In situ synchrotron radiation diffraction investigation of the compression behaviour at 350 °C of ZK40 alloys with addition of CaO and Y

The evolution of the microstructure during compression is investigated with in situ synchrotron radiation diffraction in as-cast ZK40, ZK40-2CaO and ZK40-1Y Mg alloys. The specimens were compressed at 350 °C with a strain rate of 10−3 s−1 until 30% deformation. The Y containing alloy showed the highest 0.2% proof strength in compression of 35 MPa at 350 °C which is double that of the ZK40 alloy, while the CaO added alloy shows a moderate increment at 23 MPa. The Y containing alloy shows some work hardening, while the CaO modified and the ZK40 alloys do not show work hardening after yield. Synchrotron radiation diffraction timelines show that continuous and discontinuous dynamic recrystallization occurs during deformation of the ZK40 alloy while a small amount of dynamic recrystallization was observed in the ZK40-1Y alloy. However, dynamic recrystallization was not present in the ZK40-2CaO alloy. SEM-EBSD analysis conducted on the deformed samples shows a significantly high volume fraction of twins in the Y and CaO containing alloys which was absent in the ZK40 alloy. The modified deformation behaviours observed in the CaO and Y containing alloys were attributed to the presence of intermetallic particles found at the grain boundaries and to the role of Ca and Y in stabilising twinning.The authors acknowledge the Deutsches Elektronen-Synchro-tron for the provision of facilities within the framework of proposal I-20130434.RHBacknowledgesUniversityofSãoPaulofor granting the fellowship 'Bolsa Empreendedorismo'

Phase formation during solidification of Mg-Nd-Zn alloys: An in situ synchrotron radiation diffraction study

Mg-4Nd base alloys with Zn additions of 3, 5 and 8 wt % were investigated with in situ synchrotron radiation diffraction during solidification. This method enabled the investigation of phase formation and transformation in the alloys. The diffraction results were supported with TEM observations on the as-solidified samples. The results show the effect of increased Zn addition on stabilizing the Mg3RE phase (RE—rare earth). The experimental results agree only partially with the theoretical calculations indicating the need to improve the existing thermodynamic database on the alloy syste

Plasticity analysis by synchrotron radiation in a Mg97Y2Zn1 alloy with bimodal grain structure and containing LPSO phase

© 2015 Acta Materialia Inc. All rights reserved. Deformation behaviour has been examined by synchrotron radiation diffraction in an extruded magnesium - long-period-stacking-order phase alloy comprising three components of microstructure. The variation of internal strains and intensities of the important crystallographic planes of the two phases has been examined during compression at several temperatures. The long-period-stacking-order phase remains elastic to stresses beyond the macroscopic yield stress while deformation in the magnesium matrix is dominated by twinning and basal slip, with the coarse-grained regions deforming plastically at stresses well below the macroscopic yield stress while regions with fine grain size deform plastically only at much higher stresses.We would like to acknowledge financial support of the Spanish Ministry of Education and Science under project number MAT2012-34135. We would like to acknowledge the expert support of Miguel Acedo and Edurne Laurin for assistance with the extrusion processing and the metallographical preparation, respectively.Peer Reviewe

On the influence of solution and ageing treatments on the microstructure of ZK40 alloys modified with Ca, Gd, Nd and y additions

Abstract As-cast ZK40 alloys, modified with the addition of CaO, Gd, Nd and Y were investigated. Solution heat treatments were performed based on differential thermal analysis results. The unmodified ZK40 alloy exhibited microstructure with nearly no intermetallic compound but with precipitates formed during the solution treatment. The modified ZK40 alloys exhibited a semi-dissolved network of intermetallic compounds along the grain boundaries and zones of intermetallic compounds within the grains. Interestingly, no precipitates were observed immediately next to the grain boundaries. The energy dispersive X-ray spectroscopy line scans showed an enrichment of Zn and Zr in the regions where the precipitates are found, suggesting that they are Zn-Zr precipitates. The ageing behaviour was compared between the as-cast and the solution treated materials and it was found that apart from the ZK40-Gd, ZK40-Nd and ZK40-Y aged at 200 °C after solution treatment, there is no notable ageing response for the investigated alloys.</jats:p

Fibromuscular Arterial Disease

Peer Reviewedhttp://deepblue.lib.umich.edu/bitstream/2027.42/75604/1/j.1440-1673.1970.tb01633.x.pd

Reliability of Synaptic Transmission at the Synapses of Held In Vivo under Acoustic Stimulation

