Efeito de película de carbono tipo diamante nas propriedades mecânicas e de superfície da resina acrílica termopolimerizável

Introduction: The acrylic resin is used in dentistry for making dentures, orthodontic appliances and myo-relaxants splints; however, it has some limitations, such as low strength and high surface roughness. The diamond-like carbon (DLC) is a metastable form of amorphous carbon that can improve the resistance of various materials when applied as a film. Objective: To evaluate the effect of the DLC film application on the mechanical properties and surface of the acrylic resin thermally activated by power microwave (RAAT) (Vipi Wave). Materials and methods: Bodies of the test piece (flexural strength: 64 mm long x 10 mm wide x 3 mm; wear resistance: 4 mm diameter x 20 mm height, roughness: 10 mm diameter x 4 mm height) were obtained from the inclusion of replicas fiberglass flasks and polymerized according to the manufacturer. The deposition of films occurred by PECVD (Deposition Chemical Steam Assisted Plasma) with a thickness of 250 nm. They were divided into groups Gc (control) and Gt (treated) and underwent flexural strength test (n=18) in mechanical testing machine Instron (speed: 5 mm/min); wear resistance (n=18) biaxial Instron testing machine (load: 200 N, amplitude: 15 and frequency: 1,6 Hz) and analysis of the topography and surface roughness (Ra) by optical profilometry (n=18), with 5 objective measures of 20 X. the mean values were subjected to statistical tests of Mann-Whitney and t test to check the differences between the groups (p<0.05). Results: Gt showed higher roughness (0,108 ± 0,01 μm) than Gc (0,038 ± 0,01 μm), p<0,0001. There was no statistically significant difference (p=0,606) between Gt (103,3 MPa, IQ 97,67 ± 110,32) and Gc (105,3 MPa, IQ 98,95 ± 109,06) for resistance to flexion. There was no statistically significant difference between the groups in terms of straightness (Gt: 0,006 ± 0,0059 mm and Gc: 0,005 ± 0,0052 mm, p=0,774) and the depth of the indentations (Gt: 29,974 ± 8,69 μm and Gc : 28,169 ± 5,71 μm, p=0,610) after wear. Conclusion: The application of the DLC film on the surface of RAAT influenced the surface roughness having no effect on the flexural strength and wear.Introdução: A resina acrílica é utilizada na Odontologia para confecção de próteses dentárias, aparelhos ortodônticos e placas mio-relaxantes; porém, apresenta algumas limitações, como baixa resistência e alta rugosidade de superfície. O carbono tipo diamante (DLC) é uma forma metaestável de carbono amorfo que pode melhorar a resistência de vários materiais quando aplicado como uma película. Objetivo: Avaliar o efeito da aplicação de película de DLC nas propriedades mecânicas e de superfície da resina acrílica ativada termicamente por energia de micro-ondas (RAAT) (Vipi Wave). Materiais e métodos: Corpos-de-prova (resistência à flexão: 64 mm comprimento x 10 mm largura x 3 mm altura; resistência ao desgaste: 4 mm diâmetro x 20 mm altura; rugosidade: 10 mm diâmetro x 4 mm altura) foram obtidos a partir da inclusão de réplicas em muflas de fibra de vidro e polimerizadas segundo o fabricante. A deposição dos filmes ocorreu por PECVD (Deposição Química a Vapor Assistida por Plasma), com espessura de 250 nm. Os mesmos foram divididos nos grupos Gc (controle) e Gt (tratado) e passaram por ensaio de resistência à flexão (n=18) em máquina de ensaios mecânicos Instron (velocidade: 5 mm/min); resistência ao desgaste (n=18) em máquina de ensaio biaxial Instron (carga: 200 N, amplitude: 15° e frequencia: 1,6 Hz) e análise da topografia e rugosidade superficiais (Ra) por meio de perfilometria ótica (n=18), com 5 medidas em objetiva de 20 X. Os valores médios foram submetidos aos testes estatísticos de Mann-Whitney e teste t para verificar as diferenças entre os grupos (p<0,05). Resultados: Gt apresentou maior rugosidade (0,108 ± 0,01 μm) do que Gc (0,038 ± 0,01 μm), com p<0,0001. Não foi encontrada diferença estatisticamente significante (p=0,606) entre Gt (103,3 MPa; IQ 97,67 ± 110,32) e Gc (105,3 MPa; IQ 98,95 ± 109,06) em relação à resistência à flexão. Não foi encontrada diferença estatisticamente significante entre os grupos quanto à retilineidade (Gt: 0,006 ± 0,0059 mm e Gc: 0,005 ± 0,0052 mm, p=0,774) e profundidade das edentações (Gt: 29,974 ± 8,69 μm e Gc: 28,169 ± 5,71 μm, p=0,610) após o desgaste. Conclusão: A aplicação da película de DLC na superfície da RAAT influenciou a rugosidade superficial não tendo efeito na resistência à flexão e ao desgaste

