An investigation of the thermal stability of an Mg-Dy alloy after processing by high-pressure torsion
An Mg-0.41Dy (wt%) alloy was successfully processed by high-pressure tension (HPT) through 5 turns at room temperature. The evolution of the recrystallization microstructure and the texture and mechanical properties of the deformed alloy were investigated after annealing at 200 and 400 °C for 1 h using Electron Backscatter Diffraction (EBSD) and Vickers measurements. The recrystallization temperature and activation energy were evaluated using Differential Scanning Calorimetry (DSC). Processing by HPT led to significant grain refinement with an average grain size of ~0.5 ± 0.1 μm which increased to ~1.2 ± 0.8 μm after annealing at 400 °C. This slow increase in grain size at a high temperature demonstrates a good thermal stability of the microstructure. The alloy exhibited two main fiber textures after HPT processing: firstly a typical basal fiber (φ1 = 0–360°, Φ = 0° and φ2 = 0–60°) and secondly a fiber localized at φ1 = 180°, Φ = 60° and φ2 = 0–90°. These textures were retained after annealing at 400 °C. There was no change in the microhardness value after annealing at 200 °C (41 ± 1 Hv) and only a minor decrease after annealing at 400 °C (38.4 ± 0.5 Hv). The DSC results showed that the temperature associated with the recrystallization process increased with increasing heating rate and the activation energy for recrystallization was measured as ~25 kJ mol−1
Recrystallization in an Mg-Nd alloy processed by high-pressure torsion: a calorimetric analysis
Differential scanning calorimetry (DSC) was used to evaluate the recrystallization temperature and activation energy for an Mg-1.43Nd (wt.%) alloy after severe plastic deformation by high-pressure torsion (HPT) at room temperature up to 10 turns. The recrystallization kinetics were determined from DSC analysis. The results show that the recrystallization temperature increases with increasing heating rate and decreases with increasing numbers of HPT turns. Severe plastic deformation by HPT significantly reduces the recrystallization temperature. The estimated activation energy for recrystallization was in the range of ~ 84-89 kJ mol-1
On the groove pressing of Ni-W alloy: microstructure, texture and mechanical properties evolution
International audienceThe microstructure, texture and mechanical properties of the Ni-14%W(wt.%) alloy with two different initial grain sizes and textures were investigated after groove pressing (GP) at 450 °C to 4 cycles using Electron Back Scatter Diffraction (EBSD) and microhardness measurements. The initial first series was characterized by small equiaxed grains and Cube dominant texture component. The second series has elongated grains and β-fiber texture. EBSD analysis has shown that GP processing led to a slight refinement (less than 15%) of equiaxed grains in series I while greater refinement (~55%) of the mean spacing along normal direction was observed in series II. The texture did not drastically change from the initial ones and was characterized by the weakening of the Cube component in series I and rapid decrease of Copper component for series II. GP processing reduces very slightly the plastic anisotropy of the alloy with initial elongated granular microstructure
Poopćenje analitičkih izraza za pseudo -voigtovu funkciju koja se rabi u analizama difrakcijskih vrhova
Nous revisitons ici la théorie, utilisée en analyse des profils de raies de diffraction des rayons X et des neutrons, relative à la fonction de forme du pic dite de pseudo -Voigt (notée pV). Nous présentons une généralisation des expressions de la largeur intégrale et à mi-hauteur de la fonction pV, de la transformée de Fourier de cette fonction ainsi que du seuil du paramètre de mélange h. Nous incorporons nos résultats dans la procédure de fit, ce qui améliore les facteurs de précision.Razmatramo teoriju koja se primjenjuje u analizi linija difraktiranog rentgenskog zračenja i neutrona a odnosi se na tzv. pseudo-Voigtovu (skraćeno pV) funkciju za opis oblika vrha. Dajemo poopćenje analitičkog izraza za ukupnu širinu i širinu na pola visine vrha funkcije pV, Fourierovu transformaciju izraza, kao i prag parametra miješanja η. Primijenjujemo naš postupak za prilagodbu i postižemo poboljšanje točnosti
Poopćenje analitičkih izraza za pseudo -voigtovu funkciju koja se rabi u analizama difrakcijskih vrhova
