80 research outputs found
A simple test for thermomechanical evaluation of ceramic fibers
A simple bend stress relaxation (BSR) test was developed to measure the creep related properties of ceramic fibers and whiskers. The test was applied to a variety of commercial and developmental Si based fibers to demonstrate capabilities and to evaluate the relative creep resistance of the fibers at 1200 to 1400 C. The implications of these results and the advantages of the BSR test over typical tensile creep tests are discussed
Modeling the Elastic Modulus of 2D Woven CVI SiC Composites
The use of fiber, interphase, CVI SiC minicomposites as structural elements for 2D-woven SiC fiber reinforced chemically vapor infiltrated (CVI) SiC matrix composites is demonstrated to be a viable approach to model the elastic modulus of these composite systems when tensile loaded in an orthogonal direction. The 0deg (loading direction) and 90deg (perpendicular to loading direction) oriented minicomposites as well as the open porosity and excess SiC associated with CVI SiC composites were all modeled as parallel elements using simple Rule of Mixtures techniques. Excellent agreement for a variety of 2D woven Hi-Nicalon(TradeMark) fiber-reinforced and Sylramic-iBN reinforced CVI SiC matrix composites that differed in numbers of plies, constituent content, thickness, density, and number of woven tows in either direction (i.e, balanced weaves versus unbalanced weaves) was achieved. It was found that elastic modulus was not only dependent on constituent content, but also the degree to which 90deg minicomposites carried load. This depended on the degree of interaction between 90deg and 0deg minicomposites which was quantified to some extent by composite density. The relationships developed here for elastic modulus only necessitated the knowledge of the fractional contents of fiber, interphase and CVI SiC as well as the tow size and shape. It was concluded that such relationships are fairly robust for orthogonally loaded 2D woven CVI SiC composite system and can be implemented by ceramic matrix composite component modelers and designers for modeling the local stiffness in simple or complex parts fabricated with variable constituent contents
Modeling the Stress Strain Behavior of Woven Ceramic Matrix Composites
Woven SiC fiber reinforced SiC matrix composites represent one of the most mature composite systems to date. Future components fabricated out of these woven ceramic matrix composites are expected to vary in shape, curvature, architecture, and thickness. The design of future components using woven ceramic matrix composites necessitates a modeling approach that can account for these variations which are physically controlled by local constituent contents and architecture. Research over the years supported primarily by NASA Glenn Research Center has led to the development of simple mechanistic-based models that can describe the entire stress-strain curve for composite systems fabricated with chemical vapor infiltrated matrices and melt-infiltrated matrices for a wide range of constituent content and architecture. Several examples will be presented that demonstrate the approach to modeling which incorporates a thorough understanding of the stress-dependent matrix cracking properties of the composite system
Stable Boron Nitride Interphases for Ceramic Matrix Composites
Ceramic matrix composites (CMC's) require strong fibers for good toughness and weak interphases so that cracks which are formed in the matrix debond and deflect around the fibers. If the fibers are strongly bonded to the matrix, CMC's behave like monolithic ceramics (e.g., a ceramic coffee cup), and when subjected to mechanical loads that induce cracking, such CMC's fail catastrophically. Since CMC's are being developed for high temperature corrosive environments such as the combustor liner for advanced High Speed Civil Transport aircraft, the interphases need to be able to withstand the environment when the matrix cracks
Single-Tow Minicomposite Test Used to Determine the Stressed-Oxidation Durability of SiC/SiC Composites
SiC-fiber-reinforced SiC-matrix composites are considered future materials for high temperature (less than 1200 C), air-breathing applications. For these materials to be successful, they must be able to maintain desirable mechanical properties at high temperatures while existing in highly corrosive environments. The critical constituent of a ceramic matrix composite is a thin interphase layer between the fiber and matrix which enables matrix cracks to deflect around the fibers, that is, to perform even when damaged. Unfortunately, the only interphase materials (to date) that offer the desired properties are carbon and boron nitride. Both of these materials react with oxidizing environments to form gaseous or liquid oxidation products that can lead to fiber-strength degradation or strong bonding between the fiber and the matrix at temperatures above approx. 600 C
Stressed-Oxidation Lifetime of Different SiC Fiber, CVI Matrix SiC Minicomposites in Air
