26 research outputs found
Utilization of Renewable Biomass and Waste Materials for Production of Environmentally-Friendly, Bio-based Composites
The introduction of renewable biomass into a polymer matrix is an option competing with other
possibilities, such as energy recovery and/or re-use in the carbonized state, or production of
chemicals, such as, in the case of ligno-cellulosic waste, concentrates on the production of simple
sugars, then possibly leading to the development of biopolymers. These competitive applications
have also some interest and market, however with a considerable energy, water and materials
consumption, due also to the not always high yielding. Other possibilities for renewable biomass are
therefore being used as fillers to increase mechanical performance of polymers or to allow e.g., the
absorption of toxic chemicals. This review concentrates on the use of biomass as close as possible
to the “as received” state, therefore avoiding whenever suitable any thermal treatment. More
specifically, it focuses on its introduction into the three categories of oil-based (or bio-based
replacement) of engineered polymers, into industrial biopolymers, such as poly(lactic acid) (PLA)
and self-developed biopolymers, such as thermoplastic starch (TPS)
Solid-state fermentation of oil palm frond petiole for lignin peroxidase and xylanase-rich cocktail production
In current practice, oil palm frond leaflets and stems are re-used for soil nutrient recycling, while the petioles are typically burned. Frond petioles have high commercialization value, attributed to high lignocellulose fiber content and abundant of juice containing free reducing sugars. Pressed petiole fiber is the subject of interest in this study for the production of lignocellulolytic enzyme. The initial characterization showed the combination of 0.125 mm frond particle size and 60% moisture content provided a surface area of 42.3 m2/g, porosity of 12.8%, and density of 1.2 g/cm3, which facilitated fungal solid-state fermentation. Among the several species of Aspergillus and Trichoderma tested, Aspergillus awamori MMS4 yielded the highest xylanase (109 IU/g) and cellulase (12 IU/g), while Trichoderma virens UKM1 yielded the highest lignin peroxidase (222 IU/g). Crude enzyme cocktail also contained various sugar residues, mainly glucose and xylose (0.1–0.4 g/L), from the hydrolysis of cellulose and hemicellulose. FT-IR analysis of the fermented petioles observed reduction in cellulose crystallinity (I900/1098), cellulose–lignin (I900/1511), and lignin–hemicellulose (I1511/1738) linkages. The study demonstrated successful bioconversion of chemically untreated frond petioles into lignin peroxidase and xylanase-rich enzyme cocktail under SSF condition
Preparation of cellulose nanofibers with hydrophobic surface characteristics.
The aim of this study was to develop cellulose nanofibers with hydrophobic surface characteristics using chemical modification. Kenaf fibers were modified using acetic anhydride and cellulose nanofibers were isolated from the acetylated kenaf using mechanical isolation methods. Fourier transform infrared spectroscopy (FTIR) indicated acetylation of the hydroxyl groups of cellulose. The study of the dispersion demonstrated that acetylated cellulose nanofibers formed stable, well-dispersed suspensions in both acetone and ethanol. The contact angle measurements showed that the surface characteristics of nanofibers were changed from hydrophilic to more hydrophobic when acetylated. The microscopy study showed that the acetylation caused a swelling of the kenaf fiber cell wall and that the diameters of isolated nanofibers were between 5 and 50 nm. X-ray analysis showed that the acetylation process reduced the crystallinity of the fibers, whereas mechanical isolation increased it. The method used provides a novel processing route for producing cellulose nanofibers with hydrophobic surfaces
Enhanced Capacities of Mixed Fatty Acid-Modified Sawdust Aggregators for Remediation of Crude Oil Spill
Corrosion and mechanical behaviour of biodegradable PLA-cellulose nanocomposite coating on AZ31 magnesium alloy
Chemical investigation on wood tree species in a temperate forest, east-northern Romania
A quantitative evaluation of wood chemical components for some tree species in a forest area from east-northern Romania is presented here, through a comparative study from 1964 to 2000. Investigation upon the wood tree-rings in a Quercus robur L. tree species, as a dominant species, as regards its chemical composition and structure of the natural polymer constituents - cellulose and lignin - was also performed through chemical methods to separate the main wood components, FT-IR spectroscopy, and thermogravimetry. Having in view the impact of climate and external factors (such as pollutant depositions), some possible correlations between wood chemical composition and its further use can be made. The FT-IR spectra give evidence of differences in the frequency domains of 3400-2900 cm-1 and 1730-1640 cm-1, due to some interactions between the chemical groups (OH, C=O). The crystallinity index of cellulose presents variations in the oak wood tree-rings. Thermogravimetry analyses show different behaviour of cellulose at thermal decomposition, as a function of radial growth and tree’s height. A preliminary chemical investigation of oak wood sawdust shows a relatively high content of mineral elements (ash), compared with a previous study performed in 1964, fact that may indicate an intense drying process of the oak tree, a general phenomenon present in European forests for this species
Processing of hybrid wood plastic composite reinforced with short PET fibers
Poly(ethylene terephthalate) (PET) fibers (virgin, waste, and mixed) were incorporated in the composite poly(methyl methacrylate) (PMMA)-wood. Hybrid composite panels were prepared by pressure molding. Toluene-2,4-diisocyanate (TDI) and (3-mercaptopropyl)trimethoxysilane (MPTMS) were used as cross-linking bonding agents for modification of wood fibers. Influence of cross-linking bonding agents, structure, and composition of PET fibers was examined by studying thermomechanical properties as well as moisture absorption. Moisture absorption was lower for composites with bonding agents. Mechanical testing revealed that the addition of PET fibers drastically enhances properties of the composites. Covalent and hydrogen bonds formed with the addition of bonding agents have also improved mechanical properties compared to the untreated composites