Nous revisitons ici la théorie, utilisée en analyse des profils de raies de diffraction des rayons X et des neutrons, relative à la fonction de forme du pic dite de pseudo -Voigt (notée pV). Nous présentons une généralisation des expressions de la largeur intégrale et à mi-hauteur de la fonction pV, de la transformée de Fourier de cette fonction ainsi que du seuil du paramètre de mélange h. Nous incorporons nos résultats dans la procédure de fit, ce qui améliore les facteurs de précision.Razmatramo teoriju koja se primjenjuje u analizi linija difraktiranog rentgenskog zračenja i neutrona a odnosi se na tzv. pseudo-Voigtovu (skraćeno pV) funkciju za opis oblika vrha. Dajemo poopćenje analitičkog izraza za ukupnu širinu i širinu na pola visine vrha funkcije pV, Fourierovu transformaciju izraza, kao i prag parametra miješanja η. Primijenjujemo naš postupak za prilagodbu i postižemo poboljšanje točnosti
Cr cluster characterization in Cu-Cr-Zr alloy after ECAP processing and aging using SANS and HAADF-STEM
International audienceThe precipitation of nano-sized Cr clusters was investigated in a commercial Cu-1Cr-0.1Zr (wt.%) alloy processed by Equal-Channel Angular Pressing (ECAP) and subsequent aging at 550 °C for 4 hours using small angle neutron scattering (SANS) measurements and high-angle annular dark-field-scanning transmission electron microscopy (HAADF-STEM). The size and volume fraction of nano-sized Cr clusters were estimated using both techniques. These parameters assessed from SANS (d~3.2 nm, Fv~1.1 %) agreed reasonably with those from HAADF-STEM (d ~2.5 nm, Fv~2.3%). Besides nano-sized Cr clusters, HAADF-STEM technique evidenced the presence of rare cuboid and spheroid sub-micronic Cr particles about 380-620 nm mean size. Both techniques did not evidence the presence of intermetallic CuxZry phases within the aging conditions
An investigation by EXAFS of local atomic structure in an Mg-Nd alloy after processing by high-pressure torsion and ageing.
The local atomic structure of an Mg-1.44Nd (wt.%) alloy was investigated after solution annealing, high-pressure torsion (HPT) processing up to 1 and 10 turns and ageing at 250 °C for 5 h using X-ray absorption fine structure (XAFS) measurements at the Nd LIII-edge. The results show that HPT processing has no effect on the atomic structure around Nd atoms compared to the unprocessed state, whereas ageing at 250 °C for 5 h induces a significant modification in the coordination number and interatomic distances around the Nd atoms. These variations are analyzed based on the correlations between precipitation, defects and atomic mobility of the chemical species
Evaluating the textural and mechanical properties of an Mg-Dy alloy processed by high-pressure torsion
Samples of an Mg-0.41Dy (wt. %) alloy were severely deformed by high-pressure torsion (HPT) at room temperature up to 15 turns and the texture, microstructure and microhardness values in the centres, mid-radial points and edges of the HPT-deformed discs were investigated using X-ray diffraction, Electron BackScatter Diffraction and Vickers microhardness measurements. The textures in the centres of discs were characterized by a typical weak basal fiber whereas at both the mid-points and edges of the discs there was a strong basal texture where the c-axis of most grains was shifted 15° away from the shear direction. An almost homogeneous ultrafine-grained structure with a grain size of about 0.75 μm was achieved after 15 HPT turns. The microhardness values in these three positions increased with increasing numbers of turns, reached a maximum and then decreased to a lower steady-state level at large strains. In addition to dislocation and grain size hardening, the results show that texture strengthening contributes significantly to the rapid increase in hardening in the early stages of deformation
Nonlinear characterization of a bistable energy harvester dynamical system
International audienceThis chapter explores the nonlinear dynamics of a piezo-magneto-elastic bistable energy device system regards the influence of external forcing parameters influence on system response. Time series, Poincaré maps, phase space trajectories, and bifurcation diagrams are employed in order to reveals system dynamics complexity and nonlinear effects, such as chaos incidence and hysteresis
- …