Catalytic Activity of Calcium Oxide From Fishbone Waste in Waste Cooking Oil Transesterification Process
Calcium oxide was obtained from waste fish bones that has been carried out systematically by decomposition at various temperatures that 800oC, 900oC and 1000oC for 4 hours. Calcium oxide from the decomposition process was characterized using XRD, FTIR, SEM EDX and SAA. The result of XRD Diffractogram showed that the crystallinity increased as the calcination temperature increased. The absorption bands in the FTIR spectra of calcium oxide from calcined waste fish bones shown at 355 cm-1 region indicated Ca–O vibration, which was reinforced by the emergence of a peak at 859 cm-1. Based on the analysis using SEM EDX, the calcined waste fish bones typically irregular particles and contained dominant calcium element. The low value of BET surface area and the total of pore volume were consistent with the adsorption measurement with SAA. The calcium oxide was applied for biodiesel synthesis from Waste cooking oil through transesterification reaction. The result of the optimization that the calcium oxide was decomposed from waste fish bones at 900oC. It exhibited best catalytic activity in the transesterification of waste cooking oil providing maximum biodiesel yield of 93% at 4% (w/v) of catalyst loading. The decomposition of biodiesel are determined by GC MS that produced methyl palmitate, methyl linoleate, methyl elaidate, methyl linoleolate, methyl stearate and methyl linolenate
Histone deacetylase adaptation in single ventricle heart disease and a young animal model of right ventricular hypertrophy.
BackgroundHistone deacetylase (HDAC) inhibitors are promising therapeutics for various forms of cardiac diseases. The purpose of this study was to assess cardiac HDAC catalytic activity and expression in children with single ventricle (SV) heart disease of right ventricular morphology, as well as in a rodent model of right ventricular hypertrophy (RVH).MethodsHomogenates of right ventricle (RV) explants from non-failing controls and children born with a SV were assayed for HDAC catalytic activity and HDAC isoform expression. Postnatal 1-day-old rat pups were placed in hypoxic conditions, and echocardiographic analysis, gene expression, HDAC catalytic activity, and isoform expression studies of the RV were performed.ResultsClass I, IIa, and IIb HDAC catalytic activity and protein expression were elevated in the hearts of children born with a SV. Hypoxic neonatal rats demonstrated RVH, abnormal gene expression, elevated class I and class IIb HDAC catalytic activity, and protein expression in the RV compared with those in the control.ConclusionsThese data suggest that myocardial HDAC adaptations occur in the SV heart and could represent a novel therapeutic target. Although further characterization of the hypoxic neonatal rat is needed, this animal model may be suitable for preclinical investigations of pediatric RV disease and could serve as a useful model for future mechanistic studies
Computationally designed variants of Escherichia coli chorismate mutase show altered catalytic activity
Computational protein design methods were used to predict five variants of monofunctional Escherichia coli chorismate mutase expected to maintain catalytic activity. The variants were tested experimentally and three active site mutants exhibited catalytic activity similar to or greater than the wild-type enzyme. One mutant, Ala32Ser, showed increased catalytic efficiency
Steam-Induced Coarsening of Single-Unit-Cell MFI Zeolite Nanosheets and Its Effect on External Surface Brønsted Acid Catalysis.
