Calibration approach to electron probe microanalysis: A study with PWA-1480, a nickel base superalloy

The utility of an indirect calibration approach in electron probe microanalysis is explored. The methodology developed is based on establishing a functional relationship between the uncorrected k-ratios and the corresponding concentrations obtained using one of the ZAF correction schemes, for all the desired elements in the concentration range of interest. In cases where a very large number of analyses are desired, such a technique significantly reduces the total time required for the microprobe analysis without any significant loss of precision in the data. A typical application of the method in the concentration mapping of the transverse cross-section of a dendrite in directionally solidified PWA-1480, a nickel-based superalloy, is described

Macrosegregation during plane front directional solidification of Csl-1 wt. percent Tll alloy

Macrosegregation produced during vertical Bridgeman directional solidification of Csl-1 wt. pct. Tll in crucibles of varying diameter, from 0.5 to 2.0 cm, was examined. Gravity driven convection is present in the melt even in the smallest crucible diameter of 0.5 cm. Observed solutal profiles are in agreement with the analytical boundary layer model of Favier which describes macrosegregation in the presence of convection. The scintillation efficiency of Csl decreases along the specimen length as the thallium iodide content of the alloy increases

Robust procedure for creating and characterizing the atomic structure of scanning tunneling microscope tips

Scanning tunneling microscopes (STM) are used extensively for studying and manipulating matter at the atomic scale. In spite of the critical role of the STM tip, the control of the atomic-scale shape of STM tips remains a poorly solved problem. Here, we present a method for preparing tips {\it in-situ} and for ensuring the crystalline structure and reproducibly preparing tip structure up to the second atomic layer. We demonstrate a controlled evolution of such tips starting from undefined tip shapes.Comment: 12 pages preprint-style; 5 figure

Structural, optical and nanomechanical properties of (1 1 1) oriented nanocrystalline ZnTe thin films

Structural, optical and nanomechanical properties of nanocrystalline Zinc Telluride (ZnTe) films of thickness upto 10 microns deposited at room temperature on borosilicate glass substrates are reported. X-ray diffraction patterns reveal that the films were preferentially oriented along the (1 1 1) direction. The maximum refractive index of the films was 2.74 at a wavelength of 2000 nm. The optical band gap showed strong thickness dependence. The average film hardness and Young’s modulus obtained from loaddisplacement curves and analyzed by Oliver-Pharr method were 4 and 70 GPa respectively. Hardness of (1 1 1) oriented ZnTe thin films exhibited almost 5 times higher value than bulk. The studies show clearly that the hardness increases with decreasing indentation size, for indents between 30 and 300 nm in depth indicating the existence of indentation size effect. The coefficient of friction for these films as obtained from the nanoscratch test was ∼0.4.Financial support in the form of fellowships to MSRNK and SK from the ACRHEM project of DRDO is acknowledged

Floating phase in a dissipative Josephson junction array

We consider dissipative quantum phase transitions in Josephson junction arrays and show that the disordered phase in this extended system can be viewed as an unusual floating phase in which the states of local $(0+1)$-dimensional elements (single Josephson junctions) can slide past each other despite arbitrary range spatial couplings among them. The unusual character of the metal-superconductor quantum critical point can be tested by measurements of the current voltage characteristic. This may be the simplest and most natural example of a floating phase.Comment: 4 pages, RevTex4. The revised version contains higher order renormalization group equations and the corresponding phase diagra