Modification of Rice Husk-Based Activated Carbon using Sodium Lauryl Sulfat (SLS) for Lead (Pb) Ions Removal

A rice husk-based active carbon modified using SLS surfactant showed an increase on Pb ionic metal removal with the efficiency of 99.96%. Activated carbon is commonly applied as adsorben in waste water treatment, in particularly, waste water containing heavy metals and dye molecules. Even though it is commonly used, the adsorption efficiency of activated carbon to the heavy metal waste is still low. Therefore, in the present work, carbon from rice husk was modified using surfactant which further it is called surfactant modified active carbon (SMAC). Firstly, rice husk-based carbon was activated using 40% H3PO4 for 2, 6, 10, 14, 15 and 16 hours. The activated carbon was then modified by contacting it into SLS in different concentration 10, 20, 30, 40, 50, 60 and 70 ppm for 5 hours. Finally, the SMAC was then applied to remove Pb ionic metal. Moreover, several characterisation techniques were performed including FTIR, SEM, UV-Vis and AAS. Keywords: activated carbon, surfactant-modified active carbon, adsorption, rice hus

Synthesis of Rice Husk-Based Zeolit using Hydrothermal Method and Its Detergent Builder Properties

Detergents are cleaning agents that consist of a complex formulation such as surfactants, builders, bleaching, fillers and other additives. Detergent builder that commonly used is sodium tripolyphosphate (STPP) that are unfriendly environmentally. One of the detergent builders that is more environmentally friendly is zeolite. Therefore, in the present work, zeolite was synthesized using hydrothermal method by varying the temperature and characterised its detergent builder properties. Zeolite was synthesized by mixing sodium silicate (Na2SiO3) and sodium aluminate NaAl(OH)4 with the presence of NaOH. Firstly, a mixture of sodium silicate and sodium aluminate formed sol and gradually become gel. After that, the gel had been treated by hydothermal for 7 hours at different temperatures: 500C, 1000C and 1500C. Several characteristic techniques such as FTIR and XRD were applied to identify functional group and the crystal structure, respectively. Furthermore, the detergent builder properties were characterised using cation exchange capacity (CEC) and detergency test. The result showed that zeolite synthesized at 100 0C gave better washing capability than others

Synthesis of Rice Husk-Based Zeolit using Hydrothermal Method and Its Detergent Builder Properties

Detergents are cleaning agents that consist of a complex formulation such as surfactants, builders, bleaching, fillers and other additives. Detergent builder that commonly used is sodium tripolyphosphate (STPP) that are unfriendly environmentally. One of the detergent builders that is more environmentally friendly is zeolite. Therefore, in the present work, zeolite was synthesized using hydrothermal method by varying the temperature and characterised its detergent builder properties. Zeolite was synthesized by mixing sodium silicate (Na2SiO3) and sodium aluminate NaAl(OH)4 with the presence of NaOH. Firstly, a mixture of sodium silicate and sodium aluminate formed sol and gradually become gel. After that, the gel had been treated by hydothermal for 7 hours at different temperatures: 500C, 1000C and 1500C. Several characteristic techniques such as FTIR and XRD were applied to identify functional group and the crystal structure, respectively. Furthermore, the detergent builder properties were characterised using cation exchange capacity (CEC) and detergency test. The result showed that zeolite synthesized at 100 0C gave better washing capability than others

Modification of Rice Husk-Based Activated Carbon using Sodium Lauryl Sulfat (SLS) for Lead (Pb) Ions Removal

A rice husk-based active carbon modified using SLS surfactant showed an increase on Pb ionic metal removal with the efficiency of 99.96%. Activated carbon is commonly applied as adsorben in waste water treatment, in particularly, waste water containing heavy metals and dye molecules. Even though it is commonly used, the adsorption efficiency of activated carbon to the heavy metal waste is still low. Therefore, in the present work, carbon from rice husk was modified using surfactant which further it is called surfactant modified active carbon (SMAC). Firstly, rice husk-based carbon was activated using 40% H3PO4 for 2, 6, 10, 14, 15 and 16 hours. The activated carbon was then modified by contacting it into SLS in different concentration 10, 20, 30, 40, 50, 60 and 70 ppm for 5 hours. Finally, the SMAC was then applied to remove Pb ionic metal. Moreover, several characterisation techniques were performed including FTIR, SEM, UV-Vis and AAS

Media pembelajaran video produk kreatif dalam pembuatan softcase laptop produk kreatif di era pandemi covid-19