Commonly used methods to assess crystallinity, micro-/mesoporosity, Brønsted acid site density and distribution (in micro- vs. mesopores), and catalytic activity suggest nearly invariant structure and function for aluminosilicate zeolite MFI two-dimensional nanosheets before and after superheated steam treatment. Yet, pronounced reaction rate decrease for benzyl alcohol alkylation with mesitylene, a reaction that cannot take place in the zeolite micropores, is observed. Transmission electron microscopy images reveal pronounced changes in nanosheet thickness, aspect ratio and roughness indicating that nanosheet coarsening and the associated changes in the external (mesoporous) surface structure are responsible for the changes in the external surface catalytic activity. Superheated steam treatment of hierarchical zeolites can be used to alter nanosheet morphology and regulate external surface catalytic activity while preserving micro- and mesoporosity, and micropore reaction rates
Synthesis of an acidic biomorphic carbon-based catalyst for simultaneous esterification and transesterification reactions
The activation of cellulose followed by sulfonation produces a biomorphic functionalized carbon material with acid catalytic activity as a solid-acid replacement for homogeneous catalysts. The carbon-based material contains carboxylic and sulfonic acid groups and exhibits high catalytic performance for liquid-phase acid-catalyzed reactions in presence of water. The activation of cellulose at high temperature (600ºC) followed by sulfonation also results in an amorphous carbon with an acidity value close to 1.52 mmol.g-1. The catalytic test shows that the sulfated carbon has enough amount of sulfonic acid groups and exhibit high catalytic activity and stability for esterification and tranesterification of raw materials; achieving a comversion value close to 90.5% at 2h of reaction comparable to an homogeneous catalysts. Structural and active site analyses suggest that the marked difference in catalytic activity is due to the accessibility of reactants to sulfonic acid groups in the carbon structure.Universidad de Málaga. Campus de Excelencia Internacional Andalucía Tech
Co3O4 Nanocrystals on Graphene as a Synergistic Catalyst for Oxygen Reduction Reaction
Catalysts for oxygen reduction and evolution reactions are at the heart of
key renewable energy technologies including fuel cells and water splitting.
Despite tremendous efforts, developing oxygen electrode catalysts with high
activity at low costs remains a grand challenge. Here, we report a hybrid
material of Co3O4 nanocrystals grown on reduced graphene oxide (GO) as a
high-performance bi-functional catalyst for oxygen reduction reaction (ORR) and
oxygen evolution reaction (OER). While Co3O4 or graphene oxide alone has little
catalytic activity, their hybrid exhibits an unexpected, surprisingly high ORR
activity that is further enhanced by nitrogen-doping of graphene. The
Co3O4/N-doped graphene hybrid exhibits similar catalytic activity but superior
stability to Pt in alkaline solutions. The same hybrid is also highly active
for OER, making it a high performance non-precious metal based bi-catalyst for
both ORR and OER. The unusual catalytic activity arises from synergetic
chemical coupling effects between Co3O4 and graphene.Comment: published in Nature Material
The alpha-effect in cyclic secondary amines: new scaffolds for iminium ion accelerated transformations
Five-membered secondary amine heterocycles containing an α-heteroatom were prepared and shown to be ineffective as catalysts for the iminium ion catalysed Diels–Alder reaction between cinnamaldehyde and cyclopentadiene. Their six-membered counterparts proved to be highly active catalysts. In stark contrast, the catalytic activity observed when comparing the non α-heteroatom cyclic amines proline methyl ester and methyl pipecolinate showed the five-membered ring amine was significantly more active. Concurrent density functional theoretical calculations suggest a rationale for the observed trends in reactivity, highlighting that LUMO activation through an iminium ion intermediate plays a key role in catalytic activity
Impact of silica structure of copper and iron-containing SBA-15 and SBA-16 materials on toluene oxidation
Copper and iron modified SBA-15 and SBA-16 materials were prepared by incipient wetness impregnation technique and characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), N2 physisorption, temperature-programmed reduction (TPR-TGA), UV-Vis diffuse reflectance and Mössbauer spectroscopy. Formation of finely dispersed copper and iron-oxide species was observed on both supports, whereas copper ferrite could be evidenced only on SBA-15. It was found that the structural and surface properties of the mesoporous supports determine the type of formed metal oxides, their dispersion, reducibility and the catalytic activity in total oxidation of toluene. On SBA-16 support penetration of metal salt into the bimodal channel system is hindered therefore separate copper- and iron-oxide phases are formed on the outer surface of catalysts. The catalytic activity and stability are lower due to the easier agglomeration of particles. On SBA-15 support finely dispersed metal-oxides can be found in the mesoporous channels. Their interaction is favored to form bimetallic phases enhancing the catalytic activity and stability in total oxidation of toluene
- …