The stressed-oxidation lifetime properties of several minicomposites composed of single fiber tows with a CVI SiC matrix were compared. The minicomposites were made up of Nicalon(Tm) and Hi-Nicalon(Tm) SiC fibers with carbon or BN interphases. Constant load stress-rupture tests were performed between 600 and 13000 C in air for all of the minicomposite systems. Cyclic load testing was performed on the Hi-Nicalon minicomposite systems. The factors controlling the different lifetime behaviors: fiber rupture properties, interphase oxidation, fiber degradation, and fiber-matrix bonding, are discussed in light of different minicomposite constituents. All of the systems were subject to intermediate temperature embrittlement. The Hi-Nicalon fiber, BN interphase system, performed the best for constant load conditions. For cyclic load conditions, both the BN- interphase and C-interphase minicomposites displayed poor, but different failure behavior
Advanced Woven SiC/SiC Composites for High Temperature Applications
The temperature, stress, and environmental conditions of many gas turbine, hypersonic, and even nuclear applications make the use of woven SiC/SiC composites an attractive enabling material system. The development in SiC/SiC composites over the past few years has resulted in significant advances in high temperature performance so that now these materials are being pursued for several turbine airfoil and reusable hypersonic applications. The keys to maximizing stress capability and maximizing temperature capability will be outlined for SiC/SiC. These include the type of SiC fiber, the fiber-architecture, and the matrix processing approach which leads to a variety of matrix compositions and structure. It will also be shown that a range of mechanical, thermal, and permeability properties can be attained and tailored depending on the needs of an application. Finally, some of the remaining challenges will be discussed in order for the use of these composite systems to be fully realized
SiC/SiC Composites: The Effect of Fiber Type and Fiber Architecture on Mechanical Properties
Woven SiC/SiC composites represent a broad family of composites with a broad range of properties which are of interest for many energy-based and aero-based applications. Two important features of SiC/SiC composites which one must consider are the reinforcing fibers themselves and the fiber-architecture they are formed into. The range of choices for these two features can result in a wide range of elastic, mechanical, thermal, and electrical properties. In this presentation, it will be demonstrated how the effect of fiber-type and fiber architecture effects the important property of "matrix cracking stress" for slurry-cast melt-infiltrated SiC matrix composites, which is often considered to be a critical design parameter for this system of composites
Design Guidelines for In-Plane Mechanical Properties of SiC Fiber-Reinforced Melt-Infiltrated SiC Composites
In-plane tensile stress-strain, tensile creep, and after-creep retained tensile properties of melt-infiltrated SiC-SiC composites reinforced with different fiber types were evaluated with an emphasis on obtaining simple or first-order microstructural design guidelines for these in-plane mechanical properties. Using the mini-matrix approach to model stress-strain behavior and the results of this study, three basic general design criteria for stress and strain limits are formulated, namely a design stress limit, a design total strain limit, and an after-creep design retained strength limit. It is shown that these criteria can be useful for designing components for high temperature applications
Creep and stress relaxation modeling of polycrystalline ceramic fibers
A variety of high performance polycrystalline ceramic fibers are currently being considered as reinforcement for high temperature ceramic matrix composites. However, under mechanical loading about 800 C, these fibers display creep related instabilities which can result in detrimental changes in composite dimensions, strength, and internal stress distributions. As a first step toward understanding these effects, this study examines the validity of a mechanism-based empirical model which describes primary stage tensile creep and stress relaxation of polycrystalline ceramic fibers as independent functions of time, temperature, and applied stress or strain. To verify these functional dependencies, a simple bend test is used to measure stress relaxation for four types of commercial ceramic fibers for which direct tensile creep data are available. These fibers include both nonoxide (SCS-6, Nicalon) and oxide (PRD-166, FP) compositions. The results of the Bend Stress Relaxation (BSR) test not only confirm the stress, time, and temperature dependencies predicted by the model, but also allow measurement of model empirical parameters for the four fiber types. In addition, comparison of model tensile creep predictions based on the BSR test results with the literature data show good agreement, supporting both the predictive capability of the model and the use of the BSR text as a simple method for parameter determination for other fibers
- …