Effect of hydrochloric acid commercial presentation for microabrasion technique on loss of enamel structure and surface

Introdução: A técnica de microabrasão pode ser realizada através de pasta pronta para uso, disponível comercialmente, ou o profissional pode manipulá-la no consultório. Objetivo: Verificar o efeito da apresentação comercial do ácido clorídrico a 10% na manipulação de pasta para microabrasão sobre a superfície do esmalte. Metodologia: Foram selecionados incisivos bovinos e divididos em dois grupos, de acordo com a apresentação comercial do ácido clorídrico (líquido ou em gel). O tratamento foi realizado através de dez aplicações com 10s de duração cada, intercaladas por lavagem de 10s. Vinte incisivos (n=10) foram utilizados para se determinar a perda de estrutura do esmalte. Cada amostra foi pesada, em balança analítica, antes e após submissão à microabrasão. Outras 20 amostras (n=10) foram utilizadas para determinação da rugosidade superficial média (Ra) utilizando-se um rugosímetro. Três amostras de cada grupo do experimento anterior foram selecionadas, aleatoriamente, e outras três amostras adicionais foram preparadas como controle (baseline) para análise em MEV. Resultados: Verificou-se diferença estatística significativa entre a massa final e a inicial e rugosidade superficial das amostras, independente da apresentação comercial do ácido. Nas imagens de MEV observou-se presença de superfície regular para o grupo controle (baseline). Nas demais imagens verificou-se superfície com considerável irregularidade e dissolução discreta do esmalte. Conclusões: O tratamento realizado causou perda significativa de estrutura e aumentou a rugosidade superficial dos espécimes, independente da apresentação comercial do ácido e sem apresentar diferença entre os grupos ao final. A apresentação comercial do ácido não parece ser um fator a interferir no tratamento.Introduction: The microabrasion technique can be performed using a commercially available paste, or the dentist can prepare it in his office. Objective: To verify the effect of hydrochloric acid commercial presentation in the handling of microabrasion paste on the enamel surface. Methodology: Bovine incisors were divided into two groups, according to the commercial presentation of 10% hydrochloric acid (liquid or gel). The treatment was carried out through ten applications of 10 s duration each, intercalated with a 10s wash. Twenty teeth (n=10) were used to determine the loss of enamel structure. Each sample was weighed on an analytical balance before and after submission to microabrasion. Another 20 teeth (n=10) were used to determine the average surface roughness (Ra) using a rugosimeter. Three samples from each group of the previous experiment were selected, randomly, and another three additional samples were prepared as a control (baseline) for SEM analysis. Results: There was a statistically significant difference between the final and initial mass and the surface roughness of the samples, regardless of the acid commercial presentation. In the SEM images, a regular surface was observed for the control group (baseline). In the other images, there was a surface with considerable irregularity and a slight dissolution of the enamel. Conclusions: The treatment carried out caused a significant loss of structure and increased the surface roughness of the specimens, regardless of the acid commercial presentation and without showing any difference between groups at the end of the treatment. The acid commercial presentation did not appear to be a factor interfering

Effect of hydrochloric acid commercial presentation for microabrasion technique on loss of enamel structure and surface

