14 research outputs found
Far-infrared absorption in parallel quantum wires with weak tunneling
We study collective and single-particle intersubband excitations in a system
of quantum wires coupled via weak tunneling. For an isolated wire with
parabolic confinement, the Kohn's theorem guarantees that the absorption
spectrum represents a single sharp peak centered at the frequency given by the
bare confining potential. We show that the effect of weak tunneling between two
parabolic quantum wires is twofold: (i) additional peaks corresponding to
single-particle excitations appear in the absorption spectrum, and (ii) the
main absorption peak acquires a depolarization shift. We also show that the
interplay between tunneling and weak perpendicular magnetic field drastically
enhances the dispersion of single-particle excitations. The latter leads to a
strong damping of the intersubband plasmon for magnetic fields exceeding a
critical value.Comment: 18 pages + 6 postcript figure
Zn Se Cd S Interlayer Formation at the CdS Cu2ZnSnSe4 Thin Film Solar Cell Interface
The chemical structure of the CdS/Cu2ZnSnSe4 (CZTSe) interface was studied by a combination of electron and X-ray spectroscopies with varying surface sensitivity. We find the CdS chemical bath deposition causes a "redistribution" of elements in the proximity of the CdS/CZTSe interface. In detail, our data suggest that Zn and Se from the Zn-terminated CZTSe absorber and Cd and S from the buffer layer form a Zn-Se-Cd-S interlayer. We find direct indications for the presence of Cd-S, Cd-Se, and Cd-Se-Zn bonds at the buffer/absorber interface. Thus, we propose the formation of a mixed Cd(S,Se)-(Cd,Zn)Se interlayer. We suggest the underlying chemical mechanism is an ion exchange mediated by the amine complexes present in the chemical bath
Entrepreneurial Supply Chain Management Competence: Performance of Manufacturing Small and Medium Enterprises
Observation of audio-frequency edge magnetoplasmons in the classical two-dimensional electron gas
Experimental determination of the charge neutrality level of Poly[2 methoxy 5 2 ethylhexyloxy p phenylene vinylene] MEH PPV
One-dimensional subband effects in the conductance of multiple quantum wires in Si metal-oxide-semiconductor field-effect transistors
Contains fulltext :
112832.pdf (publisher's version ) (Open Access
Microcrystalline silicon oxides for silicon-based solar cells: impact of the O/Si ratio on the electronic structure
Hydrogenated microcrystalline silicon oxide (μc-SiOx:H) layers are one alternative approach to ensure sufficient interlayer charge transport while maintaining high transparency and good passivation in Si-based solar cells. We have used a combination of complementary x-ray and electron spectroscopies to study the chemical and electronic structure of the (μc-SiOx:H) material system. With these techniques, we monitor the transition from a purely Si-based crystalline bonding network to a silicon oxide dominated environment, coinciding with a significant decrease of the material’s conductivity. Most Si-based solar cell structures contain emitter/contact/passivation layers. Ideally, these layers fulfill their desired task (i.e., induce a sufficiently high internal electric field, ensure a good electric contact, and passivate the interfaces of the absorber) without absorbing light. Usually this leads to a trade-off in which a higher transparency can only be realized at the expense of the layer’s ability to properly fulfill its task. One alternative approach is to use hydrogenated microcrystalline silicon oxide (μc-SiOx:H), a mixture of microcrystalline silicon and amorphous silicon (sub)oxide. The crystalline Si regions allow charge transport, while the oxide matrix maintains a high transparency. To date, it is still unclear how in detail the oxygen content influences the electronic structure of the μc-SiOx:H mixed phase material. To address this question, we have studied the chemical and electronic structure of the μc-SiOx:H (0 ≤ x = O/Si ≤1) system with a combination of complementary x-ray and electron spectroscopies. The different surface sensitivities of the employed techniques help to reduce the impact of surface oxides on the spectral interpretation. For all samples, we find the valence band maximum to be located at a similar energy with respect to the Fermi energy. However, for x > 0.5, we observe a pronounced decrease of Si 3s – Si 3p hybridization in favor of Si 3p – O 2p hybridization in the upper valence band. This coincides