Спосіб приготування порошку політетрафторетилену методом механічної активації

Спосіб приготування порошку політетрафторетилену (ПТФЕ) включає процес механічної активації порошку ПТФЕ в сухому стані. Процес механічної активації проводять у високообертовому млині при числі обертів n=5000/9000 хв.-1 протягом 3/8 хвилин.Способ приготовления порошка политетрафторэтилена (ПТФЭ) включает процесс механической активации порошка ПТФЭ в сухом состоянии. Процесс механической активации проводят в высокооборотной мельнице при числе оборотов n=5000/9000 мин.-1 на протяжении 3/8 минут.A method for the preparation of polytetrafluoroethylene (PTFE) powder involves a process of mechanical activation of dry PTFE powder. Mechanical activation process is carried out in high-speed pulverizer with number of revolutions n=5,000/9,000 min.-1 for 3/8 minutes

Detection of Structural Characteristics of Nanosized SnxSy Film by the Modulation-polarization Spectroscopy of Plasmon Resonance

The present work deals with the study of the structural properties of nanosized SnS2 films deposited by the close-spaced vacuum sublimation (CSVS) method. Surface morphology of the obtained films was determined by the scanning electron microscope (SEM-102Е). Structural investigations of the films were performed with the Raman spectroscopy. The analysis of chemical composition of the layers was carried out by the scanning electron microscope by energy dispersive X-ray (ЕDS) spectroscopy. The structure features of SnxSy films were investigated by the modulation-polarization spectroscopy (MPS) technique of surface plasmon resonance

Полімерний композиційний матеріал на основі політетрафторетилену

Полімерний композиційний матеріал на основі політетрафторетилену (ПТФЕ) містить легуючу домішку співполімеру. Як легуючу домішку введено ультрадисперсний фторорганічний матеріал "Форум".Полимерный композиционный материал на основе политетрафторэтилена (ПТФЭ) содержит легирующую примесь сополимера. Как легирующая примесь введен ультрадисперсный фторорганический материал "Форум".A polymeric composite material based on polytetrafluoroethylene (PTFE) contains copolymer doping impurity. Ultrafine fluoroorganic material Forum is used as a doping impurity

Полімерна композиція

Полімерна композиція містить політетрафторетилен і як вуглецевоволокнистий наповнювач - дискретні частинки, що утворені з суміші порошку політетрафторетилену і дискретного вуглецевого волокна. Наповнювач додатково містить подрібнене вуглецеве волокно. При цитуванні документа, використовуйте посилання http://essuir.sumdu.edu.ua/handle/123456789/10034Полимерная композиция содержит политетрафторэтилен и как углеродоволокнистый наполнитель - дискретные частички, которые образованы со смеси порошка политетрафторэтилена и дискретного углеродного волокна. Наполнитель дополнительно содержит измельченное углеродное волокно. При цитировании документа, используйте ссылку http://essuir.sumdu.edu.ua/handle/123456789/10034A polymeric composition contains the polytetrafluoroethylene and discrete particles as carbon-fiber filler, which are produced from the mixture of the polytetrafluoroethylene powder and the discrete carbon fiber. The filler additionally contains milled carbon fiber. When you are citing the document, use the following link http://essuir.sumdu.edu.ua/handle/123456789/1003

Speckle tracking dobutamine stress echocardiography diagnostic accuracy in primary coronary arteries disease diagnosi

