SCC modification by use of amorphous nano-silica

In this study two different types of nano-silica (nS) were applied in self-compacting concrete (SCC), both having similar particle size distributions (PSD), but produced through two different processes: fumed powder silica and precipitated silica in colloidal suspension. The influence of nano-silica on SCC was investigated with respect to the properties of concrete in fresh (workability) and hardened state (mechanical properties and durability). Additionally, the densification of the microstructure of the hardened concrete was verified by SEM and EDS analyses. The obtained results demonstrate that nano-silica efficiently used in SCC can improve its mechanical properties and durability. Considering the reactivity of the two applied nano-silicas, the colloidal type showed a higher reactivity at early age, which influenced the final SCC properties

Non-steady state chloride migration and binding in cracked self-compacting concrete

We adopted a notch method to study the influence of crack width (macro level) on chloride transport and binding of cracked concrete under a non-steady state migration test. The results show that migration coefficient of cracked concrete increases with increasing crack width up to a critical value (0.43 mm), for the whole concrete or the area close to crack; the increase of migration coefficient could be independent from crack parameter when a critical crack width is reached. For chloride binding, Langmuir isotherms of cracked concrete samples exhibit the similar decreasing trend as crack width increases from 0.27 to 1.96 mm. The increased current value could be responsible for the trend based on the hypothesis of electric force