17 research outputs found
Thermogravimetric study of reduction of oxides present in oxidized nickel-base alloy powders
Carbon, hydrogen, and hydrogen plus carbon reduction of three oxidized nickel-base alloy powders (a solid solution strengthened alloy both with and without the gamma prime formers aluminum and titanium and the solid solution strengthened alloy NiCrAlY) were evaluated by thermogravimetry. Hydrogen and hydrogen plus carbon were completely effective in reducing an alloy containing chromium, columbium, tantalum, molybdenum, and tungsten. However, with aluminum and titanium present the reduction was limited to a weight loss of about 81 percent. Carbon alone was not effective in reducing any of the alloys, and none of the reducing conditions were effective for use with NiCrAlY
Bend strengths of reaction bonded silicon nitride prepared from dry attrition milled silicon powder
Dry attrition milled silicon powder was compacted, sintered in helium, and reaction bonded in nitrogen-4 volume percent hydrogen. Bend strengths of bars with as-nitrided surfaces averaged as high as 210 MPa at room temperature and 220 MPa at 1400 C. Bars prepared from the milled powder were stronger than those prepared from as-received powder at both room temperature and at 1400 C. Room temperature strength decreased with increased milling time and 1400 C strength increased with increased milling time
Double gloves reduce contamination of dry box atmosphere
Pair of encased low permeability hand gloves between which an inert gas circulates reduces dry box contamination. This innovation is applicable to dry boxes using radioactive and alkali metal compounds, submicron powders, and liquid metals
Method of producing refractory composites containing tantalum carbide, hafnium carbide, and hafnium boride Patent
Production of high strength refractory compounds and microconstituents into refractory metal matri
Gas purged dry box glove Patent
Gas purged dry box glove reducing permeation of air or moisture into dry box or isolator by diffusion through glov
Effect of milling and leaching on the structure of sintered silicon
Sintering was performed in He for 16 hours at 1200, 1250, and 1300 C. Compacts of as-received Si did not densify during sintering. Milling reduced the average particle size to below 0.5 micrometer and enhanced densification (1.75 g/cc). Leaching milled Si further enhanced densification (1.90 g/cc max.) and decreased structural coarsening. After sintering, the structure of the milled and leached powder compacts appears favorable for the production of reaction bonded silicon nitride
Parametric evaluation of ball milling of SiC in water
A statistically designed experiment was conducted to determine optimum conditions for ball milling alpha-SiC in water. The influence of pH adjustment, volume percent solids loading, and mill rotational speed on grinding effectiveness was examined. An equation defining the effect of those milling variables on specific surface area was obtained. The volume percent solids loading of the slurry had the greatest influence on the grinding effectiveness in terms of increase in specific surface area. As grinding effectiveness improved, mill and media wear also increased. Contamination was minimized by use of sintered alpha-SiC milling hardware
Particle size reduction of Si3N4 with Si3N4 milling hardware
The grinding of Si3N4 powder using reaction bonded Si3N4 attrition, vibratory, and ball mills with Si3N4 media was examined. The rate of particle size reduction and the change in the chemical composition of the powder were determined in order to compare the grinding efficiency and the increase in impurity content resulting from mill and media wear for each technique. Attrition and vibratory milling exhibited rates of specific surface area increase that were approximately eight times that observed in ball milling. Vibratory milling introduced the greatest impurity pickup
Effect of attrition milling on the reaction sintering of silicon nitride
Silicon powder was ground in a steel attrition mill under nitrogen. Air exposed powder was compacted, prefired in helium, and reaction sintered in nitrogen-4 v/o hydrogen. For longer grinding times, oxygen content, surface area and compactability of the powder increased; and both alpha/beta ratio and degreee of nitridation during sintering increased. Iron content remained constant