with a significant increase of the material’s resistivity, possibly indicating the breakdown of the conducting crystalline Si network. Silicon oxide layers with a thickness of several hundred nanometres were deposited in a PECVD (plasma-enhanced chemical vapor deposition) multi chamber system using an excitation frequency of 13.56 MHz with a plasma power density of 0.3 W/cm2. Glass (Corning type Eagle) and mono-crystalline silicon wafer substrates were coated in the same run at a substrate temperature of 185°C. The deposition pressure was 4 mbar and the substrate-electrode distance 20 mm. Mixtures of silane (SiH4), 1% TMB (B(CH3)3) diluted in helium, hydrogen (H2), and carbon dioxide (CO2) gases were used at flow rates of 1.25 - 0.18/0.32/500/0 – 1.07) sccm (standard cubic centimeters per minute) for the deposition of μc-SiOx:H(B) layers. By changing the CO2/SiH4 gas flow rate ratio from 0 to 6, μc-SiOx:H(B) layers with a composition of 0 ≤ x = O/Si ≤ 1 were prepared using a constant sum of SiH4 and CO2. The TMB flow and the H2 flow were kept constant within the series. For more details see Ref. [1]. The oxygen content in the films was determined using Rutherford Backscattering Spectroscopy (RBS). With RBS, the area-related atomic density of oxygen and silicon can be determined (± 2% [2]), and thus x can be calculated. This quantity considers only the number of silicon / oxygen atoms and not the number of atoms of other elements, such as hydrogen, which is also incorporated to a considerable extent: up to 20% in μc-SiOx:H (measured using the hydrogen effusion method). To avoid charging effects, the measurements were performed on films deposited on a substrate of mono-crystalline silicon wafers. The electrical conductivity was measured in the planar direction of the film in a vacuum cryostat, using voltages from - 100 V to + 100 V. For that two co-planar Ag contacts were evaporated on the film with a gap of 0.5 mm 5 mm
Microcrystalline silicon oxides for silicon-based solar cells: impact of the O/Si ratio on the electronic structure
Hydrogenated microcrystalline silicon oxide (μc-SiOx:H) layers are one alternative approach to ensure sufficient interlayer charge transport while maintaining high transparency and good passivation in Si-based solar cells. We have used a combination of complementary x-ray and electron spectroscopies to study the chemical and electronic structure of the (μc-SiOx:H) material system. With these techniques, we monitor the transition from a purely Si-based crystalline bonding network to a silicon oxide dominated environment, coinciding with a significant decrease of the material’s conductivity. Most Si-based solar cell structures contain emitter/contact/passivation layers. Ideally, these layers fulfill their desired task (i.e., induce a sufficiently high internal electric field, ensure a good electric contact, and passivate the interfaces of the absorber) without absorbing light. Usually this leads to a trade-off in which a higher transparency can only be realized at the expense of the layer’s ability to properly fulfill its task. One alternative approach is to use hydrogenated microcrystalline silicon oxide (μc-SiOx:H), a mixture of microcrystalline silicon and amorphous silicon (sub)oxide. The crystalline Si regions allow charge transport, while the oxide matrix maintains a high transparency. To date, it is still unclear how in detail the oxygen content influences the electronic structure of the μc-SiOx:H mixed phase material. To address this question, we have studied the chemical and electronic structure of the μc-SiOx:H (0 ≤ x = O/Si ≤1) system with a combination of complementary x-ray and electron spectroscopies. The different surface sensitivities of the employed techniques help to reduce the impact of surface oxides on the spectral interpretation. For all samples, we find the valence band maximum to be located at a similar energy with respect to the Fermi energy. However, for x > 0.5, we observe a pronounced decrease of Si 3s – Si 3p hybridization in favor of Si 3p – O 2p hybridization in the upper valence band. This coincides with a significant increase of the material’s resistivity, possibly indicating the breakdown of the conducting crystalline Si network. Silicon oxide layers with a thickness of several hundred nanometres were deposited in a PECVD (plasma-enhanced chemical vapor deposition) multi chamber system using an excitation frequency of 13.56 MHz with a plasma power density of 0.3 W/cm2. Glass (Corning type