Introdução: A técnica de microabrasão pode ser realizada através de pasta pronta para uso, disponível comercialmente, ou o profissional pode manipulá-la no consultório. Objetivo: Verificar o efeito da apresentação comercial do ácido clorídrico a 10% na manipulação de pasta para microabrasão sobre a superfície do esmalte. Metodologia: Foram selecionados incisivos bovinos e divididos em dois grupos, de acordo com a apresentação comercial do ácido clorídrico (líquido ou em gel). O tratamento foi realizado através de dez aplicações com 10s de duração cada, intercaladas por lavagem de 10s. Vinte incisivos (n=10) foram utilizados para se determinar a perda de estrutura do esmalte. Cada amostra foi pesada, em balança analítica, antes e após submissão à microabrasão. Outras 20 amostras (n=10) foram utilizadas para determinação da rugosidade superficial média (Ra) utilizando-se um rugosímetro. Três amostras de cada grupo do experimento anterior foram selecionadas, aleatoriamente, e outras três amostras adicionais foram preparadas como controle (baseline) para análise em MEV. Resultados: Verificou-se diferença estatística significativa entre a massa final e a inicial e rugosidade superficial das amostras, independente da apresentação comercial do ácido. Nas imagens de MEV observou-se presença de superfície regular para o grupo controle (baseline). Nas demais imagens verificou-se superfície com considerável irregularidade e dissolução discreta do esmalte. Conclusões: O tratamento realizado causou perda significativa de estrutura e aumentou a rugosidade superficial dos espécimes, independente da apresentação comercial do ácido e sem apresentar diferença entre os grupos ao final. A apresentação comercial do ácido não parece ser um fator a interferir no tratamento.Introduction: The microabrasion technique can be performed using a commercially available paste, or the dentist can prepare it in his office. Objective: To verify the effect of hydrochloric acid commercial presentation in the handling of microabrasion paste on the enamel surface. Methodology: Bovine incisors were divided into two groups, according to the commercial presentation of 10% hydrochloric acid (liquid or gel). The treatment was carried out through ten applications of 10 s duration each, intercalated with a 10s wash. Twenty teeth (n=10) were used to determine the loss of enamel structure. Each sample was weighed on an analytical balance before and after submission to microabrasion. Another 20 teeth (n=10) were used to determine the average surface roughness (Ra) using a rugosimeter. Three samples from each group of the previous experiment were selected, randomly, and another three additional samples were repared as a control (baseline) for SEM analysis. Results: There was a statistically significant difference between the final and initial mass and the surface roughness of the samples, regardless of the acid commercial presentation. In the SEM images, a regular surface was observed for the control group (baseline). In the other images, there was a surface with considerable irregularity and a slight dissolution of the enamel. Conclusions: The treatment carried out

The knowledge level of dental surgeons regarding the relationship between occlusal factors and Temporomandibular Disorders (TMD)

AbstractIntroductionThe relationship between dental occlusion and temporomandibular disorders (TMD) remains a subject of disagreement. Many professionals erroneously base diagnosis and treatment strictly on the occlusal factor, despite the fact that current scientific evidence does not show such a relationship.ObjectiveTo evaluate the knowledge of dental surgeons (DSs) from João Pessoa (PB)-Brazil, regarding the relationship between occlusal factors and TMD.Materials and methodA sample of 100 DSs who do not have expertise in TMD and orofacial pain (CG Group) and seven DSs with this specialty (EG Group) completed a questionnaire that addresses issues concerning knowledge of TMD and its relationship with occlusal factors. The questionnaire also contained information used to characterize the sample, such as age, gender, and length of experience. The current literature's degree of consensus was established as the "gold standard" response for each statement and was compared with the responses of the specialists and non-specialists. Data were tabulated using the SPSS software package and analyzed descriptively (by percentage) and statistically using the chi-square and Fisher's exact tests (p < 0.05).ResultA wide divergence could be observed between the knowledge of DSs who do not specialize in TMD and orofacial pain and that of professionals who do.ConclusionThere was low agreement between specialists and non-specialists. The relationship between dental occlusion and TMD remains unclear for the vast majority of participating professionals, which may prove to be reflected in diagnostic behaviors and inappropriate occlusal treatment for the management of TMD