ABSTRAK: Penggunaan media dalam proses pembelajaran dapat membangkitkan keinginan-keinginan dan minat yang baru, membangkitkan motivasi, dan rangsangan kegiatan belajar, bahkan membawa pengaruh-pengaruh psikologis terhadap siswa. Berkenaan dengan penyebaran Coronavirus Disease (covid 19) yang semakin meningkat maka kesehatan seluruh warga sekolah menjadi pertimbangan utama dalam pelaksanaan pembelajaran khususnya mengenai media pembelajaran secara daring. Dengan demikian, siswa harus punya pendamping belajar, hal ini terjadi karena nilai KKM siswa di sekolah minim. Terutama masalah pelajaran kewirausahaan siswa sebagian belum ada keinginan untuk berwirausaha. Dengan wujud media video tutorial ini dapat tumbuh imajinasi kreatifitas dari setiap siswa terkait wirausaha produk kreatif.  Salah satu media yang dapat dimanfaatkan peserta didik untuk belajar mandiri adalah menggunakan media video produk kreatif wadah laptop. Penggunaan video   sebagai media belajar dapat membuat peran guru ke arah yang lebih positif dan produktif. Guru dapat berbagi peran dengan media sehingga memiliki banyak waktu untuk memberi perhatian pada aspek-aspek edukatif lainnya, seperti membantu kesulitan belajar siswa, pembentukan kepribadian, memotivasi belajar, dan lain-lain

The Effect of White Turmeric Extract (Curcuma Zedoaria) and Lactobacillus sp Herbal Mixture as Feed Additive on Animal Productivity

This study was conducted to determine the effect of herbal white turmeric extract (Curcuma zedoaria) with Lactobaccilus sp on the productivity of livestock. The test subjects within this study are 50 broiler chickens aged 0 days which were divided equally into two observation groups, namely the control group (A) and the treated group (B). The treatments are carried out as follows: A = no animal herbal mixture was added into the drinking water; B = drinking water was added with herbal mixture. Average body weight of the chickens were (A) 460 g and (B) 484 g, the feed conversion ratio values for chicken aged 6 and 13 days respectively are 0.696 (A); 0.644 (B) and 1.25 (A); 1.18 (B), while the performance index value (IP) of broiler chickens aged 6 and 13 days were 335 (A); 390 (B) and 272 (A); 315 (B), consecutively. In this study the addition of herb as feed additives into broiler chicken drinking water can increase the average body weight of the treatment group compared to the control group, the treatment group has a lower FCR value indicating good feed efficiency and IP values ​​above 300 implying good breeding process

Pembuatan Karbon Aktif Termodifikasi Surfaktan Sodium Lauryl Sulphate (SMAC-SLS) dari Tempurung Kelapa Menggunakan Aktivator ZnCl2 dan Gelombang Mikro Sebagai Adsorben Kation Pb(II)

Penelitian tentang modifikasi karbon aktif tempurung kelapa dengan surfaktan sodium lauryl sulphate (SLS) telah dilakukan sebagai adsorben logam Pb(II). Penelitian ini bertujuan untuk membuat material baru Surfactant Modificated Activated Carbon (SMAC) dari tempurung kelapa yang lebih unggul dari karbon aktif untuk adsorben logam Pb(II).  Penelitian ini terdiri dari beberapa tahap, tahap pertama adalah  karbonisasi tempurung kelapa mengunakan pirolisis pada temperatur 400oC selama 1 jam, tahap kedua aktivasi menggunakan ZnCl2 30% dan radisasi gelombang mikro dengan daya bervariasi 80 -800 W selama waktu bervariasi 1 – 9 menit, tahap ketiga modifikasi karbon aktif menggunakan SLS 60 ppm selama 4 jam dan selanjutnya tahap aplikasi SMAC untuk adsorben logam Pb. Karakterisasi SMAC dilakukan adalah dengan FTIR, GSA, SEM dan data termodinamika. keberhasilan adsorpsi SMAC diukur dengan menentukan kapasitas adsorpsi.  Hasil modifikasi menunjukkan karbon aktif dapat mengadsorpsi SLS sebesar 1,496 mg/g. Karakterisasi SMAC  dengan FTIR menunjukkan adanya pucak S=O pada bilangan gelombang 1341 cm-1, karakterisasi dengan GSA menunjukkan luas area SMAC lebih kecil dari karbon aktif yaitu sebesar 3,924 m2/g, morfologi permukaan SMAC sebagian besar tertutup oleh surfaktan SLS dan data termodinamika memberikan nilai entalpi sebesar -10,282 kJ/mol yang menunjukkan interaksi antara karbon aktif dan SLS merupakan interaksi atau adsorpsi secara fisik. SMAC efektif mengadsorpsi logam Pb(II) dengan efisiensi sebesar 99,89% dan kapasitas sebesar 1,498 mg/g dan interaksi antara SMAC dengan kation Pb (II) merupakan interaksi elektrostatis.Kata Kunci: SMAC, Kapasitas Adsorpsi, kation P

PEMBUATAN KARBON AKTIF BERBAHAN DASAR SABUT KELAPA DENGAN AKTIVATOR H2SO4 DAN NaOH SEBAGAI ADSORBEN KATION Fe DAN Cu DALAM LIMBAH CAIR BATIK KEBUMEN

