Enhanced tensile ductility in Al-Mg alloys by solid-solution interactions
The development of methods for obtaining high tensile elongation in aluminum alloys is of great importance for the practical forming of near-net-shape parts. Current superplastic alloys are limited in use by high material costs. The utilization of solute-drag creep processes, the approach used in this study, to obtain enhanced tensile ductility in aluminum alloys has lead to tensile elongations of up to 325% in simple, binary Al-Mg alloys with coarse grain sizes. This method has the advantage of lowering processing costs in comparison with superplastic alloys because a fine grain size is not necessary. Whereas superplastic alloys typically have a strain-rate sensitivity of m = 0.5, the enhanced ductility Al-Mg alloys typically exhibit m = 0.3 where maximum ductility is observed. Although a strain-rate sensitivity of rn = 0.5 can lead to elongations of over 1000% (superplastic materials) a value of m = 0.3 is shown experimentally to be sufficient for obtaining elongations of 150% to a maximum observed of 325%. Enhanced ductility is also affected strongly by ternary alloying additions, such as Mn, for which a preliminary understanding is pursued
Novel B(Ar')2(Ar'') hetero-tri(aryl)boranes: a systematic study of Lewis acidity
A series of homo- and hetero-tri(aryl)boranes incorporating pentafluorophenyl, 3,5-bis(trifluoromethyl)phenyl, and pentachlorophenyl groups, four of which are novel species, have been studied as the acidic component of frustrated Lewis pairs for the heterolytic cleavage of H2. Under mild conditions eight of these will cleave H2; the rate of cleavage depending on both the electrophilicity of the borane and the steric bulk around the boron atom. Electrochemical studies allow comparisons of the electrophilicity with spectroscopic measurements of Lewis acidity for different series of boranes. Discrepancies in the correlation between these two types of measurements, combined with structural characterisation of each borane, reveal that the twist of the aryl rings with respect to the boron-centred trigonal plane is significant from both a steric and electronic perspective, and is an important consideration in the design of tri(aryl)boranes as Lewis acids
An Electrochemical Study of Frustrated Lewis Pairs: A Metal-free Route to Hydrogen Oxidation
[Image: see text] Frustrated Lewis pairs have found many applications in the heterolytic activation of H(2) and subsequent hydrogenation of small molecules through delivery of the resulting proton and hydride equivalents. Herein, we describe how H(2) can be preactivated using classical frustrated Lewis pair chemistry and combined with in situ nonaqueous electrochemical oxidation of the resulting borohydride. Our approach allows hydrogen to be cleanly converted into two protons and two electrons in situ, and reduces the potential (the required energetic driving force) for nonaqueous H(2) oxidation by 610 mV (117.7 kJ mol(–1)). This significant energy reduction opens routes to the development of nonaqueous hydrogen energy technology
Effects of two nights partial sleep deprivation on an evening submaximal weightlifting performance; are 1 h powernaps useful on the day of competition?
We have investigated the effects that sleep restriction (3-h sleep during two consecutive nights) have on an evening (17:00 h) submaximal weightlifting session; and whether this performance improves following a 1-h post-lunch powernap. Fifteen resistance-trained males participated in this study. Before the experimental protocol commenced, 1RM bench press and inclined leg press and normative habitual sleep were recorded. Participants were familiarised with the testing protocol, then completed three experimental conditions with two nights of prescribed sleep: (i) Normal (N): retire at 23:00 h and wake at 06:30 h, (ii) partial sleep-deprivation (SD): retire at 03:30 h and wake at 06:30 h and (iii) partial sleep-deprivation with nap (SDN): retire at 03:30 h and wake at 06:30 h with a 1-h nap at 13:00 h. Each condition was separated by at least 7 days and the order of administration was randomised and counterbalanced. Rectal (Trec) and mean skin (Ts) temperatures, Profile of Mood Scores, subjective tiredness, alertness and sleepiness values were measured at 08:00, 11:00, 14:00 and 17:00 h on the day of the weightlifting session. Following the final temperature measurements at 17:00 h, participants completed a 5-min active warm-up before a ‘strength’ protocol. Participants performed three repetitions of right-hand grip strength, then three repetitions at each incremental load (40%, 60% and 80% of 1RM) for bench press and inclined leg press, with a 5-min recovery in between each