incidence wide-angle X-ray scattering were used to correlate the DOS with the degree of crystallinity in P3HT thin films. We found an exponential increase of the defect DOS in the band gap with increasing fraction of the amorphous phase when decreasing the film thickness. The exponent increases abruptly when reducing the thickness down to 30 nm, which indicates two thickness regions with different dynamics of the defect DOS formation driven by increasing the fraction of the amorphous phase. Moreover, we observed the co-existence of two P3HT polymorphic crystalline phases with different backbone spacings, which results in the appearance of a peculiar DOS satellite peak above the highest occupied molecular orbital. The volume of the minor, more dense, crystalline phase exhibits a thickness dependence with a maximum plateau around 40 nm. These results suggest an important effect of the substrate roughness on the crystallinity and polymorphism of P3HT thin films depending on the film thickness with general implications for polymer thin films. © 2018 American Chemical Society.P3HT, SAS Institute; COFORD, Programme of Competitive Forestry Research for Development; APVV-0096-11, APVV, AgentĂșra na Podporu VĂœskumu a VĂœvoja; 2/0092/18; 1/0501/15; 2/0163/17; 26240220047; FEDER, European Regional Development FundSlovak Research and Development Agency [APVV-0096-11]; Scientific Grant Agency VEGA [1/0501/15, 2/0163/17, 2/0092/18]; Research and Development Operational Programme - ERDF [26240220047
Graphene Langmuir-Schaefer films Decorated by Pd Nanoparticles for NO2 and H2 Gas Sensors
NO2 and H2 gas sensing by few-layer graphene (FLG) were studied in dependence on the annealing and decoration of graphene by palladium nanoparticles (NPs). Graphene was deposited onto SiO2 (500 nm)/Si substrates by a modified Langmuir-Schaefer technique. A solution of FLG flakes in 1-methyl-2-pyrrolidone was obtained by a mild sonication of the expanded milled graphite. FLG films were characterized by atomic force microscopy, X-ray diffraction, Raman spectroscopy, and the Brunnauer-Emmett-Teller method. Average FLG flake thickness and lateral dimension were 5 nm and 300 nm, respectively. Drop casting of Pd NP (6â7 nm) solution onto FLG film was applied to decorate graphene by Pd. The room temperature (RT) resistance of the samples was stabilized at 15 kΩ by vacuum annealing. Heating cycles of FLG film revealed its semiconducting character. The gas sensing was tested in the mixtures of dry air with H2 gas (10 to 10 000 ppm) and NO2 gas (2 to 200 ppm) between RT and 200 °C. The response of 26 % to H2 was achieved by FLG with Pd decoration at 70 °C and 10 000 ppm of H2 in the mixture. Pure FLG film did not show any response to H2. The response of FLG with Pd to 6 ppm of NO2 at RT was â„ 23 %. It is 2 times larger than that of the pure FLG sample. Long term stability of sensors was studied
Kinetics of PolymerâFullerene Phase Separation during Solvent Annealing Studied by Table-Top Xâray Scattering
Solvent annealing is an efficient
way of phase separation in polymerâfullerene
blends to optimize bulk heterojunction morphology of active layer
in polymer solar cells. To track the process in real time across all
relevant stages of solvent evaporation, laboratory-based in situ small-
and wide-angle X-ray scattering measurements were applied simultaneously
to a model P3HT:PCBM blend dissolved in dichlorobenzene. The PCBM
molecule agglomeration starts at âŒ7 wt % concentration of solid
content of the blend in solvent. Although PCBM agglomeration is slowed-down
at âŒ10 wt % of solid content, the rate constant of phase separation
is not changed, suggesting agglomeration and reordering of P3HT molecular
chains. Having the longest duration, this stage most affects BHJ morphology.
Phase separation is accelerated rapidly at concentration of âŒ25
wt %, having the same rate constant as the growth of P3HT crystals.
P3HT crystallization is driving force for phase separation at final
stages before a complete solvent evaporation, having no visible temporal
overlap with PCBM agglomeration. For the first time, such a study
was done in laboratory demonstrating potential of the latest generation
table-top high-brilliance X-ray source as a viable alternative before
more sophisticated X-ray scattering experiments at synchrotron facilities
are performed
Directional Crystallization from the Melt of an Organic p-Type and n-Type Semiconductor Blend
info:eu-repo/semantics/publishe