Perkembangan batik di Indonesia meningkat seiring meningkatnya volume limbah cair batik yang dihasilkan dan mengandung ion logam berat  seperti Fe dan Cu sebagai parameter pencemar lingkungan karena memiliki sifat toksisitas dan dapat terakumulasi dalam rantai makanan sampai ke organisme lainnya termasuk manusia walaupun pada konsentrasi yang sangat rendah. Telah dilakukan penelitian pembuatan karbon aktif berbahan dasar sabut kelapa dengan dengan aktivator H2SO4 (K-H) dan NaOH (K-Na) pada konsentrasi 3, 4, dan 5 N sebagai adsorben kation Fe dan Cu. Waktu kontak adsorpsi juga divariasi 1 – 60 menit. Penelitian ini bertujuan untuk menentukan efisiensi adsorpsi kation Fe dan Cu terlarut dalam limbah cair batik Kebumen serta menentukan kinetika adsorpsi. Proses adsorpsi kation Fe dan Cu dilakukan dengan metode adsorpsi secara batch menggunakan karbon aktif dari sabut kelapa Analisis kandungan kation Fe dan Cu dilakukan menggunakan AAS. Konsentrasi kation Fe dan Cu sebelum adsorpsi masing-masing sebesar 27.27 ppm dan 25.42 ppm. Hasil penelitian menunjukkan bahwa sampel K-H 3 dan K-Na 4 merupakan karbon aktif terbaik.  Efisiensi adsorpsi kation Fe dan Cu menggunakan K-H 3 masing-masing sebesar 56,37% (b/b) dan 44,93% (b/b) sedangkan menggunakan K-Na 4 berturut-turut sebesar 71,54% (b/b) dan 70,89% (b/b).Waktu kontak optimum K-H 3 dan K-Na 4 adalah 30 menit untuk kation Fe dan 45 menit untuk kation Cu. Model kinetika adsorpsi kation Fe dan Cu yang sesuai oleh K-H 3 dan K-Na 4 adalah pseudo orde dua

Review: Senyawa Kimia dalam Sambiloto (Andrographis Paniculata)

Latar Belakang: Masyarakat Indonesia telah memanfaatkan bahan alam terutama tumbuhan secara turun temurun sebagai obat tradisional untuk mengatasi berbagai penyakit. Khasiat penyembuhan tumbuhan obat disebabkan senyawa bioaktif yang ada di dalamnya. Identifikasi komponen bioaktif tumbuhan merupakan salah satu aspek penting dalam penemuan dan pengembangan obat baru. Tumbuhan melakukan biosintesis berbagai senyawa kimiawi yang beragam salah satunya metabolit sekunder. Berbagai kelas metabolit sekunder seperti alkaloid, terpenoid dan fenolik memiliki potensi untuk penyembuhan berbagai penyakit. Sambiloto merupakan salah satu tanaman yang memiliki potendi dimanfaatkan untuk pengobatan penyakit. Salah satu senyawa bioaktif dalam sambiloto yaitu andrographolide merupakan agen kemoterapi yang potensial. Telah banyak dilakukan review mengenai sambiloto tetapi lebih terfokus pada aspek farmakologis tanaman ini. Hanya sedikit informasi yang tersedia yang membahas secara rinci mengenai senyawa metabolit sekunder yang terdapat dalam sambiloto. Review ini memberikan informasi terkini mengenai senyawa metabolit sekunder yang terkandung dalam sambiloto. Metodologi: Penelitian ini merupakan penelitian non eksperimental deskriptif yang dilakukan dengan tiga tahap. Pertama, penelusuran dan pemilihan artikel berdasarkan kriteria inklusi dan eksklusi. Kedua, ekstraksi dan sintesis artikel terpilih. Ketiga, penulisan hasil dan penarikan kesimpulan. Hasil Penelitian: Studi fitokimia pada sambiloto menuntun isolasi berbagai senyawa metabolit sekunder termasuk senyawa yang baru pertama kali ditemukan. Berdasarkan hasil isolasi, sambiloto mengandung berbagai senyawa dari golongan terpenoid yaitu monoterpenoid, diterpenoid, triterpenoid, noriridoid, iridoid dan norisoprenoid, golongan flavonoid serta golongan senyawa lain. Kesimpulan: Sambiloto mengandung berbagai senyawa metabolit sekunder yang beragam dan memiliki potensi besar untuk penemuan dan pengembangan obat baru

French Fries-Like Bismuth Oxide: Physicochemical Properties, Electrical Conductivity and Photocatalytic Activity

Bismuth oxide synthesis using hydrothermal method has been conducted. This study aims to examine the effect of the hydrothermal reaction time on product characteristics and photocatalytic activity in degrading methyl orange dye. Bismuth oxide synthesis was initiated by dissolving bismuth nitrate pentahydrate (Bi(NO3)3.5H2O) and Na2SO4 in a distilled water and added NaOH gradually. The solution formed was transferred into a Teflon-lined autoclave and heated at 120 °C with time variations of 8–16 h. The formation of bismuth oxide was indicated by the vibrations of the Bi−O−Bi and Bi−O groups and the crystal structure consisting of a-Bi2O3, β-Bi2O3, and g-Bi2O3. In addition, the highest photocatalytic activity can be examined through several factors, such as: content of Bi−O−Bi and Bi−OH groups, crystal structure, band gap values, morphology, and surface area, acquired as a result of the effect of hydrothermal reaction time. Copyright © 2021 by Authors, Published by BCREC Group. This is an open access article under the CC BY-SA License (https://creativecommons.org/licenses/by-sa/4.0).