4,760 research outputs found
The role of NaCl in flame chemistry, in the deposition process, and in its reactions with protective oxides as related to hot corrosion
Sodium chloride is believed to be the primary source of turbine engine contamination that contributes to hot corrosion. The behavior of NaCl-containing aerosols ingested with turbine intake air is very complex; some of the NaCl may vaporize during combustion while some may remain as particulates. The NaCl can lead to Na2SO4 formation by several possible routes or it can contribute to corrosion directly. Hydrogen or oxygen atom reaction with NaCl(c) was shown to result in the release of Na(g). Gaseous NaCl in flames can be partially converted to gaseous Na2SO4 by homogeneous reactions. The remaining gaseous NaCl and other Na-containing molecules can act as sodium carriers for condensate deposition of Na2SO4 on cool surfaces. A frozen boundary layer theory was developed to predict the rates of deposition. The condensed phase NaCl can be converted directly to condensed Na2SO4 by reaction with sulfur oxides and O2. Reaction of gaseous NaCl with Cr2O3 results in the vapor phase transport of chromium by the formation of complex Cr-containing gaseous molecules. Similar gaseous complexes are formed with molybdenum. The presence of gaseous NaCl was shown to affect the oxidation kinetics of Ni-Cr alloys. It also causes changes in the surface morphology of Al2O3 scales formed on Al-containing alloys
High-temperature mass spectrometry - Vaporization of group 4-B metal carbides
The high temperature vaporization of the metal-carbon systems TiC, ZrC, HfC, and ThC was studied by the Knudsen effusion - mass spectrometric method. For each system the metal dicarbide and tetracarbide molecular species were identified in the gas phase. Relative ion currents of the carbides and metals were measured as a function of temperature. Second- and third-law methods were used to determine enthalpies. Maximum values were established for the dissociation energies of the metal monocarbide molecules TiC, ZrC, HfC, and ThC. Thermodynamic functions used in the calculations are discussed in terms of assumed molecular structures and electronic contributions to the partition functions. The trends shown by the dissociation energies of the carbides of Group 4B are compared with those of neighboring groups and discussed in relation to the corresponding oxides and chemical bonding. The high temperature molecular beam inlet system and double focusing mass spectrometer are described
The dissociation energy of gaseous titanium mononitride
Dissociation energy of gaseous titanium nitrid
Dissociation energies of some high temperature molecules containing aluminum
The Knudsen cell mass spectrometric method has been used to investigate the gaseous molecules Al2, AlSi,AlSiO, AlC2, Al2C2, and AlAuC2. Special attention was given to the experimental considerations and techniques needed to identify and to measure ion intensities for very low abundance molecular species. Second- and third-law procedures were used to obtain reaction enthalpies for pressure calibration independent and isomolecular exchange reactions. Dissociation energies for the molecules were derived from the measured ion intensities, free-energy functions obtained from estimated molecular constants, and auxiliary thermodynamic data. The bonding and stability of these aluminum containing molecules are compared with other similar species
Mass spectrometric determination of the dissociation energies of titanium dicarbide and titanium tetracarbide
Mass spectrometric determination of dissociation energies of titanium dicarbide and titanium tetracarbid
Chemical mechanisms and reaction rates for the initiation of hot corrosion of IN-738
Sodium-sulfate-induced hot corrosion of preoxidized IN-738 was studied at 975 C with special emphasis placed on the processes occurring during the long induction period. Thermogravimetric tests were run for predetermined periods of time, and then one set of specimens was washed with water. Chemical analysis of the wash solutions yielded information about water soluble metal salts and residual sulfate. A second set of samples was cross sectioned dry and polished in a nonaqueous medium. Element distributions within the oxide scale were obtained from electron microprobe X-ray micrographs. Evolution of SO was monitored throughout the thermogravimetric tests. Kinetic rate studies were performed for several pertinent processes; appropriate rate constants were obtained from the following chemical reactions: Cr2O3 + 2 Na2SO4(1) + 3/2 O2 yields 2 Na2CrO4(1) + 2 SO3(g)n TiO2 + Na2SO4(1) yields Na2O(TiO2)n + SO3(g)n TiO2 + Na2CrO4(1) yields Na2O(TiO2)n + CrO3(g)
Reactions of chromium with gaseous NaCl in an oxygen environment
Target collection techniques and high pressure mass spectrometric sampling have been used to study the formation of volatile chromium-containing species in the reaction of Cr2O3 with O2 and NaCl gases. Experiments were performed at atmospheric pressure as a function of chromium temperature, oxygen pressure, and NaCl gas concentration. The major chromium-containing vapor species were found to be (NaCl)x CrO3 gas, with x = 1,2, and 3, which are products of heterogeneous reactions on the surface. The kinetics indicate first order dependence on oxygen and sodium chloride pressures
Oxidation in oxygen at 900 deg and 1000 deg C of four nickel-base cast superalloys: NASA-TRW VIA, B-1900, alloy 713C, and IN-738
The oxidation at 900 and 1,000 C of four nickel-base superalloys in 1 atmosphere of slowly flowing oxygen was investigated. Thermogravimetric rate data were obtained for periods to 100 hours. The morphology and composition of the oxide scales formed after 100 hours were studied by optical microscopy, X-ray diffraction, electron microprobe, scanning electron microscopy, and X-ray photoelectron spectroscopy (ESCA). Alloys B-1900 and VIA were found to be primarily alumina formers, though probably 25 percent of their surface was covered by CR2O3-containing oxides at 900 C. Alloys 713C and IN-738 were primarily chromia formers, though the surface of 713C at 1,000 C was covered with NiO, and the surface of IN-738 at both temperatures was covered with a thin layer of TiO2
Oxidative vaporization kinetics of chromium (III) oxide in oxygen from 1270 to 1570 K
Rates of oxidative vaporization of Cr2O3 on preoxidized resistively heated chromium were determined in flowing oxygen at 0.115 torr for temperatures from 1270 to 1570 K. Reaction controlled rates were obtained from experimental rates by a gold calibration technique. These rates were shown to agree with those predicted by thermochemical analysis. The activation energy obtained for the oxidative vaporation reaction corresponded numerically with the thermochemical enthalpy of the reaction. A theoretical equation is given for calculating the rate from thermodynamic data by using boundary layer theory
- …