repetition. A linear encoder was attached perpendicular to the movement, to the bar used for the exercises. Average power (AP), average force (AF), peak velocity (PV), distance (D) and time-to-peak velocity (tPV) were measured (MuscleLab software) during the concentric phase of the movements for each lift. Data were analysed using general linear models with repeated measures. The main findings were that SD reduced maximal grip (2.7%), bench press (11.2% AP, 3.3% AF and 9.4% PV) and leg press submaximal values (5.7% AP) with a trend for a reduction in AF (3.3% P = 0.06). Furthermore, RPE increased for measures of grip strength, leg and bench press during SD. Following a 1-h powernap (SDN), values of grip and bench press improved to values similar in N, as did tiredness, alertness and sleepiness. There was a main effect for “load” on the bar for both bench and leg press where AP, AF, tPV values increased with load (P < 0.05) and PV decreased from the lightest to the heaviest load for both bench and leg press. An interaction of “load and condition” was present in leg press only, where the rate of change of AP is greater in the N than SD and SDN conditions. In addition, for PV and tPV the rate of change was greater for SDN than N or SD condition values. In summary, SD had a negative effect on grip strength and some components of bench and inclined leg press. The use of a 1-h power nap that ended 3 h before the “strength” assessment had a positive effect on weightlifting performance, subjective mood and ratings of tiredness
Is the diurnal variation in muscle force output detected/detectable when multi-joint movements are analysed using the musclelab force-velocity encoder?
We have investigated the magnitude of diurnal variation in back squat and bench press performance using the MuscleLab force velocity transducer. Thirty resistance-trained males (mean ± SD: age 21.7 ± 1.4 years; body mass 80.5 ± 4.5 kg; height 1.79 ± 0.06 m) underwent two sessions at different times of day: morning (M, 07:30 h) and evening (E, 17:30 h). Each session included a period when rectal temperature (Trec) was measured at rest, a 5-min standardized 150 W warm-up on a cycle ergometer, then defined programme of bench press (at 20, 40 and 60 kg) and back squat (at 30, 50 and 70 kg) exercises. A linear encoder was attached to an Olympic bar used for the exercises and average force (AF), peak velocity (PV) and time-to-peak velocity (tPV) were measured (MuscleLab software; MuscleLab Technology, Langesund, Norway) during the concentric phase of the movements. Values for Trec at rest were higher in the evening compared to morning values (0.48°C, P < 0.0005). Daily variations were apparent for both bench press and back squat performance for AF (1.9 and 2.5%), PV (8.3 and 12.7%) and tPV (-16.6 and -9.8%; where a negative number indicates a decrease in the variable from morning to evening). There was a main effect for load where AF and tPV increased and PV decreased from the lightest load to the heaviest for both bench press and back squat (47.1 and 80.2%; 31.7 and 57.7%; -42.1 and -73.9%; P < 0.0005 where a negative number indicates a decrease in the variable with increasing load). An interaction was found only for tPV, such that the tPV occurs earlier in the evening than the morning at the highest loads (60 and 70 kg) for both bench press and back squat, respectively (mean difference of 0.32 and 0.62 s). In summary, diurnal variation in back squat and bench press was shown; and the tPV in complex multi-joint movements occurs earlier during the concentric phase of exercise when back squat or bench press is performed in the evening compared to the morning. This difference can be detected using a low cost, portable and widely available commercial instrument and enables translation of past laboratory/tightly controlled experimental research in to main-stream coaching practice
Tetrabenzoporphyrin and -mono-, - Cis -di- and tetrabenzotriazaporphyrin derivatives: Electrochemical and spectroscopic implications of meso CH Group replacement with nitrogen
