The Effect of Ultrasonic Excitation on the Electrical Properties and Microstructure of Printed Electronic Conductive Inks

Abstract: Ultrasonic Additive Manufacturing (UAM) is an advanced manufacturing technique, which enables the embedding of electronic components and interconnections within solid aluminium structures, due to the low temperature encountered during material bonding. In this study, the effects of ultrasonic excitation, caused by the UAM process, on the electrical properties and the microstructure of thermally cured screen printed silver conductive inks were investigated. The electrical resistance and the dimensions of the samples were measured and compared before and after the ultrasonic excitation. The microstructure of excited and unexcited samples was examined using combined Focused Ion Beam and Scanning Electron Microscopy (FIB/SEM) and optical microscopy. The results showed an increase in the resistivity of the silver tracks after the ultrasonic excitation, which was correlated with a change in the microstructure: the size of the silver particles increased after the excitation, suggesting that inter-particle bonding has occurred. The study also highlighted issues with short circuiting between the conductive tracks and the aluminium substrate, which were attributed to the properties of the insulating layer and the inherent roughness of the UAM substrate. However, the reduction in conductivity and observed short circuiting were sufficiently small and rare, which leads to the conclusion that printed conductive tracks can function as interconnects in conjunction with UAM, for the fabrication of novel smart metal components

The effect of ultrasonic excitation on the electrical properties and microstructure of printed electronic conductive inks

Ultrasonic Additive Manufacturing (UAM) is an advanced manufacturing technique, which enables the embedding of electronic components and interconnections within solid aluminium structures, due to the low temperature encountered during material bonding. In this study, the effects of ultrasonic excitation, caused by the UAM process, on the electrical properties and the microstructure of thermally cured screen printed silver conductive inks were investigated. The electrical resistance and the dimensions of the samples were measured and compared before and after the ultrasonic excitation. The microstructure of excited and unexcited samples was examined using combined Focused Ion Beam and Scanning Electron Microscopy (FIB/SEM) and optical microscopy. The results showed an increase in the resistivity of the silver tracks after the ultrasonic excitation, which was correlated with a change in the microstructure: the size of the silver particles increased after the excitation, suggesting that inter-particle bonding has occurred. The study also highlighted issues with short circuiting between the conductive tracks and the aluminium substrate, which were attributed to the properties of the insulating layer and the inherent roughness of the UAM substrate. However, the reduction in conductivity and observed short circuiting were sufficiently small and rare, which leads to the conclusion that printed conductive tracks can function as interconnects in conjunction with UAM, for the fabrication of novel smart metal components

Ultrasonic Additive Manufacturing as a form-then-bond process for embedding electronic circuitry into a metal matrix

Ultrasonic Additive Manufacturing (UAM) is a hybrid manufacturing process that involves the layer-by-layer ultrasonic welding of metal foils in the solid state with periodic CNC machining to achieve the desired 3D shape. UAM enables the fabrication of metal smart structures, because it allows the embedding of various components into the metal matrix, due to the high degree of plastic metal flow and the relatively low temperatures encountered during the layer bonding process. To further the embedding capabilities of UAM, in this paper we examine the ultrasonic welding of aluminium foils with features machined prior to bonding. These pre-machined features can be stacked layer-by-layer to create pockets for the accommodation of fragile components, such as electronic circuitry, prior to encapsulation. This manufacturing approach transforms UAM into a “form-then-bond” process. By studying the deformation of aluminium foils during UAM, a statistical model was developed that allowed the prediction of the final location, dimensions and tolerances of pre-machined features for a set of UAM process parameters. The predictive power of the model was demonstrated by designing a cavity to accommodate an electronic component (i.e. a surface mount resistor) prior to its encapsulation within the metal matrix. We also further emphasised the importance of the tensioning force in the UAM process. The current work paves the way for the creation of a novel system for the fabrication of three-dimensional electronic circuits embedded into an additively manufactured complex metal composite

The effect of ultrasonic excitation on the electrical properties and microstructure of printed electronic conductive inks

