Influence of vacuum activated diffusion chroming on mechanical properties of the surface of steel 25X1MF

In the work, the surface of samples made of 25X1MF steel was saturated with chromium. For this, the method of vacuum activated diffusion chromium plating was used. In this process, sodium chloride was used as an activator. It was found that vacuum activated diffusion chromium plating of samples made of 25Kh1MF steel leads to the formation of a surface layer containing from 87 to 97 wt.% of this element. It was found that an increase in the temperature of the process and its duration leads to an increase in the chromium content on the surface of the samples. The tests showed that in the case of cavitations-erosion effects on the surface of chrome-plated samples of steel 25X1MF they have higher resistance. With abrasive wear, the resistance of the chrome-plated steel surface is 1.8 to 3 times higher compared to untreated material.Проведено насичення поверхні зразків зі сталі 25Х1МФ хромом. Для цього використовували метод вакуумного активованого дифузійного хромування. У цьому процесі в якості активатора використовували хлористий натрій. Було встановлено, що вакуумне активоване дифузійне хромування зразків зі сталі 25Х1МФ призводить до формування поверхневого шару, що містить від 87 до 97 мас.% цього елемента. При цьому встановлено, що підвищення температури процесу і його тривалості призводить до збільшення вмісту хрому на поверхні зразків. Проведені випробування показали, що в разі кавітаційно-ерозійного впливу на поверхню хромованих зразків зі сталі 25Х1МФ вони мають більш високу стійкість. При абразивному зносі стійкість хромованої поверхні сталі в 1,8–3 рази вище в порівнянні з необробленим матеріалом.Проведено насыщение поверхности образцов из стали 25Х1МФ хромом. Для этого использовали метод вакуумного активированного диффузионного хромирования. В этом процессе в качестве активатора использовали хлористый натрий. Было установлено, что вакуумное активированное диффузионное хромирование образцов из стали 25Х1МФ приводит к формированию поверхностного слоя, содержащего от 87 до 97 вес.% этого элемента. При этом установлено, что повышение температуры процесса и его длительности приводит к увеличению содержания хрома на поверхности образцов. Проведенные испытания показали, что в случае кавитационно-эрозионного воздействия на поверхность хромированных образцов из стали 25Х1МФ они имеют более высокую стойкость. При абразивном износе стойкость хромированной поверхности стали в 1,8–3 раза выше по сравнению с необработанным материалом

Properties of 15Cr12WNiMoV steel after vacuum activated chromium plating of its surface

In this work, we studied the properties of samples from steel 15Cr12WNiMoV after vacuum activated chromium plating at temperatures of 1070 and 1100 °C for 4 and 10 h. It was found that after chemical-thermal treatment on the samples a diffusion layer with a thickness of 50 to 130 µm is formed, consisting of 56…82 wt.% of chromium, the rest is iron. Metallographic studies were carried out on the samples and tests for heat resistance were carried out at a temperature of T = 900 °C. It was found that chrome-plated samples significantly exceed the initial samples and nitrided ones in terms of heat resistance. Tests of samples for tensile strength after chromium plating showed a significant increase in strength indicators for ultimate strength and yield strength. The plasticity characteristics of these samples are reduced.Проведені дослідження властивостей зразків зі сталі 15Х12ВНМФ після вакуумного активованого хромування при температурах 1070 і 1100 °С протягом 4 і 10 год. Установлено, що після хіміко-термічної обробки на зразках формується дифузійний шар товщиною від 50 до 130 мкм, що складається з 56…82 ваг.% хрому, інше – залізо. На зразках були проведені металографічні дослідження й здійснені випробування на жаростійкість при Т = 900 °С. Установлено, що хромовані зразки по жаростійкості значно перевершують вихідні зразки й азотовані. Проведені випробування зразків на міцність на розрив після хромування показали істотне збільшення міцностних показників для межі міцності й межі текучості. Характеристики пластичності цих зразків зменшуються.Проведены исследования свойств образцов из стали 15Х12ВНМФ после вакуумного активированного хромирования при температурах 1070 и 1100 °С в течение 4 и 10 ч. Установлено, что после химикотермической обработки на образцах формируется диффузионный слой толщиной от 50 до 130 мкм, состоящий из 56…82 вес.% хрома, остальное – железо. На образцах были проведены металлографические исследования и осуществлены испытания на жаростойкость при Т = 900 °С. Установлено, что хромированные образцы по жаростойкости значительно превосходят исходные образцы и азотированные. Проведенные испытания образцов на прочность на разрыв после хромирования показали существенное увеличение прочностных показателей для предела прочности и предела текучести. Характеристики пластичности этих образцов уменьшаются

Production Asymmetry Measurement of High Xt Hadrons in pp Collisions at 40 GeV

Single-spin asymmetries for hadrons have been measured in collisions of transversely-polarized 40 GeV/c proton beam with an unpolarized liquid hydrogen target. The asymmetries were measured for pi+-, K+-, protons and antiprotons, produced in the central region (0.02 < Xf < 0.10 and 0.7 < Pt < 3.4 GeV/c). Asymmetries for pi+-, K+- and antiprotons show within measurement errors the linear dependence on Xt and change a sign near 0.37. For protons negative asymmetry, independent of Xt has been found. The results are compared with those of other experiments and SU(6) model predictions.Comment: 25 pages (Latex), 12 Postscript figure