Eagle) and mono-crystalline silicon wafer substrates were coated in the same run at a substrate temperature of 185°C. The deposition pressure was 4 mbar and the substrate-electrode distance 20 mm. Mixtures of silane (SiH4), 1% TMB (B(CH3)3) diluted in helium, hydrogen (H2), and carbon dioxide (CO2) gases were used at flow rates of 1.25 - 0.18/0.32/500/0 – 1.07) sccm (standard cubic centimeters per minute) for the deposition of μc-SiOx:H(B) layers. By changing the CO2/SiH4 gas flow rate ratio from 0 to 6, μc-SiOx:H(B) layers with a composition of 0 ≤ x = O/Si ≤ 1 were prepared using a constant sum of SiH4 and CO2. The TMB flow and the H2 flow were kept constant within the series. For more details see Ref. [1]. The oxygen content in the films was determined using Rutherford Backscattering Spectroscopy (RBS). With RBS, the area-related atomic density of oxygen and silicon can be determined (± 2% [2]), and thus x can be calculated. This quantity considers only the number of silicon / oxygen atoms and not the number of atoms of other elements, such as hydrogen, which is also incorporated to a considerable extent: up to 20% in μc-SiOx:H (measured using the hydrogen effusion method). To avoid charging effects, the measurements were performed on films deposited on a substrate of mono-crystalline silicon wafers. The electrical conductivity was measured in the planar direction of the film in a vacuum cryostat, using voltages from - 100 V to + 100 V. For that two co-planar Ag contacts were evaporated on the film with a gap of 0.5 mm 5 mm. In the present study, the optical band E04 is arbitrarily used as a measure for the optical band gap. E04 is defined by the photon energy E for which an optical absorption coefficient of α of 104cm-1 is obtained. The absorption coefficient α(λ) versus the wavelength λ of the films was determined by measuring the transmittance T(λ) and reflectance R(λ), using the Beer-Lambert law, as suggested by Ref. [3]. The film thickness d was measured using the step profiler close to the measurement spot of the spectrophotometer. It is important to measure the transmittance T(λ) and the reflectance R(λ) at the same spot on the sample, to avoid inaccuracies in the calculated absorption spectra that arise from non-uniformity of the film thickness and different positions of the reflectance and transmittance minima and maxima in the spectrum [4]. Hard X-ray photoelectron spectroscopy (HAXPES) experiments were conducted at the HiKE end-station [5] on the KMC-1 beamline [6] of the BESSY-II electron storage ring. This end-station is equipped with a Scienta R4000 electron energy analyzer capable of measuring photoelectron kinetic energies up to 10 keV. A pass energy of 200 eV was used for all measurements. Spectra were recorded with a photon energy of 2003 eV using the first and fourth order supplied by a Si(111) double crystal monochromator. The combined analyzer plus beamline resolution is approx. 0.25 eV for spectra taken at both photon energies. The top surface of the sample was electrically grounded for all measurements. The binding energy was calibrated by measuring the 4f spectrum of a grounded Au foil and setting the Au 4f7/2 binding energy equal to 84.00 eV. In SiO2, the inelastic mean free path of electrons was estimated to be approx. 5 and 13-16 nm for the core levels and valence band measurements performed with 2003 and 8012 eV [7]. © (2014) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only
Potassium Postdeposition Treatment Induced Band Gap Widening at Cu In,Ga Se2 Surfaces Reason for Performance Leap?
Direct and inverse photoemission
were used to study the impact
of alkali fluoride postdeposition treatments on the chemical and electronic
surface structure of CuÂ(In,Ga)ÂSe<sub>2</sub> (CIGSe) thin films used
for high-efficiency flexible solar cells. We find a large surface
band gap (E<sub>g</sub><sup>Surf</sup>, up to 2.52 eV) for a NaF/KF-postdeposition
treated (PDT) absorber significantly increases compared to the CIGSe
bulk band gap and to the E<sub>g</sub><sup>Surf</sup> of 1.61 eV found
for an absorber treated with NaF only. Both the valence band maximum
(VBM) and the conduction band minimum shift away from the Fermi level.
Depth-dependent photoemission measurements reveal that the VBM decreases
with increasing surface sensitivity for both samples; this effect
is more pronounced for the NaF/KF-PDT CIGSe sample. The observed electronic
structure changes can be linked to the recent breakthroughs in CIGSe
device efficiencies