Ultrasonic Additive Manufacturing (UAM) is an advanced manufacturing technique, which enables the embedding of electronic components and interconnections within solid aluminium structures, due to the low temperature encountered during material bonding. In this study, the effects of ultrasonic excitation, caused by the UAM process, on the electrical properties and the microstructure of thermally cured screen printed silver conductive inks were investigated. The electrical resistance and the dimensions of the samples were measured and compared before and after the ultrasonic excitation. The microstructure of excited and unexcited samples was examined using combined Focused Ion Beam and Scanning Electron Microscopy (FIB/SEM) and optical microscopy. The results showed an increase in the resistivity of the silver tracks after the ultrasonic excitation, which was correlated with a change in the microstructure: the size of the silver particles increased after the excitation, suggesting that inter-particle bonding has occurred. The study also highlighted issues with short circuiting between the conductive tracks and the aluminium substrate, which were attributed to the properties of the insulating layer and the inherent roughness of the UAM substrate. However, the reduction in conductivity and observed short circuiting were sufficiently small and rare, which leads to the conclusion that printed conductive tracks can function as interconnects in conjunction with UAM, for the fabrication of novel smart metal components

Ultrasonic additive manufacturing using feedstock with build-in circuitry for 3D metal embedded electronics

Embedded electronics and sensors are becoming increasingly important for the development of Industry 4.0. For small components, space constraints lead to full 3D integration requirements that are only achievable through Additive Manufacturing. Manufacturing metal components usually require high temperatures incompatible with electronics but Ultrasonic Additive Manufacturing (UAM) can produce components with mechanical properties close to bulk, but with the integration of internal embedded electronics, sensors or optics. This paper describes a novel manufacturing route for embedding electronics with 3D via connectors in an aluminium matrix. Metal foils with printed conductors and insulators were prepared separately from the UAM process thereby separating the electronics preparation from the part consolidation. A dual material polymer layer exhibited the best electrically insulating properties, while providing mechanical protection of printed conductive tracks stable up to 100 °C. General design and UAM process recommendations are given for 3D embedded electronics in a metal matrix

Exploring the mechanical strength of additively manufactured metal structures with embedded electrical materials

Ultrasonic Additive Manufacturing (UAM) enables the integration of a wide variety of components into solid metal matrices due to the process induced high degree of metal matrix plastic flow at low bulk temperatures. Exploitation of this phenomenon allows the fabrication of previously unobtainable novel engineered metal matrix components. The feasibility of directly embedding electrical materials within UAM metal matrices was investigated in this work. Three different dielectric materials were embedded into UAM fabricated aluminium metal-matrices with, research derived, optimal processing parameters. The effect of the dielectric material hardness on the final metal matrix mechanical strength after UAM processing was investigated systematically via mechanical peel testing and microscopy. It was found that when the Knoop hardness of the dielectric film was increased from 12.1 HK/0.01 kg to 27.3 HK/0.01 kg, the mechanical peel testing and linear weld density of the bond interface were enhanced by 15% and 16%, respectively, at UAM parameters of 1600 N weld force, 25 µm sonotrode amplitude, and 20 mm/s welding speed. This work uniquely identified that the mechanical strength of dielectric containing UAM metal matrices improved with increasing dielectric material hardness. It was therefore concluded that any UAM metal matrix mechanical strength degradation due to dielectric embedding could be restricted by employing a dielectric material with a suitable hardness (larger than 20 HK/0.01 kg). This result is of great interest and a vital step for realising electronic containing multifunctional smart metal composites for future industrial applications

Embedding of printed electronic interconnections in additively manufactured metal components

