A novel nanoindentation protocol to characterize surface free energy of superhydrophobic nanopatterned materials
Abstract
Surface Free Energy (SFE) has become a relevant design parameter to produce materials and devices with controlled wettability. The non-destructive measurement of SFE in nanopatterned super-hydrophobic hard surfaces is a challenge in both research and industry since in most cases time-consuming contact angle measurements are not feasible. In this work, we present a novel nanoindentation based method for the measurement of pull-off adhesive forces by carefully controlling environmental and instrumentation issues. The method is found to measure SFE over five orders of magnitude, covering hydrophilic to super-hydrophobic surfaces, and has been validated with contact angle measurements. Its limitations and shortcomings are critically discussed, with a specific focus on the experimental issues that could affect the reliability and reproducibility of the results. Finally, the potential applications of the newly developed methodology include fast non-destructive mapping of SFE over heterogeneous surfaces with spatially controlled wettability.
Graphic abstrac
Investigation of the thermal expansion and heat capacity of the CaCu3Ti4O12 ceramics
The thermal expansion of the CaCu3Ti4O12 ceramics has been measured over a wide temperature
range 120–1200 K. The high quality of the samples under study has been confirmed by good agreement of
the results of measurements of the heat capacity in the range 2–300 K and in the vicinity of the phase transition of magnetic nature at 25 K with the data for the single crystal. No anomalies in the thermal expansion
that can be associated with the phase transition at 726–732 K assumed by other investigators have been found.
The influence exerted on the thermal expansion by the heat treatment of the sample in a helium atmosphere
and in air has been investigated
Origin of colossal permittivity in BaTiO3 via broadband dielectric spectroscopy
Barium titanate (BT) ceramics with Ba/Ti ratios of 0.95 and 1.00 were synthesized using spark plasma sintering (SPS) technique. Dielectric spectroscopy (frequency range from 40 Hz to 1MHz and temperature range from 300K to 30K) was performed on those ceramics (SPS BT). SPS BT showed extremely high permittivity up to ~10⁵, can be referred to as colossal permittivity, with relatively low dielectric loss of ~0.05. Data analyses following Debye relaxation and universal dielectric response models indicate that the origin of colossal permittivity in BT ceramics is the result of a hopping polaron within semiconducting grains in combination with interfacial polarization at the insulating grain boundary. Furthermore, the contributions of each polarization mechanism to the colossal permittivity in SPS BT, such as a hopping polarization, internal barrier layer capacitance effect, and electrode effect, were estimated
Synthesis, thermogravimetric and high temperature X-ray diffraction analyses of zinc-substituted nickel manganites
Stoichiometric spinel phases Mn2.352xNi0.65ZnxO4 were prepared by thermal decomposition of mixed oxalate precursor powders Mn0.782aNi0.22ZnaC2O4znH2O (with 0 # a # 0.53) at 900°C. Cation-deficient phases Mn2.352xNi0.65Znxh3d/4O41d were identified in the temperature range 350–500°C. The nonstoichiometric coefficient d was found to strongly depend on the zinc content and the decomposition temperature. We showed that the introduction of zinc into the spinel phase enlarges the stability domain of the structure and inhibits oxidation at least up to 900°C. A cubic single-phase was observed for x # 1.00. The lattice parameter variation of the oxides in the composition range 0 # x # 0.60 can be explained using Poix’s method, in terms of the distribution of Zn21 cations on the tetrahedral sites. However, for higher zinc content (x . 0.6) a detailed analysis of data showed that a small fraction of Zn21 is located on octahedral sites
Cation distribution in manganese cobaltite spinels Co3−xMnxO4 (0 ≤ x ≤ 1) determined by thermal analysis
Thermogravimetric analysis was used in order to study the reduction in air of submicronic powders of Co3−x Mn x O4 spinels, with 0 ≤ x ≤ 1. For x = 0 (i.e. Co3O4), cation reduction occurred in a single step. It involved the CoIII ions at the octahedral sites, which were reduced to Co2+ on producing CoO. For 0 < x ≤ 1, the reduction occurred in two stages at increasing temperature with increasing amounts of manganese. The first step corresponded to the reduction of octahedral CoIII ions and the second was attributed to the reduction of octahedral Mn4+ ions to Mn3+. From the individual weight losses and the electrical neutrality of the lattice, the CoIII and Mn4+ ion concentrations were calculated. The distribution of cobalt and manganese ions present on each crystallographic site of the spinel was determined. In contrast to most previous studies that took into account either CoIII and Mn3+ or Co2+, CoIII and Mn4+ only, our thermal analysis study showed that Co2+/CoIII and Mn3+/Mn4+ pairs occupy the octahedral sites. These results were used to explain the resistivity measurements carried out on dense ceramics prepared from our powders sintered at low temperature (700–750 °C) in a Spark Plasma Sintering apparatus
Crack Bridging Mechanism for Glass Strengthening by Organosilane Water-Based Coatings
We used an epoxysilane/aminosilane coating deposited from an aqueous solution
to strengthen flat glass. We studied film formation, interfacial and mechanical
properties of the film. The film is highly cross-linked with a 6 GPa Young's
modulus and good adhesion. Our results suggest that crack face bridging
accounts for most of the 75 % reinforcement in this system
Trypan Blue Dye Enters Viable Cells Incubated with the Pore-Forming Toxin HlyII of Bacillus cereus
Trypan blue is a dye that has been widely used for selective staining of dead tissues or cells. Here, we show that the pore-forming toxin HlyII of Bacillus cereus allows trypan blue staining of macrophage cells, despite the cells remaining viable and metabolically active. These findings suggest that the dye enters viable cells through the pores. To our knowledge, this is the first demonstration that trypan blue may enter viable cells. Consequently, the use of trypan blue staining as a marker of vital status should be interpreted with caution. The blue coloration does not necessarily indicate cell lysis, but may rather indicate pore formation in the cell membranes and more generally increased membrane permeability
- …