Development and study of chemical vapor deposited tantalum base alloys

A technique for the chemical vapor deposition of alloys was developed. The process, termed pulsing, involves the periodic injection of reactant gases into a previously-evacuated reaction chamber where they blanket the substrate almost instantaneously. Formation of alternating layers of the alloy components and subsequent homogenization allows the formation of an alloy of uniform composition with the composition being determined by the duration and relative numbers of the various cycles. The technique has been utilized to produce dense alloys of uniform thickness and composition (Ta- 10 wt % W) by depositing alternating layers of Ta and W by the hydrogen reduction of TaCl5 and WCl6. A similar attempt to deposit a Ta - 8 wt % W - 2 wt% Hf alloy was unsuccessful because of the difficulty in reducing HfCl4 at temperatures below those at which gas phase nucleation of Ta and W occurred

Small changes in particle-size distribution dramatically delay and enhance nucleation in hard sphere colloidal suspensions

We present hard-sphere crystallization kinetics for three samples with small differences in polydispersity. We show that an increase in polydispersity of 1% is sufficient to cause dramatic changes in the crystallization kinetics: Crystallization is delayed by almost one decade in time and quantitative and qualitative changes in the crystallization scenario are observed. Surprisingly the nucleation rate density is enhanced by almost a factor of 10. We interpret these results in terms of polydispersity limited growth, where local fractionation processes lead to a delayed but faster nucleation

Crystallization of hard-sphere colloids: deviations from classical nucleation theory

The creation of three-dimensional ordered colloidal crystals, for application in a range of nanotechnologies, has been a goal for many researchers in the past few years. The main difficulty in creating macroscopic sized crystals of densely packed colloidal particles is that colloidal particles always have a range of particle sizes - ie, they are polydisperse. This paper studied the crystallization kinetics of a hard-sphere colloid with a well defined Gaussian polydispersity. The authors find that crystallization occurs in two stages, and does not follow the simple classical nucleation picture. The paper discusses the implications of these results for research into colloidal crystals as possible nano-materials

Effect of polydispersity on the crystallization kinetics of suspensions of colloidal hard spheres when approaching the glass transition

We present a comprehensive study of the solidification scenario in suspensions of colloidal hard spheres for three polydispersities between 4.8% and 5.8%, over a range of volume fractions from near freezing to near the glass transition. From these results, we identify four stages in the crystallization process: (i) an induction stage where large numbers of precursor structures are observed, (ii) a conversion stage as precursors are converted to close packed structures, (iii) a nucleation stage, and (iv) a ripening stage. It is found that the behavior is qualitatively different for volume fractions below or above the melting volume fraction. The main effect of increasing polydispersity is to increase the duration of the induction stage, due to the requirement for local fractionation of particles of larger or smaller than average size. Near the glass transition, the nucleation process is entirely frustrated, and the sample is locked into a compressed crystal precursor structure. Interestingly, neither polydispersity nor volume fraction significantly influences the precursor stage, suggesting that the crystal precursors are present in all solidifying samples. We speculate that these precursors are related to the dynamical heterogeneities observed in a number of dynamical studies

Dynamics of hard-sphere suspension using Dynamic Light Scattering and X-Ray Photon Correlation Spectroscopy: dynamics and scaling of the Intermediate Scattering Function

Intermediate Scattering Functions (ISF's) are measured for colloidal hard sphere systems using both Dynamic Light Scattering (DLS) and X-ray Photon Correlation Spectroscopy (XPCS). We compare the techniques, and discuss the advantages and disadvantages of each. Both techniques agree in the overlapping range of scattering vectors. We investigate the scaling behaviour found by Segre and Pusey [1] but challenged by Lurio et al. [2]. We observe a scaling behaviour over several decades in time but not in the long time regime. Moreover, we do not observe long time diffusive regimes at scattering vectors away from the peak of the structure factor and so question the existence of a long time diffusion coefficients at these scattering vectors.Comment: 21 pages, 11 figure

Preparation and characterization of particles with small differences in polydispersity

Colloidal particles are widely used both in fundamental research and in materials science. One important parameter influencing the physical properties of colloidal materials is the particle size distribution (polydispersity) of the colloidal particles. Recent work on colloidal crystallization has demonstrated that even subtle changes in polydispersity can have significant effects. In this study we present centrifugation techniques for subtly manipulating the width and the shape of the particle size distribution, for polydispersities less than 10%. We use scanning electron microscopy as well as dynamic and static light scattering to characterize the particle size distributions. We compare the results and highlight the difficulties associated with the determination of accurate particle size distributions