Ultrasonic Additive Manufacturing (UAM) is an advanced hybrid manufacturing technology, which enables the embedding of electronic components and interconnections within solid metal structures, due to the low temperature/high plastic flow encountered during ultrasonic bonding. The UAM process is based on the ultrasonic metal welding of thin metal foils in a layer-by-layer fashion. This work summarises the recent advances made towards the integration of UAM with printed electronics and other advanced manufacturing technologies for the encapsulation of conductive tracks between the interfaces of the welded foils. Two different approaches were followed: Screen printing was utilized in the first approach, for the deposition of an insulating polymer layer and silver-loaded conductive adhesive tracks on the surface of an aluminium substrate prepared with UAM. In the second approach, the aluminium foils were surface modified prior to welding, in order to selectively create an insulating ceramic layer directly onto the foil surface. These modified foils were bonded using UAM and a syringe system was used for the dispensing of the silver conductive tracks. The effectiveness and advantages of each of these two methodologies are illustrated and commented upon. The results of this ongoing research project are promising and showcase the successful integration of advanced manufacturing technologies for the fabrication of intricate metal structural electronic components

The effect of ultrasonic additive manufacturing on integrated printed electronic conductors

Ultrasonic additive manufacturing (UAM) is a low temperature manufacturing method capable of embedding printed electronics in metal components. The effect of UAM processing on the resistivity of conductive tracks printed with five different conductive pastes based on silver, copper or carbon flakes/particles in either a thermoplastic or thermoset filler binder are investigated. For all but the carbon-based paste, the resistivity changed linearly with the UAM energy input. After UAM processing, a resistivity increase of more than 150 times was recorded for the copper based thermoset paste. The silver based pastes showed a resistivity increase of between 1.1 and 50 times from their initial values. The carbon-based paste showed no change in resistivity after UAM processing. Focussed Ion Beam (FIB) microstructure analysis of the printed conductive tracks before and after UAM processing showed that the silver particles and flakes in at least one of the pastes partly dislodged from their thermoset filler creating voids, thereby increasing the resistivity, whereas the silver flakes in a thermoplastic filler did not dislodge due to material flow of the polymer binder. The lowest resistivity (8·10-5 Ω-cm) after UAM processing was achieved for a thermoplastic paste with silver flakes at low UAM processing energy

Ultrasonic additive manufacturing as a form-then-bond process for embedding electronic circuitry into a metal matrix

Ultrasonic Additive Manufacturing (UAM) is a hybrid manufacturing process that involves the layer-by-layer ultrasonic welding of metal foils in the solid state with periodic CNC machining to achieve the desired 3D shape. UAM enables the fabrication of metal smart structures, because it allows the embedding of various components into the metal matrix, due to the high degree of plastic metal flow and the relatively low temperatures encountered during the layer bonding process. To further the embedding capabilities of UAM, in this paper we examine the ultrasonic welding of aluminium foils with features machined prior to bonding. These pre-machined features can be stacked layer-by-layer to create pockets for the accommodation of fragile components, such as electronic circuitry, prior to encapsulation. This manufacturing approach transforms UAM into a “form-then-bond” process. By studying the deformation of aluminium foils during UAM, a statistical model was developed that allowed the prediction of the final location, dimensions and tolerances of pre-machined features for a set of UAM process parameters. The predictive power of the model was demonstrated by designing a cavity to accommodate an electronic component (i.e. a surface mount resistor) prior to its encapsulation within the metal matrix. We also further emphasised the importance of the tensioning force in the UAM process. The current work paves the way for the creation of a novel system for the fabrication of three-dimensional electronic circuits embedded into an additively manufactured complex metal composite

Selectively anodised aluminium foils as an insulating layer for embedding electronic circuitry in a metal matrix via ultrasonic additive manufacturing

Ultrasonic Additive Manufacturing (UAM) is a hybrid Additive Manufacturing (AM) process that involves layer-by-layer ultrasonic welding of metal foils and periodic machining to achieve the desired shape. Prior investigative research has demonstrated the potential of UAM for the embedding of electronic circuits inside a metal matrix. In this paper, a new approach for the fabrication of an insulating layer between an aluminium (Al) matrix and embedded electronic interconnections is presented. First, an Anodic Aluminium Oxide (AAO) layer is selectively grown onto the surface of Al foils prior to bonding. The pre-treated foils are then welded onto a UAM fabricated aluminium substrate. The bonding step can be repeated for the full encapsulation of the electronic interconnections or components. This ceramic AAO insulating layer provides several advantages over the alternative organic materials used in previous works