Nonperipherally hexyl-substituted metal-free tetrabenzoporphyrin (2H-TBP, 1a) tetrabenzomonoazaporphyrin (2H-TBMAP, 2a), tetrabenzo-cis-diazaporphyrin (2H-TBDAP, 3a), tetrabenzotriazaporphyrin (2H-TBTAP, 4a), and phthalocyanine (2H-Pc, 5a), as well as their copper complexes (1b-5b), were synthesized. As the number of meso nitrogen atoms increases from zero to four, Îmax of the Q-band absorption peak becomes red-shifted by almost 100 nm, and extinction coefficients increased at least threefold. Simultaneously the blue-shifted Soret (UV) band substantially decreased in intensity. These changes were related to the relative electron-density of each macrocycle expressed as the group electronegativity sum of all meso N and CH atom groups, âχR. X-ray photoelectron spectroscopy differentiated between the three different types of macrocyclic nitrogen atoms (the Ninner, (NH)inner, and Nmeso) in the metal-free complexes. Binding energies of the Nmeso and Ninner,Cu atoms in copper chelates could not be resolved. Copper insertion lowered especially the cathodic redox potentials, while all four observed redox processes occurred at larger potentials as the number of meso nitrogens increased. Computational chemical methods using density functional theory confirmed 1b to exhibit a Cu(II) reduction prior to ring-based reductions, while for 2b, Cu(II) reduction is the first reductive step only if the nonperipheral substituents are hydrogen. When they are methyl groups, it is the second reduction process; when they are ethyl, propyl, or hexyl, it becomes the third reductive process. Spectro-electrochemical measurements showed redox processes were associated with a substantial change in intensity of at least two main absorbances (the Q and Soret bands) in the UV spectra of these compounds
Recommended from our members
Ancient and Modern Laminated Composites - From the Great Pyramid of Gizeh to Y2K
Laminated metal composites have been cited in antiquity; for example, a steel laminate that may date as far back as 2750 B.C., was found in the Great Pyramid in Gizeh in 1837. A laminated shield containing bronze, tin, and gold layers, is described in detail by Homer. Well-known examples of steel laminates, such as an Adze blade, dating to 400 B.C. can be found in the literature. The Japanese sword is a laminated composite at several different levels and Merovingian blades were composed of laminated steels. Other examples are also available, including composites from China, Thailand, Indonesia, Germany, Britain, Belgium, France, and Persia. The concept of lamination to provide improved properties has also found expression in modern materials. Of particular interest is the development of laminates including high carbon and low carbon layers. These materials have unusual properties that are of engineering interest; they are similar to ancient welded Damascus steels. The manufacture of collectable knives, labeled ''welded Damascus'', has also been a focus of contemporary knifemakers. Additionally, in the Former Soviet Union, laminated composite designs have been used in engineering applications. Each of the above areas will be briefly reviewed, and some of the metallurgical principles will be described that underlie improvement in properties by lamination. Where appropriate, links are made between these property improvements and those that may have been present in ancient artifacts
Recommended from our members
On the importance of target materials interfaces during low speed impact
We are conducting a Cooperative Research and Development Project under the sponsorship of the U.S. Department of Energy to determine the applicability of aluminum particulate reinforced alloy laminates to aircraft structures and for containment of aircraft engine turbine blades and debris due to catastrophic engine failure. Within this framework, we are studying the terminal interaction of projectiles impacting targets at speeds of 150- to 500 m/s. Our presentation focuses on a special series of experiments and computational physics analyses of 6061-T6 aluminum alloy targets in single plate and laminate form impacted by steel cylindrical projectiles. Four cases are examined, projectile impact into (1) a single plate, (2) three contiguous plates (frictional interfaces), (3) three contiguous plates separated by Teflon layers (frictionless interfaces), and (4) a spaced array of three plates. We found that the ratio of projectile kinetic energies just at target perforation for the highest to lowest critical projectile speeds over the four targets is 1.75. Considering that target areal density is held constant across the four targets, this is a dramatic result. 2 refs., 7 figs
Recommended from our members
Laminated metals composites fracture and ballistic impact behavior
Recent advances in the fracture and ballistic impact response of laminated metal composites (LMCs) are reviewed. The laminate structure can provide significant improvements to these properties relative to the component materials. Typical fracture and ballistic impact properties in LMCs are illustrated for systems containing Al alloys and Al matrix composites. The unique mechanisms operating in a layered structure that contribute to fracture or ballistic impact resistance are discussed. The influence of laminate architecture, component material properties and interface strength on mechanisms and properties are briefly reviewed for these Al-based LMCs
- …