Synthesis and optimisation of IrO2 electrocatalysts by Adams fusion method for solid polymer electrolyte electrolysers
IrO2 as an anodic electrocatalyst for the oxygen evolution reaction (OER) in solid polymer electrolyte (SPE) electrolysers was synthesised by adapting the Adams fusion method. Optimisation of the IrO2 electrocatalyst was achieved by varying the synthesis duration (0.5 – 4 hours) and temperature (250 - 500°C). The physical properties of the electrocatalysts were characterised by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and x-ray diffraction (XRD). Electrochemical characterisation of the electrocatalysts toward the OER was evaluated by chronoamperometry (CA). CA analysis revealed the best electrocatalytic activity towards the OER for IrO2 synthesised for 2 hours at 350oC which displayed a better electrocatalytic activity than the commercial IrO2 electrocatalyst used in this study. XRD and TEM analyses revealed an increase in crystallinity and average particle size with increasing synthesis duration and temperature which accounted for the decreasing electrocatalytic activity. At 250°C the formation of an active IrO2 electrocatalyst was not favoured
Effects of heat treatment on the catalytic activity and methanol tolerance of carbon-supported platinum alloys
This work studies the effect of heat treatment of carbon-dispersed platinum and platinum alloys on its methanol tolerance and catalytic activity as gas diffusion electrodes for oxygen reduction reaction (ORR) in acid medium. The catalyst powders were subjected to heat treatments at three different temperatures for a fixed period at controlled atmospheres. Differences in catalyst morphology were characterized using X-ray diffraction, energy dispersive X-ray analysis and transmission electron microscope techniques. The electrochemical characteristics and activity of the electro-catalysts were evaluated for ORR and methanol tolerance using cyclic voltammetry, in the form of gas diffusion electrodes. The optimum heat-treatment temperature is found to be strongly dependent on the individual catalyst. The maximum ORR activity and better methanol tolerance for the oxygen reduction reaction (ORR) was observed in Pt-Fe/C and Pt-Cu/C catalysts subjected to heat treatment at 350 °C.A trend of catalytic activity for oxygen reduction reaction (ORR) was obtained: Pt-Cu/C (350°C)>Pt-Fe/C (350°C) > Pt-Ni/C (350°C) > Pt-Co/C (250°C) > Pt/C (350°C), showing that Pt-Cu/C-type catalysts had a higher catalytic activity with reasonable methanol tolerance
Nanoparticulate TiO2-promoted PtRu/C catalyst for methanol oxidation: TiO2 nanoparticles promoted PtRu/C catalyst for MOR
To improve the electrocatalytic properties of PtRu/C in methanol electrooxidation, nanoparticulate TiO2-promoted PtRu/C catalysts were prepared by directly mixing TiO2 nanoparticles with PtRu/C. Using cyclic voltammetry, it was found that the addition of 10 wt% TiO2 nanoparticles can effectively improve the electrocatalytic activity and stability of the catalyst during methanol electro-oxidation. The value of the apparent activation energy (Ea) for TiO2-PtRu/C was lower than that for pure PtRu/C at a potential range from 0.45 to 0.60 V. A synergistic effect between PtRu and TiO2 nanoparticles is likely to facilitate the removal of CO-like intermediates from the surface of PtRu catalyst and reduce the poisoning of the PtRu catalysts during methanol electrooxidation. Therefore, we conclude that the direct introduction of TiO2 nanoparticles into PtRu/ C catalysts offers an improved facile method to enhance the electrocatalytic performance of PtRu/C catalyst in methanol electrooxidation.Web of Scienc
Bifunctional non-noble metal oxide nanoparticle electrocatalysts through lithium-induced conversion for overall water splitting
Developing earth-abundant, active and stable electrocatalysts which operate in the same electrolyte for water splitting, including oxygen evolution reaction and hydrogen evolution reaction, is important for many renewable energy conversion processes. Here we demonstrate the improvement of catalytic activity when transition metal oxide (iron, cobalt, nickel oxides and their mixed oxides) nanoparticles (~20 nm) are electrochemically transformed into ultra-small diameter (2–5 nm) nanoparticles through lithium-induced conversion reactions. Different from most traditional chemical syntheses, this method maintains excellent electrical interconnection among nanoparticles and results in large surface areas and many catalytically active sites. We demonstrate that lithium-induced ultra-small NiFeOx nanoparticles are active bifunctional catalysts exhibiting high activity and stability for overall water splitting in base. We achieve 10 mA cm−2 water-splitting current at only 1.51 V for over 200 h without degradation in a two-electrode configuration and 1 M KOH, better than the combination of iridium and platinum as benchmark catalysts.open10
Characterization of Au and Bimetallic PtAu Nanoparticles on PDDA-Graphene Sheets as Electrocatalysts for Formic Acid Oxidation
Characteristics and properties of nano-LiCoO2 synthesized by pre-organized single source precursors: Li-ion diffusivity, electrochemistry and biological assessment
Background: LiCoO2 is one of the most used cathode materials in Li-ion batteries. Its conventional synthesis requires high temperature (>800 degrees C) and long heating time (>24 h) to obtain the micronscale rhombohedral layered high-temperature phase of LiCoO2 ( HT-LCO). Nanoscale HT-LCO is of interest to improve the battery performance as the lithium (Li+) ion pathway is expected to be shorter in nanoparticles as compared to micron sized ones. Since batteries typically get recycled, the exposure to nanoparticles during this process needs to be evaluated. Results: Several new single source precursors containing lithium (Li+) and cobalt (Co2+) ions, based on alkoxides and aryloxides have been structurally characterized and were thermally transformed into nanoscale HT-LCO at 450 degrees C within few hours. The size of the nanoparticles depends on the precursor, determining the electrochemical performance. The Li-ion diffusion coefficients of our - LiCoO2 nanoparticles improved at least by a factor of 10 compared to commercial one, while showing good reversibility upon charging and discharging. The hazard of occupational exposure to nanoparticles during battery recycling was investigated with an in vitro multicellular lung model. Conclusions: Our heterobimetallic single source precursors allow to dramatically reduce the production temperature and time for HT-LCO. The obtained nanoparticles of LiCoO2 have faster kinetics for Li+ insertion/extraction compared to microparticles. Overall, nano-sized - LiCoO2 particles indicate a lower cytotoxic and (pro-)inflammogenic potential in vitro compared to their micron-sized counterparts. However, nanoparticles aggregate in air and behave partially like microparticles
Photocatalytic reduction of methylene blue by TiO2 nanotube arrays: effects of TiO2 crystalline phase
Tuning Complex Transition Metal Hydroxide Nanostructures as Active Catalysts for Water Oxidation by a Laser–Chemical Route
Ethylene glycol oxidation on ternary PtRhNi/C electrocatalyst with different metal compositions
- …