The aim of the work was to evaluate STE feasibility as DSE visualization method and its accuracy compared to coronary angiography (CAG) in the patients with moderate-tohigh coronary arteries disease (CAD) risk. Materials and methods: We prospectively examined 140 pts (84 (60.0%) men) with suspected CAD in order to verify diagnosis and evaluate myocardial viability and coronary reserve. Results: Mean LV EF was 54.4±15.8%. All pts had normal BP and HR during the test. There were no significant hemodynamics alterations during the test. There were no significant complications during DSE – 15 (12.9%) cases of different relatively low-grade supraventricular and ventricular arrhythmia, mainly transitory without interventions. There were 116 (82.9%) positive DSE results, of which 2 (1.72%) were false-positive. In 2 (8.3%) pts with negative DSE results CAG revealed 1-vessel insignificant (50 – 70%) lesions with developed collaterals (false-negative results). According to DSE and CAG results, 96 (82.3%) pts underwent revascularization interventions – 86 (89.6%) PCI’s and (10.4%) CABG surgeries. Sensitivity and specificity of DSE with STE for primary CAD diagnosis according to “golden standard” CAG results were 98.3% and 91.7%, respectively, with identical positive and negative predictive value and very high method overall accuracy (AUC = 0.98) and OR = 627.0 (p<0.0001). Sensitivity and specificity of DSE with STE for defining indications for intervention and revascularization were 97.9% and 91.7%, respectively, with high overall accuracy (AUC = 0.95; OR = 564.0, p<0.0001). Combined quantification of ΔGLS and ΔWMSI for primary CAD diagnosis showed significantly lower sensitivity 86.2% (р=0.0002) and specificity 80.4% (р=0.0064) with significantly lower integral method accuracy (AUC 0.83, р<0.0001). Conclusions: DSE with STE as a visualization method is a safe and optimal method for ischemia diagnosis and myocardial viability and coronary reserve evaluation in the pts with CAD suspicion. Given the lower ΔGLS and ΔWMSI accuracy compared to integral DSE with STE result evaluation, as well as frequent GLS growth in significant amount of patients with definite positive test result, authors recommend evaluating integral test result rather than strain value

Plasmonic effects in tin disulfide nanostructured thin films obtained by the close-spaced vacuum sublimation

This work reports the investigation of plasmonic effects in tin disulfide (SnS2) nanostructured films obtained by the close-spaced vacuum sublimation method (CSS). Structural properties and phase composition of SnS2 films were studied with the help of field emission scanning electron microscopy (FE-SEM), atomic force microscopy (AFM), Xray diffraction (XRD) and Raman spectroscopy. Surface morphology and optical polarization properties of SnS2 films deposited at different substrate temperature were investigated by modulation-polarization spectroscopy (MPS). Surface plasmon resonances (SPR) with localized and polariton types were observed by measuring of angular and spectral characteristics of polarization difference. Radiative and nonradiative modes of surface plasmons have been analyzed at different light incident angles. The influence of surface morphology on resonant parameters of different types of SPR was studied. Correlation between the experimental results and theoretical calculations was established. The refractive and absorption indexes were found for the SnS2 films at different substrate temperature

Спосіб одержання вуглецевоволокнистого наповнювача фторопластоматричного композита

Спосіб одержання вуглецевоволокнистого наповнювача фторопластоматричного композита шляхом попереднього подрібнення вуглецевої тканини та наступного здрібнення утворених волокон, яке здійснюють у присутності введеного порошку фторопласту. При цитуванні документа, використовуйте посилання http://essuir.sumdu.edu.ua/handle/123456789/10197A process for the production of carbon fibre filler of fluoroplastic matrix composite consists in preliminary comminuting carbon fabric followed by comminuting fibers formed which is carried out in the presence of fluoroplastic powder. При цитировании документа, используйте ссылку http://essuir.sumdu.edu.ua/handle/123456789/1019

Створення модифікованих полімеркомпозиційних матеріалів з комплексом керованих властивостей для трибосистем ковзання

Об’єкт дослідження – керований технологічний процес одержання полімерних композиційних систем, у тому числі нанокомпозитних, з комплексом прогнозованих властивостей. Мета роботи – встановлення основних закономірностей, створення моделей та вдосконалення технологічних процесів формування складу, структури та функціональних властивостей одно- і багатокомпонентних полімерних речовин, у тому числі удосконалення способів виробництва, обробки та підбору технологічних параметрів процесу одержання інгредієнтів полімерної композиції, що забезпечувала б оптимізацію режимів переробки і відтворення заданого технічними умовами рівня фізикомеханічних властивостей