BACKGROUND:The giant synapses of Held play an important role in high-fidelity auditory processing and provide a model system for synaptic transmission at central synapses. Whether transmission of action potentials can fail at these synapses has been investigated in recent studies. At the endbulbs of Held in the anteroventral cochlear nucleus (AVCN) a consistent picture emerged, whereas at the calyx of Held in the medial nucleus of the trapezoid body (MNTB) results on the reliability of transmission remain inconsistent. In vivo this discrepancy could be due to the difficulty in identifying failures of transmission. METHODS/FINDINGS:We introduce a novel method for detecting unreliable transmission in vivo. Based on the temporal relationship between a cells' waveform and other potentials in the recordings, a statistical test is developed that provides a balanced decision between the presence and the absence of failures. Its performance is quantified using simulated voltage recordings and found to exhibit a high level of accuracy. The method was applied to extracellular recordings from the synapses of Held in vivo. At the calyces of Held failures of transmission were found only rarely. By contrast, at the endbulbs of Held in the AVCN failures were found under spontaneous, excited, and suppressed conditions. In accordance with previous studies, failures occurred most abundantly in the suppressed condition, suggesting a role for inhibition. CONCLUSIONS/SIGNIFICANCE:Under the investigated activity conditions/anesthesia, transmission seems to remain largely unimpeded in the MNTB, whereas in the AVCN the occurrence of failures is related to inhibition and could be the basis/result of computational mechanisms for temporal processing. More generally, our approach provides a formal tool for studying the reliability of transmission with high statistical accuracy under typical in vivo recording conditions

As cast microstructures on the mechanical and corrosion behaviour of ZK40 modified with Gd and Nd additions

The microstructure of ZK40, ZK40 with 2 wt% of Nd and Gd (ZK40-2Nd and ZK40-2Gd, respectively) were investigated with optical, scanning and transmission electron microscopy, X-ray diffraction and Scanning Kelvin Probe Force Microscopy. The mechanical properties and the corrosion behaviour were correlated with the microstructure. The 2 wt% Gd addition enhanced the ductility, while the Nd addition resulted in deterioration in mechanical properties. The corrosion behaviour was also enhanced with the addition of Gd.The authors acknowledge the Deutsches Elektronen-Synchrotron (DESY) for the provision of facilities within the framework of proposal I-20130434. RHB acknowledges University of Sao Paulo for granting the fellowship ´Bolsa Empreendedorismo´. MM acknowledges the Alexander von Humboldt foundation for the provision of financial support in the form of post-doctoral fellowship

Dental Health and Mortality in People With End-Stage Kidney Disease Treated With Hemodialysis: A Multinational Cohort Study

Background Dental disease is more extensive in adults with chronic kidney disease, but whether dental health and behaviors are associated with survival in the setting of hemodialysis is unknown. Study Design Prospective multinational cohort. Setting & Participants 4,205 adults treated with long-term hemodialysis, 2010 to 2012 (Oral Diseases in Hemodialysis [ORAL-D] Study). Predictors Dental health as assessed by a standardized dental examination using World Health Organization guidelines and personal oral care, including edentulousness; decayed, missing, and filled teeth index; teeth brushing and flossing; and dental health consultation. Outcomes All-cause and cardiovascular mortality at 12 months after dental assessment. Measurements Multivariable-adjusted Cox proportional hazards regression models fitted with shared frailty to account for clustering of mortality risk within countries. Results During a mean follow-up of 22.1 months, 942 deaths occurred, including 477 cardiovascular deaths. Edentulousness (adjusted HR, 1.29; 95% CI, 1.10-1.51) and decayed, missing, or filled teeth score ≥ 14 (adjusted HR, 1.70; 95% CI, 1.33-2.17) were associated with early all-cause mortality, while dental flossing, using mouthwash, brushing teeth daily, spending at least 2 minutes on oral hygiene daily, changing a toothbrush at least every 3 months, and visiting a dentist within the past 6 months (adjusted HRs of 0.52 [95% CI, 0.32-0.85], 0.79 [95% CI, 0.64-0.97], 0.76 [95% CI, 0.58-0.99], 0.84 [95% CI, 0.71-0.99], 0.79 [95% CI, 0.65-0.95], and 0.79 [95% CI, 0.65-0.96], respectively) were associated with better survival. Results for cardiovascular mortality were similar. Limitations Convenience sample of clinics. Conclusions In adults treated with hemodialysis, poorer dental health was associated with early death, whereas preventive dental health practices were associated with longer survival